Emerald green glaze

A technology of jade green glaze and raw materials, applied in the field of glaze, can solve the problems of yellowing of green glaze and impure color, etc., and achieve the effects of high yield, pure and natural color, jade texture and strong opacity.

Inactive Publication Date: 2018-08-17
禹州市土魂钧瓷有限公司
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of the preparation methods of green glaze use copper oxide as the colorant and are fired in an oxidizing atmosphere.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Emerald green glaze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] An emerald green glaze, which is prepared from the following raw materials in parts by weight: 10-16 parts of this medicine, 39-45 parts of feldspar, 11-17 parts of quartz, 13-19 parts of calcite, 4-6 parts of talc, iron 3.5-4.3 parts of ore, 0.08-0.12 parts of chromium oxide, 5-7 parts of zinc oxide.

[0021] The preparation method of above-mentioned emerald green glaze, comprises the following steps:

[0022] (1) Preparation of glaze slurry: Add appropriate amount of water to mix the above raw materials, and ball mill to obtain glaze slurry with a mass concentration of 55-57%;

[0023] (2) Glazing: Immerse the green body in the glaze slurry prepared in step (1) for a while, take it out for a while, immerse it again for a while, take it out, and use the water absorption of the green body to make the glaze slurry evenly adhere to the surface of the green body; the thickness of the glaze 1.5-1.7mm;

[0024] (3) Firing, the firing temperature is 1300-1320°C;

[0025] T...

Embodiment 2

[0031] An emerald green glaze, which is prepared from the following raw materials in parts by weight: 13 parts of this medicine, 42 parts of feldspar, 14 parts of quartz, 16 parts of calcite, 5 parts of talc, 3.9 parts of iron ore, 0.1 part of chromium oxide, 6 parts of zinc oxide.

[0032] The preparation method of above-mentioned emerald green glaze, comprises the following steps:

[0033] (1) Preparation of glaze slurry: Add appropriate amount of water to mix the above raw materials, and ball mill to obtain glaze slurry with a mass concentration of 56%;

[0034] (2) Glazing: Immerse the green body in the glaze slurry prepared in step (1) for a while, take it out for a while, immerse it again for a while, take it out, and use the water absorption of the green body to make the glaze slurry evenly adhere to the surface of the green body; the thickness of the glaze 1.6mm;

[0035] (3) Firing, the firing temperature is 1310°C;

[0036] The firing process specifically includes...

Embodiment 3

[0042] An emerald green glaze, which is prepared from the following raw materials in parts by weight: 12 parts of this medicine, 39 parts of feldspar, 16 parts of quartz, 16 parts of calcite, 5 parts of talc, 4.1 parts of iron ore, 0.1 part of chromium oxide, 6 parts of zinc oxide.

[0043] The preparation method of above-mentioned emerald green glaze, comprises the following steps:

[0044] (1) Preparation of glaze slurry: Add appropriate amount of water to mix the above raw materials, and ball mill to obtain glaze slurry with a mass concentration of 57%;

[0045] (2) Glazing: Immerse the green body in the glaze slurry prepared in step (1) for a while, take it out for a while, immerse it again for a while, take it out, and use the water absorption of the green body to make the glaze slurry evenly adhere to the surface of the green body; the thickness of the glaze 1.5mm;

[0046] (3) Firing, the firing temperature is 1300°C;

[0047] The firing process specifically includes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides emerald green glaze which is prepared from, by weight, 10-16 parts of primary medicines, 39-45 parts of melilite, 11-17 parts of quartz, 13-19 parts of calcite, 4-6 parts of talcum, 3.5-4.3 parts of iron ores, 0.08-0.12 part of chromium oxide and 5-7 parts of zinc oxide. Compared with the prior art, the emerald green glaze has the advantages that iron and chromium serve as coloring agents and are fired in reducing atmosphere to form the emerald green glaze, and the emerald green glaze with pure natural colors, strong jade texture and opalescence and high yield can be prepared by firing without removing iron in raw materials.

Description

technical field [0001] The invention relates to a glaze material, in particular to an emerald green glaze. Background technique [0002] Jun porcelain is based on the thickness of the glaze. Its color is either sunken at the bottom of the glaze, or suspended in the glaze, or floating on the surface of the glaze. Jun porcelain is transformed into a god by the kiln, and the natural transformation of the kiln is the essence of Jun porcelain art, and it is also the rarity of Jun porcelain that is famous all over the world and famous in the porcelain forest. The same kind of glaze is applied during firing, and once fired, it will be colorful, that is, "one color when entering the kiln, and many colors when leaving the kiln". The ever-changing kiln transformation effect forms the magic of endless color changes. The dividends are purple, purple is dark blue, blue is white, white is red, and the colors are infiltrating and shining. known as. [0003] The key to Jun porcelain lies...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C03C2205/02C04B41/5022C04B41/86C04B41/4539C04B41/0072
Inventor 王志勇
Owner 禹州市土魂钧瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap