Preparation and application of a low-hardness and high-elasticity epoxy potting adhesive for water treatment membrane components

A technology of water treatment film and high elasticity, which is applied in the direction of epoxy resin glue, adhesive, adhesive type, etc., which can solve the problems of high brittleness of epoxy resin, failure to achieve flexible packaging, and harsh use conditions, etc., to achieve excellent adhesion Excellent connection performance, excellent protection performance, and easy operation

Active Publication Date: 2021-10-26
浙江航通舟新材料科技股份有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polyurethane potting glue has good flexibility, can reduce the fracture of the end of the membrane filament, and has the advantages of low viscosity and fast curing speed, but the isocyanate group in the polyurethane potting glue is very easy to react with water, and the cured product Air bubbles reduce sealing, so its use conditions are more severe
Epoxy resin has excellent adhesion, mechanical strength and corrosion resistance, and is cost-effective. However, epoxy resin is brittle and easy to cause broken wires, so toughening modification is required
In related patents in the field, a variety of toughening agents are applied to epoxy resin potting adhesives, such as liquid rubber (patent CN201210256771.8), low-molecular polyurethane or polyol glycidyl ether (CN201410606987.1), rubber / dipolymer Acid / polyurethane-modified epoxy resin (CN201611229888.1, CN201710552507.1), but the hardness of the epoxy resin cured product described in each technical solution is only Shore hardness A70-A80 at the lowest, which does not reach the real flexible packaging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation and application of a low-hardness and high-elasticity epoxy potting adhesive for water treatment membrane components

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] 70 parts by weight of E-51, 8 parts by weight of butyl glycidyl ether, 10 parts by weight of epoxy-terminated polyurethane, 9.9 parts by weight of talc, 0.1 parts by weight of KH-550, 2 parts by weight of polyoxygen Ethylene polyoxypropylene pentaerythritol ether was mixed and stirred evenly to obtain component A; 50 parts by weight of polyetheramine D400, 40 parts by weight of Baxxodur EC252, 10 parts by weight of 2,4,6-tris(dimethylaminomethyl) Mix phenol with light and stir component B; mix component A and component B at a weight ratio of 100:50 and stir evenly to obtain a low-hardness and high-elasticity epoxy potting glue.

Embodiment 2

[0047]50 parts by weight of E-51, 10 parts by weight of benzyl glycidyl ether, 10 parts by weight of o-cresyl glycidyl ether, 20 parts by weight of epoxy-terminated polyurethane, 6.9 parts by weight of titanium dioxide, 3 parts by weight of KH-570, 0.1 parts by weight of glycerol polyether stearic acid triester were mixed and stirred evenly to obtain component A; 20 parts by weight of Baxxodur EC310, 70 parts by weight of Baxxodur EC210, 10 parts by weight of 2,4,6- Mix tri(dimethylaminomethyl)phenol with light and stir component B; mix and stir components A and B at a weight ratio of 100:20 to obtain a low-hardness and high-elasticity epoxy potting glue.

Embodiment 3

[0049] 30 parts by weight of E-44, 10 parts by weight of 1,4-butanediol diglycidyl ether, 8 parts by weight of ethylene glycol diglycidyl ether, 20 parts by weight of epoxy-terminated polyethylene glycol, 30 parts by weight of fumed silica, 1 part by weight of KH-560, and 1 part by weight of nonylphenol polyoxyethylene ether were mixed and stirred evenly to obtain component A; 40 parts by weight of D2000, 45 parts by weight of TAC-900 , 10 parts by weight of 2,4,6-tris-2-ethylhexanoate of 6-tris(dimethylaminomethyl)phenol, 5 parts by weight of salicylic acid mixed with light and stirring component B; group A Part and B component are mixed and stirred evenly at a weight ratio of 100:10 to obtain a low-hardness and high-elasticity epoxy potting glue.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Shore hardnessaaaaaaaaaa
Shore hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses the preparation and application of epoxy potting adhesive for water treatment membrane components with low hardness and high elasticity. The epoxy potting glue includes A component and B component, and the A component includes 30-70 parts of epoxy resin; 5-20 parts of reactive diluent; 10-20 parts of toughening agent; 5-30 parts of filler; 0.1 to 3 parts of coupling agent; B component includes 20 to 50 parts of polyetheramine; 40 to 70 parts of alicyclic amine; 2 to 15 parts of curing accelerator; the weight ratio of the A component and the B component is 100 :10~100:50. The present invention realizes the characteristics of low hardness, high elasticity and stable hardness of the epoxy potting glue through the "trinity" toughening modification method of flexible toughening agent, active toughening diluent and flexible curing agent ; and while the epoxy potting glue has excellent bonding performance, it has low initial viscosity, fast mold filling speed, and easy operation, which can greatly improve the sealing efficiency of the membrane module, and is suitable for the packaging of water treatment membrane modules and the flexibility of electronic devices. Packaging and other fields.

Description

technical field [0001] The invention relates to an adhesive, in particular to the preparation and application of a low-hardness and high-elasticity epoxy potting glue for water treatment membrane components. Background technique [0002] With the development of society and economy, human beings consume more and more water resources, and problems such as shortage of fresh water resources and water pollution are becoming more and more serious. Membrane water treatment technology is an energy-saving and high-efficiency purification technology. Its process uses a selectively permeable membrane as the separation medium. When there are driving forces such as pressure and concentration differences on both sides of the membrane, its uniform pore size is used to intercept water. Particles, bacteria and other substances to achieve the purpose of separation and purification. Hollow fiber membrane is a kind of separation membrane with high surface area, fibrous shape and self-supportin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J163/00C08G59/50
CPCC08G59/5026C09J163/00
Inventor 胡宏军朱增裕
Owner 浙江航通舟新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap