Piston one-time forming process method
A molding process and piston technology, applied in the field of one-time piston molding process, can solve the problems of complicated preparation process, insufficient adhesion, poor anti-oxidation ability of piston, etc., and achieve the effect of smooth outer surface and avoiding rust spots.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0023] Example 1
[0024] A one-step forming process method for a piston, including the following steps
[0025] Preparation of blank materials: mixed materials
[0026] The components of the mixture: iron powder 100-200kg, copper powder 12-20kg, graphite 7-10kg, kaolin 10-15kg, manganese sulfide 1-5kg, differential wax 5-10kg, spindle oil 0.2-0.5kg, binder 5-10kg;
[0027] Mix the raw materials, put the mixture into the mixer, now mix 50kg of iron powder, 15kg of copper powder, 12kg of kaolin, 8.2kg of graphite, 3kg of manganese sulfide, and 7kg of differential wax. After mixing, add 0.2kg of spindle oil;
[0028] After the mixture is finished, add 50kg of iron powder to the mixer and mix for 40 minutes;
[0029] Screening material: Pour the mixed large material mixed by the mixer into the vibrating screen, and vibrate through the vibrating screen, so that the material is screened and vibrated.
[0030] Mix the raw materials, put the mixture into the mixer, now mix 50kg of iron powder, ...
Example Embodiment
[0043] Example 2
[0044] A one-step forming process method for a piston, including the following steps
[0045] Preparation of blank materials: mixed materials
[0046] The components of the mixture: iron powder 100-200kg, copper powder 12-20kg, graphite 7-10kg, kaolin 10-15kg, manganese sulfide 1-5kg, differential wax 5-10kg, spindle oil 0.2-0.5kg, binder 5-10kg;
[0047] Mix the raw materials, put the mixture into the mixer, now mix 50kg of iron powder, 15kg of copper powder, 12kg of kaolin, 8.2kg of graphite, 3kg of manganese sulfide, and 7kg of differential wax. After mixing, add 0.2kg of spindle oil;
[0048] After the mixture is finished, add 50kg iron powder to the mixer and mix for 40 minutes;
[0049] Screening material: Pour the mixed large material mixed by the mixer into a vibrating screen, and vibrate through the vibrating screen, so that the material is screened and vibrated.
[0050] Mix the raw materials, put the mixture into the mixer, now mix 50kg of iron powder, 15kg ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap