Low-toxicity flame-retardant double-component marked line coating agent and preparation method thereof

A two-component, marking paint technology, applied in the direction of coating, etc., can solve the problems of long curing time, etc., and achieve the effect of good adhesion, prolonging the use time, and beautiful colors

Inactive Publication Date: 2018-08-03
王建周
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the existing two-component marking primers on the market are unsaturated resins, which take a long time to cure when used, and are flammable and explosive dangerous chemicals. The danger to the production, transportation, construction and other links of the operator and the lives of the surrounding personnel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The low-toxic flame-retardant marking line primer of this embodiment is based on parts by weight. The main raw materials are: 320 parts of acrylic resin, 30 parts of dioctyl phthalate, and A and B two-component solvent, among them,

[0032] The formula of component A by weight is: 320 parts of dichloromethane, 20.4 parts of isopropanol or tert-butanol;

[0033] The formula of component B in parts by weight is: 5 parts of butyl acetate, 5 parts of acetone, and 216 parts of aromatic hydrocarbons. The preparation method of the low-toxic flame-retardant marking line primer of the present embodiment comprises the following steps:

[0034] (1) Put the component A solvent into the reactor by weight, stir for 15 minutes, add the corresponding weight of acrylic resin or styrene-modified acrylic resin, and keep the speed of the reactor at 50-120 rpm until the resin is completely dissolve;

[0035] (2) In the slurry prepared in step (1), put the component B solvent into the rea...

Embodiment 2

[0038] The low-toxic flame-retardant marking primer of the present embodiment, in parts by weight, consists of the main raw materials: 320 parts of styrene-modified acrylic resin, 30 parts of dioctyl phthalate, and A, B Two-component solvents, where,

[0039] The formula of component A by weight is: 320 parts of dichloromethane, 20.4 parts of isopropanol or tert-butanol;

[0040] The formula of component B in parts by weight is: 5 parts of butyl acetate, 5 parts of acetone, and 216 parts of aromatic hydrocarbons. The preparation method of the low-toxic flame-retardant marking primer of this embodiment is the same as that of Embodiment 1.

Embodiment 3

[0042] The low-toxic flame-retardant marking primer of the present embodiment is based on parts by weight. The main raw materials are: 320 parts of styrene-modified acrylic resin, 25 parts of dioctyl phthalate, phthalic acid 5 parts of dibutyl ester, and A, B two-component solvent, wherein,

[0043] The formula of component A by weight is: 320 parts of dichloromethane, 20.4 parts of isopropanol or tert-butanol;

[0044] The formula of component B in parts by weight is: 5 parts of butyl acetate, 5 parts of acetone, and 216 parts of aromatic hydrocarbons. The preparation method of the low-toxic flame-retardant marking primer of this embodiment is the same as that of Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-toxicity flame-retardant double-component marked line coating agent and a preparation method thereof. The marked line coating agent is mainly prepared from the followingraw materials in parts by weight: 320 parts of acrylic resin or styrene modified acrylic resin, 30 parts of plasticizer and a solvent with components A and B, wherein the component A is prepared fromthe following components in parts by weight: 320-330 parts of chlorinated hydrocarbons and 20.4-28.7 parts of low-grade saturated monohydric alcohol; and the component B is prepared from the followingcomponents in parts by weight: 5-10 parts of butyl acetate, 5-10 parts of acetone and 216-289 parts of aromatic hydrocarbons. The product can form a firm adaptor with asphalt, modified asphalt and acement road surface, can avoid influences, on paint reaction activity, of soluble during MMA double-component marked line construction; and the formed mark line is good in adhesion force, is great intoughness, is high in hardness, is good in wear resistance, is strong in pollutant resistance, and is bright in color, so that the use time of the marked line can be prolonged; and the flammable and combustible risk is avoided in each link of production, transportation and construction, so that life safety of an operator and people around of each link of production, transportation and constructionis ensured.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a low-toxicity flame-retardant two-component marking primer and a preparation method thereof. Background technique [0002] During the construction of MMA two-component marking paint, the petroleum resin and synthetic rubber contained in the ordinary marking primer will be dissolved. At the same time, the asphalt and modified asphalt in the road surface will be dissolved, and the dissolved petroleum resin and synthetic rubber will be dissolved. , asphalt, and modified asphalt will reduce the active components of MMA two-component coatings (among them, the active components are active monomers, initiators, accelerators, and curing agents), resulting in reduced reactivity of the reactant and prolonged curing time. The formed marking lines are yellowish and flowery, have low hardness, poor toughness, and low wear resistance, which shortens the service life of the markin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D125/14C09D7/20
CPCC09D133/04C09D7/20C09D125/14
Inventor 王建周王硕刘晰王磊
Owner 王建周
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap