High manganese steel with ultra-low yield ratio and manufacturing method thereof

A manufacturing method and yield-strength ratio technology, applied in the field of high manganese steel and its manufacturing, can solve the problems of high cost, complex process, low yield-strength ratio, etc., and achieve the effects of energy saving, simple process production and high efficiency

Active Publication Date: 2018-11-02
ANGANG STEEL CO LTD
View PDF8 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] Although most of the high-manganese steels disclosed in the above documents have achieved high strength and high toughness, there are not many involving low yield ratio...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High manganese steel with ultra-low yield ratio and manufacturing method thereof
  • High manganese steel with ultra-low yield ratio and manufacturing method thereof
  • High manganese steel with ultra-low yield ratio and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0045] The technical problems involved in the present invention are solved by the following technical solutions: a high manganese steel with extremely low yield ratio and its manufacturing method, the mass percentage of its chemical composition is C 0.010%~0.090%, Si 0.15%~0.60%, Mn10.0%~16.0%, Nb 0.020%~0.040%, Ti 0.005%~0.03%, Ni 1.0%~4.0%, Al0.020%~0.060%, P≤0.020%, S≤0.010%, N≤0.0080 %, the rest is Fe and unavoidable impurities. After continuous casting, stacking and slow cooling are required for more than 72 hours. When cleaning the slab, the temperature of the slab should be controlled at 100-200°C, and the heating temperature before rolling should be 1150-1250°C; two-stage controlled rolling is adopted, and the first stage rolling starts rolling The temperature is 1150-1030°C, the final rolling temperature is 1040-980°C; the second-stage rolling start temperature is 950-850°C, the final rolling temperature is 900-750°C, and air-cooled after rolling. In addition, one of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses high manganese steel with an ultra-low yield ratio and a manufacturing method thereof. The high manganese steel comprises, by weight, 0.010-0.090% of C, 0.15-0.60% of Si, 10.0-16.0% of Mn, 0.020-0.040% of Nb, 0.005-0.03% of Ti, 1.0-4.0% of Ni, 0.020-0.060% of Al, no more than 0.020% of P, no more than 0.010% of S, no more than 0.0080% of N and the balance Fe and inevitableimpurities. Stacking for slow-cooling is conducted for more than 72 hours after continuous casting, and the temperature of a plate billet during cleaning is 100-200 DEG C; the heating temperature is 1150-1250 DEG C; at the first stage, the rolling starting temperature is 1150-1030 DEG C, and the finished rolling temperature is 1040-980 DEG C; at the second stage, the rolling starting temperature is 950-850 DEG C, the finished rolling temperature is 900-750 DEG C, and air cooling is conducted after rolling; and thermal treatment of one of normalizing, quenching, tempering or quenching + tempering is conducted after rolling. The yield ratio of the produced high manganese steel is 0.12-0.39, and the produced high manganese steel has excellent toughness and low-temperature toughness.

Description

technical field [0001] The invention belongs to the field of metal materials, in particular to a high manganese steel with extremely low yield ratio and a manufacturing method thereof. Background technique [0002] Traditional high-strength medium and heavy plate products generally adopt low carbon (0.06% ~ 0.2%) and low manganese (Mn: 1.0% ~ 1.8%), and add precious metal elements such as Cr and Mo at the same time. Production by cooling process or heat treatment process. And as the thickness of the steel plate increases, it is necessary to add a large amount of alloying elements such as Cr and Mo to improve hardenability, which greatly increases the production cost. At the same time, it is supplemented by an increase in the C content, which seriously deteriorates the weldability and low temperature toughness. Moreover, my country is a country with little Mo and no Cr resources, and the application of a large amount of precious metal elements such as Cr and Mo will highligh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/12C22C38/14C22C38/08C22C38/06C22C33/04C21D8/02
CPCC21D8/0221C21D8/0247C22C33/04C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/14
Inventor 林田子侯华兴张涛杨颖张哲
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap