Lightweight wear-resistant aluminum alloy softball bat material and preparation method thereof

An aluminum alloy and softball technology, applied in the field of aluminum alloys, can solve the problems of many surface pits, poor wear resistance, and easy breakage of the bat, and achieve the effect of refining grains, good wear resistance, and improving mechanical properties.

Inactive Publication Date: 2018-09-25
TIANCHANG ZHENGMU ALUMINUM TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, metal bats are mainly used. Aluminum bats are widely used because of their advantages of light weight, no running-in, and better durability. However, they have poor wear resistance and low hardness. Long-term used bats are easy to break and have many surface pits. , cannot meet people's needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A light wear-resistant aluminum alloy softball bat material, its raw materials include: zinc 0.5wt%, silicon 0.4wt%, titanium 0.2wt%, beryllium 0.05wt%, nano palladium-niobium-silicon carbide mixed powder 0.1wt %, the balance is aluminum.

[0019] Nano-palladium-niobium-silicon nitride mixed powder is prepared by the following process: after adding palladium into a furnace at a temperature of 1600 ° C to melt, add niobium powder and silicon carbide powder and mix evenly, and then atomize and granulate to obtain a mixture powder; the mixture The powder was put into a ball mill and ball milled at a speed of 100 r / min for 3 hours to obtain a nano-palladium-niobium-silicon carbide mixed powder.

Embodiment 2

[0021] A light wear-resistant aluminum alloy softball bat material, its raw materials include: zinc 1.5wt%, silicon 0.8wt%, titanium 0.4wt%, beryllium 0.08wt%, nano palladium-niobium-silicon carbide mixed powder 0.3wt %, the balance is aluminum.

[0022] Nano-palladium-niobium-silicon nitride mixed powder is prepared by the following process: after adding palladium into a furnace at a temperature of 1700 ° C to melt, add niobium powder and silicon carbide powder and mix evenly, and then atomize and granulate to obtain a mixture powder; the mixture The powder was put into a ball mill and ball milled at a speed of 200r / min for 4 hours to obtain a nano-palladium-niobium-silicon carbide mixed powder.

Embodiment 3

[0024] A light wear-resistant aluminum alloy softball bat material, its raw materials include: zinc 0.8wt%, silicon 0.5wt%, titanium 0.25wt%, beryllium 0.06wt%, nano palladium-niobium-silicon carbide mixed powder 0.15wt by weight percentage %, the balance is aluminum.

[0025] Nano-palladium-niobium-silicon nitride mixed powder is prepared by the following process: add palladium into a furnace at a temperature of 1650 ° C to melt, add niobium powder and silicon carbide powder and mix evenly, and then atomize and granulate to obtain a mixture powder; the mixture Add the powder into a ball mill and mill it at a speed of 140r / min for 3.3h to prepare nano palladium-niobium-silicon carbide mixed powder

[0026] The preparation method of the above-mentioned lightweight wear-resistant aluminum alloy softball bat material comprises the following steps:

[0027] S1, press C 2 Cl 6 The weight ratio to aluminum is 0.3:100. Aluminum, zinc, silicon, titanium, beryllium, and refining age...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a lightweight wear-resistant aluminum alloy softball bat material, which is prepared from zinc, silicon, titanium, beryllium, a nano-palladium-niobium-silicon carbide powder mixture, and the balance of aluminum. The invention also provides a preparation method of the lightweight wear-resistant aluminum alloy softball bat material. The preparation method comprises the following steps: adding aluminum, zinc, silicon, titanium, beryllium and a refining agent into a melting furnace, melting at high temperature and removing slag, so as to obtain a mixing solution; adding thenano-palladium-niobium-silicon carbide powder mixture into the mixing solution, carrying out ultrasonic treatment and heat preservation, casting for molding, and cooling to room temperature, so as toobtain the lightweight wear-resistant aluminum alloy softball bat material. The aluminum alloy material has light weight and good wear resistance, and is suitable for use in a softball bat.

Description

technical field [0001] The invention relates to the technical field of aluminum alloys, in particular to a lightweight wear-resistant aluminum alloy softball bat material and a preparation method thereof. Background technique [0002] Softball is developed from baseball. Compared with baseball, softball requires a small field, a large ball, and slow ball speed, which are widely loved by people. A softball bat is a stick used to hit the ball in a softball game. It is commonly made of metal, bamboo, plastic, carbon lead, magnesium, fiberglass, ceramics or other synthetic materials. At present, metal bats are mainly used. Aluminum bats are widely used because of their advantages of light weight, no running-in, and better durability. However, they have poor wear resistance and low hardness. Long-term used bats are easy to break and have many surface pits. , cannot meet people's needs. Contents of the invention [0003] Based on the technical problems existing in the backgrou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/02C22C21/10C22C32/00C22C1/10B22F9/08B22F9/04B82Y40/00
CPCC22C1/1005C22C1/1036C22C21/02C22C21/10C22C32/0063B82Y40/00B22F9/04B22F9/082B22F2009/043C22C1/1047
Inventor 周良正
Owner TIANCHANG ZHENGMU ALUMINUM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap