A kind of magnetic alloy hollow microsphere and preparation method thereof

A magnetic alloy, microsphere technology, applied in the nano field, can solve the problems of high temperature energy consumption, complicated and multi-step, harsh conditions and so on

Active Publication Date: 2021-05-04
ZHEJIANG NORMAL UNIVERSITY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above method adopts hard template, high temperature calcination or electroless plating process, so there are disadvantages such as complicated and multi-step, high temperature energy consumption, special requirements for equipment, long cycle and harsh conditions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of magnetic alloy hollow microsphere and preparation method thereof
  • A kind of magnetic alloy hollow microsphere and preparation method thereof
  • A kind of magnetic alloy hollow microsphere and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Dissolve 1.2g (12g / L) surfactant [polyvinylpyrrolidone (PVP)] in a mixed solution of 98mL pure ethylene glycol and 4.5mL deionized water and stir evenly, then add 0.6424g (0.027M) CoCl 2 ·6H 2 O and 0.4279g (0.018M) NiCl 2 ·6H 2 O electric power was stirred for 2 h, and then 2.5 mL of anhydrous hydrazine hydrate was added dropwise to the solution and stirred for 1 h. Then the mixture was heated to 197°C to boil, condensed and refluxed for four hours. After cooling, it was washed with absolute ethanol for multiple times of magnetic separation and separation until the solution was clear, and finally dried to obtain the required magnetic alloy hollow microspheres.

[0034] The phase, elemental composition and morphology of the obtained product observed under the scanning electron microscope are as follows: Figure 1~3 As shown, the particle diameter is 0.72~1.68μm, and the wall thickness is 28~73nm; figure 2 As shown, the Co / Ni atomic ratio is 1.96; the static magneti...

Embodiment 2

[0036] Same step as Example 1, but only add 1.0706g (0.045M) CoCl in the solution 2 ·6H 2 O, the morphology of the resulting product observed under the scanning electron microscope is as follows Figure 8As shown, the particle diameter is 0.84-1.85 μm, and the wall thickness is 4-17 nm. Static magnetic properties such as Figure 5 , the saturation magnetization is 152.89emu·g -1 ; Its two-dimensional reflectivity is as follows Figure 9 As shown, paraffin is used as the base, when the mass fraction is 50%, the reflectance is -18.08dB at 2GHz, and the sample thickness is 7.9mm.

Embodiment 3

[0038] Same as Example 1, but add 0.5353g (0.0225M) CoCl to the solution simultaneously 2 ·6H 2 O and 0.5348g (0.0225M) NiCl 2 ·6H 2 O. The morphology of the obtained product observed under the scanning electron microscope is as follows: Figure 10 As shown, the particle diameter is 0.76-1.82 μm, and the wall thickness is 47-78 nm. Energy spectrum analysis such as figure 2 As shown, the Co / Ni atomic ratio is 1.69. Static magnetic properties such as Figure 5 , the saturation magnetization is 105.93emu g -1 ; its electromagnetic parameters such as Figure 5-6 As shown, in the frequency range of 2-18GHz, the real part and imaginary part of the permittivity increase by 0.75-1.39 and 0.21-0.79 times respectively compared with the hollow Co sphere, and the real part and imaginary part of the permeability increase by 0.98-1.02 compared with the and 0.11 to 0.96 times. Its two-dimensional reflectivity is as Figure 11 As shown, paraffin is used as the base, when the mass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a magnetic alloy hollow microsphere and a preparation method thereof. The components of the microspheres are cobalt and nickel, and its structural formula is Co x Ni 1‑x , where: 0.14≤x≤1; it has a hollow structure with a diameter of 0.32-3.35μm and a wall thickness of 4-370nm; its saturation magnetization is 80.4-152.89emu·g –1 . The microspheres are made by the mixed solvent high-temperature liquid phase reduction method: first add the organic solvent, water and surfactant into the three-necked flask according to a certain ratio, and stir for 10 minutes; then add the metal salt and stir for 2 hours, and drop the reducing agent Electric stirring for 1 hour, then condensing and reflux at 170-197°C for 3-4 hours, cooling, washing with ethanol for multiple magnetic separation, and finally drying to obtain the required magnetic alloy hollow microspheres. The raw materials of the invention are cheap and easy to obtain, low in cost, simple in process, high in efficiency, and easy to popularize; the magnetic ball chain has the characteristics of adjustable size and composition, and can be used in magnetorheology, magnetic separation, catalysis, electrode materials, microwave absorption or high density Applications in magnetic recording materials.

Description

technical field [0001] The invention relates to the field of nanotechnology, in particular to a simple method for preparing magnetic alloy hollow microspheres. Background technique [0002] Due to their unique electrical, optical, magnetic and excellent chemical properties, magnetic metal nanomaterials have been widely used in nuclear magnetic resonance imaging, optical nanodevices, targeted drugs, magnetic storage, catalysts, etc. Among them, hollow magnetic micro-nano materials have attracted much attention because of their low density, high specific surface area, low thermal expansion coefficient and refractive index. The methods for preparing hollow microspheres mainly include traditional hard template method, sacrificial template synthesis method, soft template preparation method and template-free method. At present, only a few literatures and patents report the preparation of magnetic metal / alloy hollow microspheres. Chinese patent document (CN201510083390.8) disclos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/24B22F1/00B82Y30/00B82Y40/00
CPCB82Y30/00B82Y40/00B22F9/24B22F1/0549B22F1/0655B22F1/07B22F1/054
Inventor 童国秀刘琳孙嘉诚乔儒陈锦绣宫培军韩佳女胡潘冰吴文华
Owner ZHEJIANG NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com