Preparation method of fleece thermal cloth

A fabric and fleece technology, applied in the field of textile fabrics, can solve the problems of easy wrinkling and poor wear resistance, and achieve the effects of fast evaporation rate, good thermal performance, and strong moisture-conducting effect

Inactive Publication Date: 2018-07-31
HAIYAN SHUOCHUANG CLOTHING RES INST
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to provide a preparation method for fleece thermal fabric, the preparation method is simple to operate, suitable for large-scale industrial production, and the prepared fabric overcomes the problems of easy wrinkling and poor wear resistance of existing fabrics. Good thermal performance, good flame retardant performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Embodiment 1: the preparation method of fleece warm-keeping cloth:

[0012] 1) Preparation of pearl fiber: Take polyvinyl alcohol, nano-pearl powder and polyester chips and mix them in a mass ratio of 2:7:80, then press the melt out from the spinneret hole at 263°C, and put it in water Cool and solidify into silk to obtain pearl fiber; the prepared fiber has a variety of amino acids contained in nano-pearls, has the effect of pearl beauty and skin care, and long-term contact with the skin has the functions of pearl beauty care, clearing away fire and detoxification, and whitening skin. Anti-ultraviolet effect;

[0013] 2) Preparation of polyester fiber: polyester chips are melt-spun to obtain polyester fiber, wherein the spinning temperature is 280°C, the spinning speed is 900m / min, the stretching temperature is 65°C, and the pre-stretching ratio It is 1.04, the draw ratio of the first pass is 2.8, and the draw ratio of the second pass is 1.05; under this condition, th...

Embodiment 2

[0015] Embodiment 2: the preparation method of fleece warm-keeping cloth:

[0016] 1) Preparation of pearl fiber: Take polyvinyl alcohol, nano-pearl powder and polyester chips and mix them in a mass ratio of 5:12:80, then press the melt out from the spinneret hole of the spinneret at 275°C, and put it in water Cool and solidify into silk to obtain pearl fiber; the prepared fiber has a variety of amino acids contained in nano-pearls, has the effect of pearl beauty and skin care, and long-term contact with the skin has the functions of pearl beauty care, clearing away fire and detoxification, and whitening skin. Anti-ultraviolet effect;

[0017] 2) Preparation of polyester fiber: melt-spin polyester chips to obtain polyester fiber, wherein the spinning temperature is 290°C, the spinning speed is 1200m / min, the stretching temperature is 75°C, and the pre-stretching ratio It is 1.08, the draw ratio of the first pass is 3.2, and the draw ratio of the second pass is 1.15; under thi...

Embodiment 3

[0019] Embodiment 3: the preparation method of fleece warm-keeping cloth:

[0020] 1) Preparation of pearl fiber: Take polyvinyl alcohol, nano-pearl powder and polyester chips and mix them in a mass ratio of 3:8:80, then press the melt out from the spinneret hole at 266°C, and put it in water Cool and solidify into silk to obtain pearl fiber; the prepared fiber has a variety of amino acids contained in nano-pearls, has the effect of pearl beauty and skin care, and long-term contact with the skin has the functions of pearl beauty care, clearing away fire and detoxification, and whitening skin. Anti-ultraviolet effect;

[0021] 2) Preparation of polyester fiber: melt-spin polyester chips to obtain polyester fiber, wherein the spinning temperature is 281°C, the spinning speed is 950m / min, the stretching temperature is 66°C, and the pre-stretching ratio It is 1.05, the draw ratio of the first pass is 2.9, and the draw ratio of the second pass is 1.06; under this condition, the vi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of fleece thermal cloth. The method includes the steps that pearl fibers are prepared, polyester fibers are prepared, and the cloth is prepared. The preparation method has the advantages that the preparation method is easy to operate and suitable for large-scale industrialized production; the prepared cloth overcomes the defects that existing cloth is not likely to wrinkle and poor in abrasion resistance; the cloth is good in thermal insulation, high in wet conduction and high in evaporation rate of water molecules.

Description

technical field [0001] The invention relates to the field of textile fabrics, in particular to a method for preparing fleece thermal fabrics. Background technique [0002] With the continuous improvement of material living standards, people's pursuits are also constantly changing. Basic needs such as food and clothing have gradually become a thing of the past, and health and comfort have become the current standard. People put forward higher requirements on the quality of clothing fabrics. Fashionable, healthy, comfortable and casual clothing is more and more favored by consumers. Clothing fabrics are developing in the direction of high-grade, diversification and functionalization. Contents of the invention [0003] The object of the present invention is to provide a preparation method for fleece thermal fabric, the preparation method is simple to operate, suitable for large-scale industrial production, and the prepared fabric overcomes the problems of easy wrinkling and p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D02G3/02D01F6/92D01F6/62D01F6/84D01F1/10D03D15/283D03D15/50D03D15/58
CPCD01F1/10D01F1/106D01F6/62D01F6/84D01F6/92D02G3/02D03D15/00D10B2331/04D10B2321/06
Inventor 王硕
Owner HAIYAN SHUOCHUANG CLOTHING RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com