A fishing net with excellent aging resistance

An anti-aging, fishing net technology, used in fishing nets, fiber chemical characteristics, fishing and other directions, can solve the problems of poor anti-aging performance of polyethylene, general mechanical properties, affecting the performance of fishing nets, etc., to prevent aging and improve durability. Effect

Active Publication Date: 2020-12-15
威海市世一网业有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Modern fishing nets are mainly processed with polyethylene, nylon and other raw materials. Among them, polyethylene fishing nets are made of polyethylene materials through melt plasticization, spinning, and ply twisting. They are used for marine trawls, purse seines, and wind-resistant sea nets. Boxes, etc., have a longer service life and higher fishing efficiency, but the mechanical properties of polyethylene itself are average. With the continuous improvement of fishing net manufacturing technology, the strength and wear resistance of fishing nets have gradually been improved. The aging performance is poor, and the use environment of the fishing net is relatively complicated, which determines that the aging of the fishing net will seriously affect the performance of the fishing net. The existing technology usually improves the weather resistance of the fishing net by adding anti-aging agents, but it will correspondingly affect the performance of the fishing net. Physical properties, therefore, further research on the weather resistance of fishing nets is required

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A fishing net with excellent aging resistance
  • A fishing net with excellent aging resistance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A fishing net with excellent aging resistance, made of 2-diphenylphosphineethyltriethoxysilane grafted with graphene oxide and modified polyethylene under melting conditions to make a masterbatch, and then made through the obtained masterbatch Fishnet line, woven into fishing nets.

[0017] Further, the preparation method of the graphene oxide is:

[0018] Mix graphite, hydrogen peroxide, and amphetamine peroxide uniformly in a mass ratio of 3:4:5, heat in a water bath to 80°C, keep warm for 30 minutes, then add them to the ball mill jar, and vacuum the ball mill jar to 0.025MPa, Carry out ball milling, the ball-to-material ratio is 100:3, and the ball milling time is 3 hours, then after washing, filtering, and drying, graphene oxide is obtained.

[0019] Further, the graphite is flake graphite.

[0020] Further, the particle size of the graphene oxide is 1800 mesh.

[0021] Further, the material of the balls used in the ball milling is a ceramic-based material.

[...

Embodiment 2

[0026] A fishing net with excellent aging resistance, made of 2-diphenylphosphineethyltriethoxysilane grafted with graphene oxide and modified polyethylene under melting conditions to make a masterbatch, and then made through the obtained masterbatch Fishnet line, woven into fishing nets.

[0027] Further, the preparation method of the graphene oxide is:

[0028] Graphite, hydrogen peroxide, and amphetamine peroxide were evenly mixed together in a mass ratio of 3:4:5, heated in a water bath to 90°C, kept for 30 minutes, then added to the ball mill jar, and the ball mill jar was evacuated to 0.028MPa, Carry out ball milling, the ball-to-material ratio is 100:3, and the ball milling time is 4 hours, then after washing, filtering, and drying, graphene oxide is obtained.

[0029] Further, the graphite is flake graphite.

[0030] Further, the particle size of the graphene oxide is 1800 mesh.

[0031] Further, the material of the balls used in the ball milling is a ceramic-based ...

Embodiment 3

[0036] A fishing net with excellent aging resistance, made of 2-diphenylphosphineethyltriethoxysilane grafted with graphene oxide and modified polyethylene under melting conditions to make a masterbatch, and then made through the obtained masterbatch Fishnet line, woven into fishing nets.

[0037] Further, the preparation method of the graphene oxide is:

[0038] Graphite, hydrogen peroxide, and amphetamine peroxide were evenly mixed together in a mass ratio of 3:4:5, heated in a water bath to 85°C, kept for 30 minutes, then added to the ball mill jar, and the ball mill jar was evacuated to 0.026MPa, Carry out ball milling, the ball-material ratio is 100:3, the ball milling time is 3-4 hours, then after washing, filtering and drying, graphene oxide is obtained.

[0039] Further, the graphite is flake graphite.

[0040] Further, the particle size of the graphene oxide is 1800 mesh.

[0041] Further, the material of the balls used in the ball milling is a ceramic-based materi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fishing net with excellent ageing-resistant performance. 2-diphenylphosphine ethyltriethoxysilane grafted oxidized graphene modifies polyethylene under the melting condition,master batches are prepared, the obtained master batches are made into fishing net threads, and the fishing net is woven by using the fishing net threads; according to the fishing net, the 2-diphenylphosphine ethyltriethoxysilane grafted oxidized graphene modifies the polyethylene fishing net, significant reinforcing and toughening effects can be achieved, and the ageing-resistant performance isimproved.

Description

technical field [0001] The invention belongs to the technical field of new materials, and in particular relates to a fishing net with excellent aging resistance. Background technique [0002] Modern fishing nets are mainly processed with polyethylene, nylon and other raw materials. Among them, polyethylene fishing nets are made of polyethylene materials through melt plasticization, spinning, and ply twisting. They are used for marine trawls, purse seines, and wind-resistant sea nets. Boxes, etc., have a longer service life and higher fishing efficiency, but the mechanical properties of polyethylene itself are average. With the continuous improvement of fishing net manufacturing technology, the strength and wear resistance of fishing nets have gradually been improved. The aging performance is poor, and the use environment of the fishing net is relatively complicated, which determines that the aging of the fishing net will seriously affect the performance of the fishing net. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A01K75/00D01F6/46D01F1/10
CPCA01K75/00D01F1/106D01F6/46
Inventor 胡海燕张俊
Owner 威海市世一网业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products