PP precoating film
A pre-coating and sticking technology, applied in the direction of lamination, layered products, synthetic resin layered products, etc., can solve problems such as poor adhesion, and achieve the effect of strong bonding force
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] A PP pre-coating film formed by three-layer co-extrusion of the first layer, the second layer and the core layer, with a thickness of 30 μm;
[0018] The raw material components and weight percentages of the first layer are: PP 85%, anti-adhesive agent 5%, and the balance is polycarbonate functional masterbatch;
[0019] The raw material components and weight percentages of the first layer are: PP 85%, anti-sticking agent 15%;
[0020] The raw material components and weight percentage of the core layer are: 95% of PP, 2% of antistatic agent, and the balance of slippery agent.
[0021] The anti-sticking agent consists of 25 parts of water-based acrylic modified epoxy resin, 10 parts of titanium dioxide, 3 parts of tetraethylamine tetrafluoroborate, 3 parts of light calcium carbonate, 5 parts of solvent, 2 parts of oridonin and Flufenacet 2 parts made.
[0022] During molding, the main extruder temperature is 230°C, the water tank temperature is 30°C, the cold roll temp...
Embodiment 2
[0024] A PP pre-coating film formed by three-layer co-extrusion of the first layer, the second layer and the core layer, with a thickness of 10 μm;
[0025] The raw material components and weight percentages of the first layer are: 92% PP, 2% anti-adhesive agent, and the balance is polycarbonate functional masterbatch;
[0026] The raw material components and weight percentages of the first layer are: 92% PP, 8% anti-sticking agent;
[0027] The raw material components and weight percentages of the core layer are: 97% of PP, 1% of antistatic agent, and the balance of slip agent.
[0028] The anti-sticking agent consists of 50 parts of water-based acrylic modified epoxy resin, 7 parts of titanium dioxide, 6 parts of tetraethylamine tetrafluoroborate, 1 part of light calcium carbonate, 15 parts of solvent, 1 part of oridonin and Flufenacet 4 parts are made.
[0029] During molding, the main extruder temperature is 220°C, the water tank temperature is 35°C, the cold roll temper...
Embodiment 3
[0031] A PP pre-coating film formed by three-layer co-extrusion of the first layer, the second layer and the core layer, with a thickness of 20 μm;
[0032] The raw material components and weight percentages of the first layer are: PP 90%, anti-adhesive agent 4%, and the balance is polycarbonate functional masterbatch;
[0033] The raw material components and weight percentages of the first layer are: PP88%, anti-sticking agent 12%;
[0034] The raw material components and weight percentage of the core layer are: 96% of PP, 1.5% of antistatic agent, and the balance of smooth agent.
[0035] The anti-sticking agent consists of 35 parts of water-based acrylic modified epoxy resin, 9 parts of titanium dioxide, 4 parts of tetraethylamine tetrafluoroborate, 2 parts of light calcium carbonate, 11 parts of solvent, 1.6 parts of oridonin and Flufenacet 3.2 parts are made.
[0036] During molding, the main extruder temperature is 225°C, the water tank temperature is 32°C, the cold ro...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
stretch ratio | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com