Waste asphalt regeneration method

A technology of waste asphalt and recycled asphalt, which is applied in the field of waste asphalt regeneration, can solve the problems of complicated operation steps and long working hours, and achieve the effect of avoiding harmful gases and increasing the flash point

Active Publication Date: 2019-02-19
CHANGSHA UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF13 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The previous method took too long and the operation steps were complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waste asphalt regeneration method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A kind of asphalt regeneration method, the regeneration additive used is composed of, calculated in parts by weight:

[0038] Naphthenic oil 60%

[0039] Petroleum resin 30%

[0040] Ethyl Acrylate 2%

[0041] Methyl methacrylate 4%

[0042] Cellulose 2%

[0043] Styrene 2%.

[0044] Concrete asphalt regeneration method comprises the following steps:

[0045] The waste asphalt is milled from the road surface, crushed and screened,

[0046] Mix waste asphalt aggregates, fillers, asphalt emulsifiers, recycled asphalt additives, and stir and mix,

[0047] Compact the mixture described in the previous step;

[0048] The composition of the mixture comprises: 70% (weight) of waste asphalt, 23% (weight) of aggregate, 2% (weight) of filler, 1% (weight) of asphalt emulsifier, and 4% (weight) of recycled asphalt additive.

[0049] Portland cement is selected as aggregate; limestone is selected as filler; quaternary ammonium salt emulsifier is selected as asphalt emulsifie...

Embodiment 2

[0052] A kind of asphalt regeneration method, the regeneration additive used is composed of, calculated in parts by weight:

[0053] Naphthenic oil 70%

[0054] Petroleum resin 20%

[0055] Ethyl Acrylate 3%

[0056] Methyl methacrylate 3%

[0057] Cellulose 1%

[0058] Styrene 3%

[0059] Concrete asphalt regeneration method comprises the following steps:

[0060] The waste asphalt is milled from the road surface, crushed and screened,

[0061] Mix waste asphalt aggregates, fillers, asphalt emulsifiers, recycled asphalt additives, stir and mix, and compact the mixture described in the previous step;

[0062] The composition of the mixture includes: 60% (weight) of waste asphalt, 30% (weight) of aggregate, 2% (weight) of filler, 5% (weight) of asphalt emulsifier, and 3% (weight) of recycled asphalt additive.

[0063] Portland cement and steelmaking slag are selected as aggregates; slaked lime is selected as filler; alkylamide polyamine asphalt emulsifier is selected as ...

Embodiment 3

[0066] A kind of asphalt regeneration method, the regeneration additive used is composed of, calculated in parts by weight:

[0067]Naphthenic oil 60%

[0068] Petroleum resin 20%

[0069] Ethyl Acrylate 5%

[0070] Methyl methacrylate 5%

[0071] Cellulose 5%

[0072] Styrene 5%.

[0073] Concrete asphalt regeneration method comprises the following steps:

[0074] The waste asphalt is milled from the road surface, crushed and screened,

[0075] Mix waste asphalt aggregates, fillers, asphalt emulsifiers, recycled asphalt additives, stir and mix, and compact the mixture described in the previous step;

[0076] The composition of the mixture comprises: 65% (weight) of waste asphalt, 30% (weight) of aggregate, 2% (weight) of filler, 1% (weight) of asphalt emulsifier, and 2% (weight) of recycled asphalt additive.

[0077] Portland cement or steelmaking slag is used as aggregate; fly ash is selected as filler; quaternary ammonium salt emulsifier is selected as asphalt emulsi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flash pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a waste asphalt mixture regeneration method. The method includes the following steps of milling a waste asphalt mixture from pavement, conducting crushing and screening, mixing waste asphalt aggregate, fillers, an asphalt emulsifier and a recycled asphalt additive, conducting stirring and mixing, and compacting the mixture above, wherein the mixture is composed of, by weight, 40-70% of the waste asphalt, 23-50% of the aggregate, 2-4% of the fillers, 1-5% of the asphalt emulsifier and 4-6% of the recycled asphalt additive, the flash point of the recycled asphalt additive is higher than 250 DEG C, the kinematic viscosity (35 DEG C, SFS) is 15-85, then the viscosity ratio after heating is 2.0-3.0%, and the change in weight after heating does not exceed 0.3%. The asphalt regeneration method using the additive can realize the waste asphalt regeneration process at the room temperature.

Description

technical field [0001] The present application relates to a method for regenerating waste asphalt, in particular to a method for regenerating pavement asphalt. Background technique [0002] After the asphalt pavement has experienced long-term rain, snow and rutting pressure, the internal structure of the pavement will undergo great changes, such as the decline in fatigue resistance, elasticity and strength. If the asphalt pavement is not repaired and regenerated in time, the structure of the pavement will be damaged, which will cause hidden dangers to driving safety. Asphalt pavement recycling technology refers to the old asphalt pavement that needs to be refurbished or discarded, after being excavated, recycled, heated, crushed and screened by special equipment for pavement regeneration, and regenerated agent, new asphalt, new aggregate, etc. in a certain proportion It is a complete process of re-mixing into a mixture to meet certain road performance and re-paving on the r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L91/00C08L57/02C08L1/02
CPCC08L95/00C08L2205/035C08L2207/20C08L91/00C08L57/02C08L1/02
Inventor 刘宏富夏诚东黄拓杨新宇于华南黄梅芳杨晨熙
Owner CHANGSHA UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com