Cloisonne enamel picture capable of releasing anions, and manufacturing method thereof

A production method and negative ion technology, applied in heating methods, special decorative structures, decorative arts, etc., can solve the problems of backward production level, poor weather resistance, low efficiency, etc., and achieve high practicability, high artistic appreciation value, and removal of formaldehyde Effect

Active Publication Date: 2018-07-27
广州蓝雀工坊艺术品有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the fact that most of the market is workshop-style production, there is no dedicated R&D team and technical personnel, and the production level is relatively backward, resulting in low product quality, low efficiency, high production costs, unenvironmental materials, poor weather resistance and other common problems.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A method for making a cloisonné enamel painting that releases negative ions, comprising the following steps:

[0048] 1) Grind the enamel glaze material to 80-100 mesh, and mix it into enamel color glaze. During the mixing process of the enamel color glaze, it is necessary to mix the main color and transition color;

[0049] 2) The white negative ion powder is mixed into the adjusted enamel color glaze in the ratio of 10wt%; the white negative ion powder contains the following components in mass percentage: Ce 22.98%, La 15.56%, Ca 17.01%, Na9.05 %, Mg6.95%, Si 3.29% and P 2.78%; the particle size of the white anion powder is 2000-2200 mesh;

[0050] 3) On the carcass, use hand-drawn fine brushwork line draft;

[0051] 4) Step 3) Use a UV photocurable resin adhesive to stick metal wires on the carcass after processing; the UV photocurable resin adhesive has high transparency, high cohesive force, high temperature resistance and water resistance , which greatly improves ...

Embodiment 2

[0055] 1) Grind the enamel glaze material to 800-1000 mesh, and mix it into enamel color glaze. During the mixing process of the enamel color glaze, it is necessary to mix the main color and transition color;

[0056] 2) The white negative ion powder is mixed into the adjusted enamel color glaze in the ratio of 13wt%; the white negative ion powder contains the following components in mass percentage: Ce 22.98%, La 15.56%, Ca 17.01%, Na9.05 %, Mg6.95%, Si 3.29% and P 2.78%; the particle size of the white anion powder is 2000-2200 mesh;

[0057] 3) Draw fine brushwork on the carcass by inkjet;

[0058] 4) Step 3) Use a UV photocurable resin adhesive to stick metal wires on the carcass after processing; the UV photocurable resin adhesive has high transparency, high cohesive force, high temperature resistance and water resistance , which greatly improves the operation time and flexibility of filigree;

[0059] 5) On the carcass after step 4), fill the enamel color glaze after st...

Embodiment 3

[0062] 1) Grind the enamel glaze material to 1000-1200 mesh, and mix it into enamel color glaze. During the mixing process of the enamel color glaze, it is necessary to mix the main color and transition color;

[0063] 2) The white negative ion powder is mixed into the adjusted enamel color glaze in the ratio of 3wt%; the white negative ion powder contains the following components in mass percentage: Ce 22.98%, La 15.56%, Ca 17.01%, Na9.05 %, Mg6.95%, Si 3.29% and P 2.78%; the particle size of the white anion powder is 2000-2200 mesh;

[0064] 3) Draw meticulous line drafts on the carcass by silk screen printing;

[0065] 4) Step 3) Use a UV photocurable resin adhesive to stick metal wires on the carcass after processing; the UV photocurable resin adhesive has high transparency, high cohesive force, high temperature resistance and water resistance , which greatly improves the operation time and flexibility of filigree;

[0066] 5) On the carcass after step 4), fill the ename...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cloisonne enamel picture capable of releasing anions, and a manufacturing method thereof. The method comprises the following steps of (1) grinding enamel glaze material, andblending to obtain an enamel pigmented glaze; (2) mixing white anion powder into the prepared enamel pigmented glaze according to the proportion of 3 to 15 percent by weight; (3) drawing a fine brushwork line draft on a matrix; (4) adhering cloison on the matrix processed through the step (3), inlaying cloison and making patterns; (5) filling the enamel pigmented glaze into parts outside the cloison, and applying the enamel; and (6) spraying an adhesive for shaping, and drying to obtain the cloisonne enamel picture capable of releasing the anions. The cloisonne enamel picture capable of releasing the anions is good in color and luster, the color and luster of the cloisonne enamel picture capable of releasing the anions cannot be influenced, and meanwhile, the anions can be permanently released for effectively removing formaldehyde and purifying air, so that the cloisonne enamel picture capable of releasing the anions has higher practicability on indoor decoration.

Description

technical field [0001] The invention relates to the technical field of air purification products, in particular to a cloisonné enamel painting releasing negative ions and a manufacturing method thereof. Background technique [0002] With the development of cities, people pay more and more attention to air quality. Indoor decoration, furniture configuration, daily chemicals, etc. bring a large amount of formaldehyde, which is extremely harmful to human health. [0003] Formaldehyde, also known as formaldehyde, is a colorless gas with a strong pungent odor. Formaldehyde is easily polymerized into paraformaldehyde, which is prone to depolymerization when heated, and can slowly release monomeric formaldehyde at room temperature. Formaldehyde is mainly used in the production of various decoration and building materials, wood-based panels, plastics, leather, paper, artificial fibers, glass fibers, rubber, paints, medicines, paints, soaps and other products. Therefore, there is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B44C5/04F24F3/16C03C8/00
CPCB44C5/0438B44C5/0446C03C8/00F24F3/16F24F8/30
Inventor 陈锦增
Owner 广州蓝雀工坊艺术品有限公司