A kind of aluminum alloy welding wire containing nano-alumina particles and preparation method thereof

A technology of aluminum alloy welding wire and nano-alumina, which is applied in the field of aluminum alloy welding wire, can solve problems such as weld thermal cracking, low weld strength, and poor weld stability, so as to improve weld strength, realize weld strength, The effect of thermal stability improvement

Active Publication Date: 2020-05-19
NORTHEASTERN UNIV LIAONING
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of aluminum alloy welding wire containing nano-alumina particle and preparation method thereof, this aluminum alloy welding wire containing nano-alumina particle is a kind of containing nano-alumina particle Al-Zn-Mg-Cu-Zr- Ti-Ag-Sc-Er aluminum alloy welding wire is specially used for welding 7XXX high-strength aluminum alloys to solve the problems of weld thermal cracking, poor weld stability and low weld strength during the welding process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] An aluminum alloy welding wire containing nano-alumina particles, the components it contains and the mass percentage of each component are: n-Al2 o 3 (nano alumina) content 0.1%, Zn content 12%, Mg content 4.0%, Cu content 0.2%, Zr content 0.2%, Ag content 1.1%, Sc content 0.23%, Ti content 0.36%, Er content 0.4%, The content of other impurity elements is Fe≤0.15%, Si≤0.06%, and the balance is Al.

[0044] The n-Al 2 o 3 (Nano-alumina) Copper-plated nano-Al 2 o 3 , and its particle size is 10-15nm.

[0045] A method for preparing an aluminum alloy welding wire containing nano-alumina particles, the process is as follows:

[0046] Step 1: Low Frequency Semi-Continuous Casting

[0047] 1) According to the above alloy chemical composition and weight percentage requirements, raw materials include: pure Al, n-Al 2 o 3 (nano-alumina), pure Zn, pure Mg, Al-Cu master alloy, Al-Ti-B master alloy, Al-Er master alloy, industrial pure Ag, Al-Sc master alloy, Al-Zr master al...

Embodiment 2

[0066] An aluminum alloy welding wire containing nano-alumina particles, the components it contains and the mass percentage of each component are: n-Al 2 o 3 (nano alumina) content 0.5%, Zn content 10.5%, Mg content 4.0%, Cu content 0.4%, Zr content 0.3%, Ag content 1.2%, Sc content 0.3%, Ti content 0.2%, Er content 0.14%, The content of other impurity elements is Fe≤0.15%, Si≤0.06%, and the balance is Al.

[0067] The n-Al 2 o 3 (Nano-alumina) Copper-plated nano-Al 2 o 3 , and its particle size is 20-23nm.

[0068] A preparation method of an aluminum alloy welding wire containing nano-alumina particles, comprising the following steps:

[0069] Step 1: Low Frequency Semi-Continuous Casting

[0070] 1) Ingredients: According to the above alloy chemical composition and weight percentage requirements, the raw materials and the mass percentage of each raw material are: n-Al 2 o 3 (nano alumina) content 0.5%, Zn content 10.5%, Mg content 4.0%, Cu content 0.4%, Zr content 0...

Embodiment 3

[0089] An aluminum alloy welding wire containing nano-alumina particles, the components it contains and the mass percentage of each component are: n-Al 2 o 3 (nano alumina) content 1%, Zn content 11%, Mg content 4.2%, Cu content 0.3%, Zr content 0.4%, Ag content 1.6%, Sc content 0.35%, Ti content 0.25%, Er content 0.24%, The content of impurity elements is Fe≤0.15%, Si≤0.06%, and the balance is Al.

[0090] The n-Al 2 o 3 (Nano-alumina) Copper-plated nano-Al 2 o 3 , and its particle size is 25-30nm.

[0091] A preparation method of an aluminum alloy welding wire containing nano-alumina particles, comprising the following steps:

[0092]Step 1: Low Frequency Semi-Continuous Casting

[0093] 1) Ingredients: According to the above alloy chemical composition and weight percentage requirements, the raw materials and the mass percentage of each raw material are: n-Al 2 o 3 (nano alumina) content 1%, Zn content 11%, Mg content 4.2%, Cu content 0.3%, Zr content 0.4%, Ag conte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an aluminum alloy welding wire containing nanometer aluminum oxide particles and a preparation method thereof, and belongs to the technical field of aluminum alloy welding wires. The welding wire comprises the following components in percentage by mass: 0.1-1% of Al2O3, 10-12% of Zn, 4.0-4.4% of Mg, 0.2-0.4% of Cu, 0.2-0.4% of Zr, 1.0-2.0% of Ag, 0.2-0.4% of Sc, 0.2-0.4% ofTi, 0.1-0.4% of Er, Fe not more than 0.15%, Si not more than 0.06%, and the balance of Al; and the diameter of the welding wire is 1.2-3.0 mm. The preparation method comprises the steps of low-frequency semi-continuous casting, annealing, homogenization, extrusion and drawing. The welding wire is special for welding of 7XXX high-strength aluminum alloys, and solves the problems of hot cracking ofwelding lines in the welding process, weak stability of the welding lines, lower strength of the welding lines and the like. The welding wire is simple and operable in preparation process, lower in production cost, suitable for industrial production and broad in market prospect.

Description

technical field [0001] The invention relates to the technical field of aluminum alloy welding wire, in particular to an aluminum alloy welding wire containing nano-alumina particles and a preparation method thereof. Background technique [0002] The use of high-strength aluminum alloys instead of steel materials for weight reduction not only has an outstanding weight reduction effect, but also has unparalleled advantages in terms of cost compared with titanium alloys and composite materials. Therefore, more and more high-strength aluminum alloy structural materials are widely used instead of steel products in military and civilian fields such as aviation, aerospace and other weapons and equipment, and high-speed train tracks. The connection mode between aluminum alloy parts is changed from mechanical connection to welding seam connection. At present, the high-strength aluminum alloy plates that use aluminum instead of steel are mostly Al-Zn-Mg-Cu alloys, and their welding p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/28C22C21/10C22C1/03C22C1/10C22F1/053B23K35/40
CPCB23K35/288B23K35/40C22C1/1036C22C21/10C22F1/053
Inventor 高文林王向杰班春燕崔建忠
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com