Regeneration charcoal manufactured from durian shells

A technology of durian shell and mechanism charcoal, which is applied in special forms of dry distillation, petroleum industry, biofuels, etc., can solve problems such as irritating odor, and achieve the effect of prolonging burning time, reducing irritating odor, and reducing the production of carbon monoxide.

Inactive Publication Date: 2018-07-10
黎娟
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are some machine-made charcoals on the market, but during the combustion process, there will be a phenomenon of pungent odor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A mechanism charcoal made of durian shells, comprising the following raw materials in parts by weight: 70 parts of durian shell powder, 12 parts of jasmine powder, 70 parts of sawdust, 6 parts of turpentine powder, 6 parts of diatomite, the durian shell powder, The particle diameter of jasmine pollen, sawdust, and turpentine powder is 3mm. The method for making the machine-made charcoal includes the following steps: (1) preparing materials: first drying each raw material until the moisture content is 18%; (2) making rods: making The above-mentioned processed powder after drying is evenly mixed with diatomaceous earth to make a hollow cylindrical fuel rod, and the cylindrical fuel rod is provided with a plurality of small holes through the inner and outer walls of the cylindrical fuel rod; (3) carbonization: the fuel rod is Put it into a container, burn and carbonize the fuel rod for 85 hours at a temperature of 250°C under anaerobic conditions, and cool naturally to obta...

Embodiment 2

[0014] A mechanism charcoal made of durian shells, comprising the following raw materials in parts by weight: 50 parts of durian shell powder, 10 parts of jasmine powder, 60 parts of sawdust, 5 parts of turpentine powder, 5 parts of diatomite, the durian shell powder, The particle diameter of jasmine pollen, sawdust, and turpentine powder is 2mm. The method for making the machine-made charcoal includes the following steps: (1) material preparation: firstly dry each raw material until the moisture content is 15%; (2) rod making: put The above-mentioned processed powder after drying is evenly mixed with diatomaceous earth to make a hollow cylindrical fuel rod, and the cylindrical fuel rod is provided with a plurality of small holes through the inner and outer walls of the cylindrical fuel rod; (3) carbonization: the fuel rod is Put it into a container, burn and carbonize the fuel rod for 80 hours at a temperature of 200°C under anaerobic conditions, and cool naturally to obtain m...

Embodiment 3

[0016] A mechanism charcoal made of durian shells, comprising the following raw materials in parts by weight: 80 parts of durian shell powder, 15 parts of jasmine powder, 80 parts of sawdust, 8 parts of turpentine powder, 8 parts of diatomite, the durian shell powder, The particle diameter of jasmine pollen, sawdust, and turpentine powder is 4mm. The method for making the machine-made charcoal includes the following steps: (1) material preparation: firstly dry each raw material until the moisture content is 20%; (2) rod making: put The above-mentioned processed powder after drying is evenly mixed with diatomaceous earth to make a hollow cylindrical fuel rod, and the cylindrical fuel rod is provided with a plurality of small holes through the inner and outer walls of the cylindrical fuel rod; (3) carbonization: the fuel rod is Put it into a container, burn and carbonize the fuel rod for 90 hours at a temperature of 300°C under anaerobic conditions, and cool naturally to obtain m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses regeneration charcoal manufactured from durian shells. The regeneration charcoal is manufactured from, by weight, 50-80 parts of durian shell powder, 10-15 parts of Arabian jasmine flower powder, 60-80 parts of sawdust, 5-8 parts of rosin powder and 5-8 parts of kieselguhr. The particle diameters of the durian shell powder, the Arabian jasmine flower powder, the sawdust andthe rosin powder range from 2 mm to 4 mm. The manufacturing method of the regeneration charcoal comprises the following steps of 1, preparing materials, wherein the raw materials are dried until thewater content is 15-20%; 2, manufacturing rods, wherein the dried machining powder and kieselguhr are mixed to be uniform, hollow cylinder firewood rods are manufactured, and the cylinder firewood rods are provided with a plurality of small holes running through the inner and outer walls of the cylinder firewood rods; 3, charring, wherein the firewood rods are placed into a container, under the anaerobic condition, under the temperature of 200-300 DEG C, the firewood rods are burnt and charred for 80-90 h, natural cooling is performed, and the regeneration charcoal is obtained. The charcoal has the durian flavor, and the durian shells are recycled.

Description

technical field [0001] The invention relates to the production field of machine-made charcoal, in particular to a machine-made charcoal made from durian shells. Background technique [0002] Humans have a long history of using charcoal. Charcoal is widely used as fuel, such as heating, barbecue, and hot pot fuel. Charcoal is made by burning or pyrolyzing wood under anaerobic conditions. However, due to the increasingly scarce forest resources , The use of wood to make charcoal will increase the cost of making charcoal; in addition, cutting down a large number of trees will destroy the natural ecological environment; charcoal prepared by general processes has a short burning time and low calorific value, which does not meet the requirements of energy conservation and environmental protection. The country has now banned logging and burning raw charcoal. There are some machine-made charcoals on the market, but during the combustion process, a pungent odor will be produced. C...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10B53/02
CPCC10B53/02Y02E50/10
Inventor 黎娟
Owner 黎娟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com