Preparation method for colored sand glaze ceramic tile

A production method and technology for colored sand, applied in the field of materials, can solve the problems of high cost of raw materials, easy precipitation of glaze paste, rough surface, etc., and achieve the effects of simple glazing, bright colors and high flexibility

Inactive Publication Date: 2018-07-31
FUJIAN UNIV OF TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims to solve the problems of complex process, high cost of raw materials and easy precipitation of glaze slurry in the existing preparation of colored sand glaze, and proposes a method of using quartz sand as the main raw material to prepare colored sand glaze at one time. On the premise of obtaining high-quality colored sand glaze, the preparation process is simplified to the greatest extent, the production cost is reduced, and the problem of easy precipitation of glaze slurry during glazing is effectively solved. The surface of the glaze is rough and uniform, the color is bright, and the variety is complete. , suitable for bathroom floor tiles and other fields, green and environmentally friendly, with broad application prospects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for colored sand glaze ceramic tile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The mass percent of the raw material formula of this example is: 70% of quartz sand, 4% of potassium feldspar, 5% of kaolin, 6% of sodium carboxymethyl cellulose, and 15% of red pigment. Proportion according to the formula, wet grinding in a planetary ball mill for 5 minutes, material: ball = 1:1.5, sodium carboxymethyl cellulose: water = 1:40. Glaze the surface of the tiles, the thickness of the glaze layer is 1mm when it is not dry, and dry at room temperature for 10h until the glaze layer is dry. Put the dried tiles in a resistance furnace for high-temperature firing, the heating rate is 7.2°C / min, the maximum firing temperature is 1230°C, the holding time is 20min, and cool with the furnace. The glaze surface of the product is rough, the quartz sand particles are fine and evenly distributed, the overall shape is simple and generous, the hand feels comfortable, and the base glaze is well combined.

Embodiment 2

[0023] The weight ratio of the raw material formula of this example is: 80% of quartz sand, 2% of potassium feldspar, 3% of kaolin, 4% of sodium carboxymethyl cellulose, and 11% of navy blue colorant. Proportion according to the formula, wet grinding in a planetary ball mill for 30 minutes, material: ball = 1:1.5, sodium carboxymethylcellulose: water = 1:50. Glaze the surface of the tiles, the thickness of the glaze layer is 2mm when it is not dry, and dry at room temperature for 12 hours until the glaze layer is dry. The dried tiles are fired in a resistance furnace at a high temperature, the heating rate is 7.2°C / min, the maximum firing temperature is 1250°C, the holding time is 15min, and they are cooled with the furnace. The glazed surface of the product has a matte effect, with delicate concave-convex lines on the surface, the particle size of the quartz sand is small, the hand feels comfortable, and the base glaze is well bonded.

Embodiment 3

[0025] The weight ratio of the raw material formula of this example is: 80% of quartz sand, 2% of potassium feldspar, 3% of kaolin, 4% of sodium carboxymethyl cellulose, and 11% of brown pigment. Proportion according to the formula, wet grinding in a planetary ball mill for 5 minutes, material: ball = 1:1.5, sodium carboxymethyl cellulose: water = 1:40. Glaze the surface of the tiles, the thickness of the glaze layer is 1.5mm when it is not dry, and dry it at room temperature for 12 hours until the glaze layer is dry. Put the dried tiles in a resistance furnace for high-temperature firing, the heating rate is 7.2°C / min, the maximum firing temperature is 1230°C, the holding time is 15min, and cool with the furnace. The glaze surface of the product is rough, the quartz sand is large in size, evenly distributed, comfortable to the touch, and well bonded to the glaze.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method for a colored sand glaze ceramic tile. The tile is prepared from 70-80 parts of quartz sand, 2-4 parts of potash feldspar, 3-5 parts of kaolin, 4-6 parts of carboxymethyl cellulose sodium and 11-15 parts of pigment. According to the preparation method, the quartz sand is taken as a main raw material, a certain amount of carboxymethyl cellulose sodium isadded to improve a suspension property of glaze slip, and the defect of constant stirring in the glazing process of an original preparation process is solved, the method applied to bathroom floor tiles not only is simple and convenient to glaze, but also has skidproof and decorative effects. Because the raw material cost is low, the sintering temperature is not high, the product has more color varieties, the color is bright, firm, enduring, resistant in scratch, fadeless and resistant in a high temperature, and the method has significant economic benefits and social benefits.

Description

technical field [0001] The invention relates to the field of material technology, in particular to a method for manufacturing colored sand glaze tiles. Background technique [0002] Colored sand can be generally divided into natural colored sand and artificial colored sand. Natural colored sand is crushed from natural ore. It does not fade but has more impurity colors and fewer colors. The preparation process is complicated. Artificial colored sand is based on quartz sand and coated with a layer of color-developing materials on its surface, such as chrysanthemum yellow, medium gray, blue gray, and other colors. Therefore, artificial colored sand has the advantages of bright colors and many varieties. Most of the color-developing materials of the layer are polymer materials, which are not resistant to high temperature, and are easy to lose color due to carbonization in a high-temperature environment, and the preparation process is more complicated. As artificial colored sand...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/5022C04B41/86C04B41/4539C04B41/0072
Inventor 花能斌廖振龙王乾廷陈文哲
Owner FUJIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com