Method for preparing hierarchical porous material with direct ink writing technology

A direct-writing molding, multi-level hole technology, applied in the field of 3D printing molding, to achieve the effect of simple adjustment, easy control, and wide application range

Inactive Publication Date: 2018-07-20
文昌会文鑫博睿信息科技中心
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although some progress has been made in the synthesis of hierarchical porous materials, problems closely related to practical applications, such as the controllability of hierarchical pores, the connectivity of pore structures, and the stability of product quality, still exist in the research of hierarchical porous materials. facing great challenges

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Preparation of ZrO 2 The steps for hierarchical porous materials are as follows:

[0027] (1) The dispersant sodium polyacrylate (5g) and YSZ (3 moles Y 2 o 3 Stable ZrO 2 ) powder (260g, D50 is 0.8μm) was added to 50mL deionized water for ball milling for 12h, then added emulsifier butyrate mono-diglyceride (10g) ball milled for 5h, left standing for 24h, and high-speed shear emulsification for 10min to obtain emulsification ZrO 2 slurry. Wherein, the grinding ball is a zirconia ball of 300g, the ball milling speed is 15 rad / min, and the shearing speed is 1000 rad / min;

[0028] (2) ZrO will be obtained 2 The emulsified slurry is directly written into a multi-level porous material green body. The temperature is controlled at about 30°C and the humidity is controlled at 65%. Direct writing molding pressure is 30PSI; print head moving speed is 12mm / sec;

[0029] (3) Immerse the shaped body in kerosene for 24 hours, then dry it for 12 hours at a humidity of 60% an...

Embodiment 2

[0031] Preparation of Al 2 o 3 The steps for hierarchical porous materials are as follows:

[0032] (1) Polyacrylic acid (6g) and Al 2 o 3 Powder (320g, D50 is 0.8μm) and sintering aid MgO (3.2g) were added to 120mL deionized water for ball milling for 20 hours, then emulsifier butyric acid (5g) was added for ball milling for 10 hours, stood for 2 days, and then sheared at high speed Emulsified for 15 minutes to obtain emulsified Al 2 o 3 slurry. Wherein, the grinding ball is a 350g alumina ball, the ball milling speed is 20 rad / min, and the shearing speed is 800 rad / min;

[0033] (2) will emulsify Al 2 o 3 The slurry is subjected to direct writing molding to obtain a multi-level porous material green body. The temperature is controlled at around 23°C and the humidity is controlled at 70%. Direct writing molding pressure is 50PSI; print head moving speed is 10mm / sec;

[0034] (3) Dip the formed body in diesel oil for 30 hours, then dry it for 20 hours at a humidity ...

Embodiment 3

[0036] The steps of preparing AlN hierarchical porous material are as follows:

[0037] (1) Ammonium polyacrylate (8g) and AlN powder (350g, D50 is 2μm) sintering aid Y 2 o 3 (3g) with La 2 o 3 (2.1g) was added to 100mL deionized water for 18 hours, and then the emulsifier dimethylolbutyric acid (2g) was added for ball milling for 10 hours, left to stand for 2d, and then emulsified by high-speed shear for 15min to obtain emulsified AlN slurry. Wherein, the grinding ball is a 500g zirconia ball, the ball milling speed is 12 rad / min, and the shearing speed is 2000 rad / min;

[0038] (2) The obtained emulsified AlN slurry is subjected to direct writing molding to obtain a multi-level porous material green body. The temperature is controlled at around 32°C and the humidity is controlled at 76%. Direct writing molding pressure is 40PSI; print head moving speed is 120mm / sec;

[0039] (3) Immerse the formed body in vegetable oil for 36 hours, then dry it for 38 hours at a humidi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of 3D printing forming and discloses a method for preparing a hierarchical porous material with a direct ink writing technology. The method comprises the steps as follows: firstly, preparing powder slurry; then, adding one or more emulsifiers to the slurry and adjusting the rheological property of the slurry through emulsification; finally, preparing the hierarchical porous material with the slurry. The rheological property of the powder slurry can be adjusted to meet the requirement of direct ink writing technology, the method can meet the requirement of the hierarchical porous material prepared through 3D printing forming, and the pore diameter, pore volume and porosity of the hierarchical porous material can be adjusted conveniently.

Description

technical field [0001] The invention belongs to the technical field of 3D printing molding, and in particular relates to a method for preparing a multi-level porous material by using a direct writing molding technology. Background technique [0002] Due to its low thermal conductivity, low dielectric constant, large specific surface area, high strength, wear resistance, high temperature resistance, and corrosion resistance, porous materials are widely used in environmental protection, energy, chemical, biological and other fields. Porous materials can be divided into microporous materials (<2nm), mesoporous materials (2nm ~ 50 nm) and macroporous materials (>50nm) according to the pore size. Hierarchical porous materials are materials that contain different levels of pores such as micropores, mesopores or macropores. The pore size of the multi-level porous material is distributed step by step from large to small, and the pore structure of each level is a pore material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/117C04B35/488C04B35/582C04B35/626C04B35/622C04B38/10C04B38/00B28B1/00B33Y10/00B33Y70/00
CPCB28B1/001B33Y10/00B33Y70/00C04B35/117C04B35/488C04B35/581C04B35/622C04B35/6261C04B35/62625C04B35/6263C04B38/10C04B2235/3206C04B2235/3225C04B2235/3227C04B2235/616C04B2235/6562C04B2235/6567C04B38/00
Inventor 王小锋于凯