Steel slag powder grinding aid for improving particle aggregation, and preparation method thereof

A technology of particle aggregation and steel slag powder, which is applied in the field of mineral powder grinding, can solve the problems of reducing grinding efficiency, impact on cement performance, and production decline, and achieve the effects of improving grinding efficiency, reducing the tendency of aggregation, and reducing surface tension

Inactive Publication Date: 2019-01-22
浙江长盈建材科技有限公司
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen that if the cladding and aggregation in the grinding process reduce the grinding efficiency, the output will decrease, the power consumption will increase, and even the performance of cement will be affected.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The steel slag powder grinding aid for improving particle aggregation in this embodiment, at normal temperature, selects the following raw materials in sequence according to the weight ratio of the components, and after each component is fully dissolved, the next component is added:

[0015] 45kg of water, 4kg of industrial salt, 2kg of soda, 4kg of sodium nitrite, 2kg of urea, 15kg of complex alcohol amines, 17kg of glycerin, and 4kg of sugar. When grinding steel slag powder, the mixing amount of the steel slag powder grinding aid for improving particle aggregation in this embodiment is 0.02% of the total amount of steel slag powder to be ground. Wherein the composite alcohol amine mainly comprises monoethanolamine, diethylene glycol, diethanolamine, dipropylene glycol, tripropylene glycol, triisopropanolamine etc., in the present embodiment composite alcohol amine is modified monoethanolamine and Combination of diethanolamine.

Embodiment 2

[0017] The steel slag powder grinding aid for improving particle aggregation in this embodiment, at normal temperature, selects the following raw materials in sequence according to the weight ratio of the components, and after each component is fully dissolved, the next component is added:

[0018] 46kg of water, 5kg of industrial salt, 3kg of soda, 5kg of sodium nitrite, 3kg of urea, 16kg of complex alcohol amines, 18kg of glycerin, and 5kg of sugar. When grinding steel slag powder, the mixing amount of the steel slag powder grinding aid for improving particle aggregation in this embodiment is 0.03% of the total amount of steel slag powder to be ground. Wherein the composite alcohol amine mainly includes monoethanolamine, diethylene glycol, diethanolamine, dipropylene glycol, tripropylene glycol, etc., and in this embodiment, the composite alcohol amine is a combination of modified monoethanolamine and diethanolamine.

Embodiment 3

[0020] The steel slag powder grinding aid for improving particle aggregation in this embodiment, at normal temperature, selects the following raw materials in sequence according to the weight ratio of the components, and after each component is fully dissolved, the next component is added:

[0021] 47kg of water, 6kg of industrial salt, 2kg of soda, 4kg of sodium nitrite, 4kg of urea, 17kg of complex alcohol amines, 19kg of glycerin, and 4kg of sugar. When grinding steel slag powder, the mixing amount of the steel slag powder grinding aid for improving particle aggregation in this embodiment is 0.04% of the total amount of steel slag powder to be ground. Wherein the composite alcohol amine mainly includes monoethanolamine, diethylene glycol, diethanolamine, dipropylene glycol, tripropylene glycol, etc., and in this embodiment, the composite alcohol amine is a combination of modified monoethanolamine and diethanolamine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A steel slag powder grinding aid for improving particle aggregation comprises, by weight, 45-48 parts of water, 4-6 parts of industrial salt, 2-3 parts of anhydrous sodium sulfate, 4-5 parts of sodiumnitrite, 2-4 parts of urea, 15-17 parts of compound alcohol amine, 17-20 parts of glycerol and 4-5 parts of sugar. The steel slag powder grinding aid can improve the grinding efficiency, improve theyield, reduce the power consumption of a mill, save energy and reduce the cost.

Description

technical field [0001] The invention relates to the technical field of mineral powder grinding, in particular to a steel slag powder grinding aid for improving particle aggregation and a preparation method thereof. Background technique [0002] Grinding aids are a kind of chemical admixtures. Adding a small amount or a small amount of this substance in the cement grinding process can improve the grinding efficiency and eliminate or reduce the phenomenon that hinders the normal grinding work. The aggregation of cement technology into large particles belongs to the macroscopic aspect, and the microscopic phenomenon is the re-healing of the cracks caused by the external force of the particles. During the operation of the pulverizer, the material and its temperature, the roughness of the grinding medium and the surface of the component will aggravate the formation of cladding and accumulation. When the grinding limit is reached, the material reaches a state of uniform quality, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/38C04B103/52
CPCC04B40/0039C04B2103/52C04B22/08C04B22/10C04B22/085C04B24/126C04B24/122C04B24/026C04B24/38
Inventor 顾会良钱如伟顾树美沈军刘海峰沈建荣
Owner 浙江长盈建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com