A kind of preparation method of metal coated graphene reinforced metal matrix composite material

A graphene composite, metal-clad technology, applied in metal material coating process, metal processing equipment, transportation and packaging, etc., can solve problems such as poor interface bonding, reduce agglomeration, enhance wettability, and high safety Effect

Active Publication Date: 2021-07-23
KUNMING UNIV OF SCI & TECH
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the problems existing in the prior art, the purpose of the present invention is to solve the problem of poor interface bonding between the surface of carbon nanotubes and the metal matrix, and provide a method for in-situ reduction of coated metals on the surface of carbon nanotubes, and then compounded with metals. Thereby obtaining a kind of preparation method of the carbon nanotube reinforced metal matrix composite material coated with metal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of preparation method of metal clad graphene reinforced metal matrix composite material, this preparation method is carried out according to the following steps:

[0024] a. In-situ reduction of the powdered graphene surface to coat the metal to obtain a metal-coated graphene composite powder;

[0025] B, the metal-coated graphene composite powder and the metal powder are mixed by ball milling to obtain the metal-coated graphene composite powder / metal mixed powder;

[0026] c adopt the powder metallurgy warm-pressing process to warm-press the metal-coated graphene / metal mixed powder, sinter, and process the composite material by extrusion, forging and rolling to obtain the metal-coated Graphene-reinforced metal matrix composites;

[0027] The in-situ reduction of coated metal on the surface of graphene comprises the following steps:

[0028] a powdery graphene is pressed into sheets, wherein the thickness of the sheet is 0.01cm;

[0029] b. Use the sheet press...

Embodiment 2

[0035] A kind of preparation method of metal clad graphene reinforced metal matrix composite material, this preparation method is carried out according to the following steps:

[0036] a. In-situ reduction of the powdered graphene surface to coat the metal to obtain a metal-coated graphene composite powder;

[0037] B, the metal-coated graphene composite powder and the metal powder are mixed by ball milling to obtain the metal-coated graphene composite powder / metal mixed powder;

[0038] c adopt the powder metallurgy warm-pressing process to warm-press the metal-coated graphene / metal mixed powder, sinter, and process the composite material by extrusion, forging and rolling to obtain the metal-coated Graphene-reinforced metal matrix composites;

[0039] The in-situ reduction of coated metal on the surface of graphene comprises the following steps:

[0040] a powdery graphene is pressed into sheets, wherein the thickness of the sheet is 0.1cm;

[0041] b Use the sheet pressed...

Embodiment 3

[0047] A kind of preparation method of metal clad graphene reinforced metal matrix composite material, this preparation method is carried out according to the following steps:

[0048] a. In-situ reduction of the powdered graphene surface to coat the metal to obtain a metal-coated graphene composite powder;

[0049] B, the metal-coated graphene composite powder and the metal powder are mixed by ball milling to obtain the metal-coated graphene composite powder / metal mixed powder;

[0050] c adopt the powder metallurgy warm-pressing process to warm-press the metal-coated graphene / metal mixed powder, sinter, and process the composite material by extrusion, forging and rolling to obtain the metal-coated Graphene-reinforced metal matrix composites;

[0051] The in-situ reduction of coated metal on the surface of graphene comprises the following steps:

[0052] a powdery graphene is pressed into sheets, wherein the thickness of the sheet is 0.05cm;

[0053] b. Use the sheet press...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
breaking strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a metal-coated graphene-reinforced metal-based composite material. The preparation method comprises the following steps: first reducing powdery graphene to coat metal in situ to obtain a metal-coated graphene composite powder, Then, the metal-coated graphene composite powder is mixed with metal powder by ball milling to obtain metal-coated graphene / metal mixed powder; the metal-coated graphene / metal mixed powder is processed by powder metallurgy warm pressing process Warm pressing, sintering, extrusion, forging, rolling and other processes for composite material processing. The invention improves the wettability with the metal matrix by carrying out metallization modification on the surface of the graphene, and is beneficial to disperse in the metal matrix as a reinforcing body, thereby improving the mechanical properties of the metal. The preparation method is simple and has broad application prospects.

Description

technical field [0001] The invention relates to a method for preparing a metal-coated graphene-reinforced metal matrix composite material, and belongs to the technical field of composite material preparation. . [0002] technical background [0003] With the continuous development of aerospace and automobile manufacturing technology, lightweight, high-strength metal matrix composites have received extensive attention and research. As a lightweight material with excellent mechanical, electrical, and thermal properties, carbon nanomaterials have been widely used in metal matrix composites, catalysis, and energy in recent years. Among them, graphene is a new type of two-dimensional planar carbonaceous nanomaterial discovered and synthesized in recent years, with unparalleled high electron mobility (~200000cm 2 / V·s), thermal conductivity (~5000W / m·K), Young's modulus (1100GPa) and breaking strength (125GPa), exhibiting excellent electrical, thermal and mechanical properties. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/05C22C1/10B22F1/02B22F3/14B22F3/10C23C18/31
CPCC22C1/05C23C18/31B22F3/1017B22F3/14B22F2003/145B22F2998/10B22F1/17B22F3/24
Inventor 方东鲍瑞易健宏李秀娟
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com