A kind of high-gloss anti-corrosion coating with rust coating on water-based bottom surface and preparation method thereof

A technology for anti-corrosion coatings and bottom surfaces, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of ignoring the importance of coating storage stability and corrosion resistance, and achieve simple procedures, good adhesion, and good anti-rust performance Effect

Active Publication Date: 2020-08-04
北京红狮科技发展有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this field, most of the existing technologies only pay attention to the above three aspects, while ignoring the importance of the storage stability and corrosion resistance of the coating itself

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-gloss anti-corrosion coating with rust coating on water-based bottom surface and preparation method thereof
  • A kind of high-gloss anti-corrosion coating with rust coating on water-based bottom surface and preparation method thereof
  • A kind of high-gloss anti-corrosion coating with rust coating on water-based bottom surface and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] The preparation of embodiment 1 coating 1

[0057] First, dissolve 0.15 parts of polyoxyethylene ether in deionized water, and use a disperser to dissolve ZrO with a particle size of 10-50nm 2 0.8 parts of nanoparticles are evenly dispersed in it, and set aside; 8 parts of mica powder, 5 parts of titanium dioxide, 1 part of Rebo-60, 1 part of MIT, 1 part of BIT, 0.8 parts of alkyltrimethylammonium chloride, and 1 part of Tego 245 Parts, 1 part of polydimethylsiloxane dispersed in deionized water, disperse for 20 minutes and then grind, when the grinding reaches about 15um, add 60 parts of acrylic emulsion, 28 parts of ethyl fumarate, 8 parts of allyl glycidyl ether 10 parts of polyisocyanate, 4 parts of ammonium persulfate, 7 parts of sodium vinyl sulfonate and ZrO 2 The nanometer solution was stirred rapidly for 3 hours, and the pH was adjusted to 9.0 with diethanolamine. The prepared paint is filtered and packed.

[0058] Comparative Example 1 Coating 2

[0059] F...

Embodiment 2

[0072] Coating 5: 10 parts of ethyl fumarate, 3 parts of allyl glycidyl ether, and the mass parts and preparation methods of the remaining components are the same as those in Example 1 to prepare Coating 5.

Embodiment 3

[0074] Coating 6: 15 parts of ethyl fumarate, 3 parts of allyl glycidyl ether, and the mass parts and preparation methods of the remaining components are the same as those in Example 1 to prepare Coating 6.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an aqueous bottom-side rust-coated highlight anticorrosive coating and a preparation method thereof. Polyenoic acid ester monomers other than acrylic acid and monomers with functional groups which have carboxylic acid reactivity and can participate in a reaction in a phased mode are added in acrylic emulsion. The coating has excellent adhesion on the surface of rusted iron,can be coated with rust, and further has the characteristics of uniformity of the bottom surface; and more importantly, the prepared coating has good coating gloss, good storage stability, and good corrosion resistance.

Description

technical field [0001] The invention relates to the technical field of metal surface anti-corrosion coating, in particular to a water-based anti-corrosion coating for bottom surface combined with rust coating and a preparation method thereof. Background technique [0002] With the rapid development of my country's economic construction and national economy, various steel structures, concrete structures, aluminum-plastic structures, etc. are more and more applied to bridges, buildings, ports, transportation and other industrial and civil projects, but they are easy to corrode. The characteristics of (rust) have brought huge economic losses to the equipment manufacturing industry, and are detrimental to natural resources and environmental protection. Among various anti-corrosion technologies, coatings play a very good role in protecting various engineering products and facilities. A series of anti-corrosion coatings have been developed at home and abroad, including rust coatin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D4/06C09D4/02C09D5/08C09D7/61
CPCC09D4/06C09D5/08C09D7/61
Inventor 李运德吴国华节昌澎
Owner 北京红狮科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com