Zinc-copper-titanium alloy wire material for electric arc spraying and preparation process thereof

A technology of titanium alloy wire and arc spraying, which is applied in the direction of metal material coating process, coating, fusion spraying, etc., can solve problems such as alloy composition segregation, and achieve the effect of good surface quality, moderate hardness and moderate cost

Inactive Publication Date: 2018-07-27
NANTONG XINXIANG ZINC IND
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, arc spraying metal wires widely used in the field of anti-corrosion include zinc wire, aluminum wir

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example one:

[0021] A preparation process of zinc-copper-titanium alloy wire for arc spraying includes the following steps:

[0022] 1) Refining the master alloy. The master alloy of metal zinc, copper and titanium in a weight ratio of 55:45:5 is uniformly melted in a vacuum induction furnace, and the melting temperature is 620-820℃;

[0023] 2) Molten zinc ingot: Melt zinc ingot with purity of 99.99% in a vacuum induction furnace at a melting temperature of 500-550°C. After it is completely melted, fully stir and use a special refining agent for degassing and slag removal;

[0024] 3) The alloy wire billet is made by continuous casting and hot continuous rolling;

[0025] 4) Annealing and cooling the alloy wire billet to obtain a zinc-copper-titanium alloy wire.

[0026] A zinc-copper-titanium alloy wire for arc spraying, comprising any one of the preparation processes of zinc-copper-titanium alloy wire for arc spraying, the mass content of copper is 0.4-0.6%, and the mass cont...

Example Embodiment

[0027] Embodiment two:

[0028] A preparation process of zinc-copper-titanium alloy wire for arc spraying includes the following steps:

[0029] 1) Refining the master alloy. The master alloy of metal zinc, copper and titanium in a weight ratio of 55:45:5 is uniformly melted in a vacuum induction furnace, and the melting temperature is 600-800℃;

[0030] 2) Molten zinc ingot: Melt the zinc ingot with a purity of 99.995% in a vacuum induction furnace at a melting temperature of 500-550°C. After it is completely melted, fully stir and use a special refining agent to remove gas and slag;

[0031] 3) The alloy wire billet is made by continuous casting and hot continuous rolling;

[0032] 4) Annealing and cooling the alloy wire billet to obtain a zinc-copper-titanium alloy wire.

[0033] A zinc-copper-titanium alloy wire for arc spraying, comprising any one of the preparation processes of zinc-copper-titanium alloy wire for arc spraying, the mass content of copper is 0.4-0.6%, and the mass co...

Example Embodiment

[0034] Embodiment three:

[0035] A preparation process of zinc-copper-titanium alloy wire for arc spraying includes the following steps:

[0036] 1) Refining the master alloy. The master alloy of metal zinc, copper and titanium in a weight ratio of 55:45:5 is uniformly melted in a vacuum induction furnace, and the melting temperature is 620-820℃;

[0037] 2) Molten zinc ingot: Melt the zinc ingot with a purity of 99.995% in a vacuum induction furnace at a melting temperature of 500-550°C. After it is completely melted, fully stir and use a special refining agent to remove gas and slag;

[0038] 3) The alloy wire billet is made by continuous casting and hot continuous rolling;

[0039] 4) Annealing and cooling the alloy wire billet to obtain a zinc-copper-titanium alloy wire.

[0040] A zinc-copper-titanium alloy wire for arc spraying, including any one of the preparation processes of zinc-copper-titanium alloy wire for arc spraying, the mass content of copper is 0.4-0.5%, and the mass c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melting temperatureaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of zinc-copper-titanium alloy wire material, and discloses a zinc-copper-titanium alloy wire material for electric arc spraying and a preparation process thereof, wherein the preparation method includes the following steps: 1) refining an intermediate alloy, and melting uniformly the intermediate alloy with the weight ratio of metals zinc, copper and titanium of 55:45:5 in a vacuum induction furnace; 2) melting a zinc ingot, melting the zinc ingot with the purity of 99.99% in the vacuum induction furnace, after completely melting, fully stirring, and degassing and deslagging by a special refining agent; 3) preparing an alloy wire blank by a continuous casting and hot continuous rolling method; and 4) annealing and cooling the alloy wire blank, to produce the zinc-copper-titanium alloy wire material. According to the zinc-copper-titanium alloy wire material for electric arc spraying and the preparation process thereof, the prepared zinc-copper-titanium alloy wire material has good surface quality and moderate hardness and meets the standards of electric arc spraying construction; at the same time, the zinc-copper-titanium alloy wire material product has moderate cost, is suitable for large-scale production and has prospect of vigorous promotion.

Description

technical field [0001] The invention relates to the technical field of zinc-copper-titanium alloy wire, in particular to a zinc-copper-titanium alloy wire for arc spraying and a preparation process thereof. Background technique [0002] Arc spraying technology is a kind of thermal spraying technology that emerged in China around 2000, and has a wide range of applications. Arc spraying technology is one of the most effective anti-corrosion technologies for steel structures. This technology is used to form metal coatings on the surface of steel structures, and to seal holes and heavy-duty anti-corrosion coatings on the coatings, effectively prolonging the service life of steel structures. . At present, the arc spraying metal wires widely used in the field of anti-corrosion include zinc wire, aluminum wire and zinc-aluminum alloy wire, but these wires have problems such as alloy composition segregation during use. Contents of the invention [0003] (1) Solved technical prob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C1/03C22C1/06C22C18/02B21C37/04
CPCC22C1/03B21C37/04C22C1/06C22C18/02C23C4/131
Inventor 不公告发明人
Owner NANTONG XINXIANG ZINC IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products