Preparation method of ceramic fibers

A ceramic fiber and formula technology, applied in the field of ceramic fiber, can solve the problems of low ignition point of organic thermal insulation materials, not suitable for high-end equipment, and safety, and achieve the effects of excellent tensile strength, excellent chemical stability, and low heat capacity

Inactive Publication Date: 2018-10-16
CHUZHOU SANHE FIBER MFG
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional fire-resistant and thermal insulation materials are mainly divided into two categories: organic materials and inorganic materials. Organic thermal insulation materials are not suitable for high-end equipment thermal insulation due to their low ignition point and easy fire hazards.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0018] The preparation method of a kind of ceramic fiber of the present invention is described in detail below, a kind of preparation method of ceramic fiber, the formula of ceramic fiber is as follows in parts by weight: silicon dioxide 45-55 parts, aluminum oxide 40-50 parts, iron oxide 0.8-1 part, 0.1-0.25 part of sodium oxide, 0.1-0.25 part of potassium oxide, and the length of the ceramic fiber is 130-180 mm.

[0019] A kind of preparation method of ceramic fiber that the present invention proposes, comprises the following steps:

[0020] a. take above-mentioned batching and put into the melting furnace that temperature is 2000-2500 and melt;

[0021] b. The above-mentioned molten mixture material is spun into fibers through a spinning machine, and the speed of spinning is 8000-10000r / min;

[0022] c. The above-mentioned obtained fibers are gathered into the collection aniseed material, and a layered structure is formed by a conveyor belt;

[0023] d. the loose brocade ...

Embodiment 1

[0027] The ceramic fiber formula is as follows in parts by weight: 55 parts of silicon dioxide, 44 parts of aluminum oxide, 0.8 part of iron oxide, 0.1 part of sodium oxide, and 0.1 part of potassium oxide.

[0028] A preparation method of ceramic fiber, comprising the following steps:

[0029] A. take above-mentioned batching and put into the melting furnace that temperature is 2000 ℃ and melt;

[0030] b. The above-mentioned molten mixture material is spun into fibers through a spinning machine, and the speed of spinning is 8000-10000r / min;

[0031] c. The above-mentioned obtained fibers are gathered into the collection aniseed material, and a layered structure is formed by a conveyor belt;

[0032] d. the loose brocade of above-mentioned layered structure is carried out double-sided acupuncture through acupuncture machine, forms the original ceramic fiber of certain pulling force;

[0033] e. The above-mentioned original ceramic fiber is qualitatively passed through a hig...

Embodiment 2

[0037] The ceramic fiber formula is as follows in parts by weight: 50 parts of silicon dioxide, 50 parts of aluminum oxide, 0.5 part of iron oxide, 0.25 part of sodium oxide, and 0.25 part of potassium oxide.

[0038] A preparation method of ceramic fiber, comprising the following steps:

[0039] A. take above-mentioned batching and put into the melting furnace that temperature is 225 ℃ and melt;

[0040] b. The above-mentioned molten mixture material is spun into fibers through a spinning machine, and the speed of spinning is 8000-10000r / min;

[0041] c. The above-mentioned obtained fibers are gathered into the collection aniseed material, and a layered structure is formed by a conveyor belt;

[0042] d. the loose brocade of above-mentioned layered structure is carried out double-sided acupuncture through acupuncture machine, forms the original ceramic fiber of certain pulling force;

[0043] e. The above-mentioned original ceramic fiber is qualitatively passed through a hi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of ceramic fibers. A formula of the ceramic fibers comprises the following components in parts by weight: 45 to 55 parts of silicon dioxide, 40 to 50 partsof aluminum oxide, 0.8 to 1 part of iron oxide, 0.1 to 0.25 part of sodium oxide and 0.1 to 0.25 part of potassium oxide; the preparation method comprises the following steps: a, weighing the materials and putting the materials into a melting furnace with the temperature of 2000 to 2500 DEG C and melting; b, carrying out thread throwing and fiber forming on the molten mixture through a thread throwing machine, wherein a thread throwing speed is 8000 to 10000r / min; c, conveying obtained fibers into a bulk material; forming a layer spreading structure through a conveyor belt; d, carrying out double-faced needling on bulk cotton with the layer spreading structure, so as to form original ceramic fibers with a certain tensile force; e, determining the nature of the original ceramic fibers through a high-temperature box with the height of more than ten meters; f, cutting and packaging the ceramic fibers with the determined nature. The preparation method of the ceramic fibers has the advantages that the prepared ceramic fibers have light weight and the whole quality of an industrial kiln furnace can be effectively reduced; the chemical stability is good and the chemical corrosion resisting capability is relatively strong.

Description

technical field [0001] The invention belongs to the technical field of ceramic fibers, in particular to a preparation method of ceramic fibers. Background technique [0002] With the continuous improvement of the country's scientific and technological strength, more and more high-precision equipment has been introduced or developed, and applied to production activities in various industries. As for the high-precision equipment used in high- and low-temperature environments, how to realize the design of the refractory and heat-insulating materials has become a key issue at present. Traditional refractory and thermal insulation materials are mainly divided into two categories: organic materials and inorganic materials. Organic thermal insulation materials are not suitable for thermal insulation of high-end equipment because of their low ignition point and easy ignition, which poses safety hazards. Contents of the invention [0003] The invention provides a method for prepar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/14C04B35/622
CPCC04B35/14C04B35/62245C04B2235/3201C04B2235/3217C04B2235/3272
Inventor 顾春林孙宝珑
Owner CHUZHOU SANHE FIBER MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com