Stiffness and toughness balanced ternary blend alloy material and preparation method thereof

A gold material and toughness technology, applied in the field of ternary blended gold materials and their preparation, can solve the problems of low notched impact strength and flexural modulus of POK materials, and achieve easy control of technology, excellent chemical resistance, and excellent mechanical properties. Effect

Active Publication Date: 2019-02-22
SHANGHAI GAOXINKE PLASTIC PROD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The object of the present invention is to provide a ternary blended alloy material with balanced rigidity and toughness and its preparation method. The ternary blended alloy material with balanced rigidity and toughness and its preparation method should solve the problems in the prior art. The technical problem of low notched impact strength and flexural modulus of POK material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stiffness and toughness balanced ternary blend alloy material and preparation method thereof
  • Stiffness and toughness balanced ternary blend alloy material and preparation method thereof
  • Stiffness and toughness balanced ternary blend alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Bake 90 parts by weight of polyketone POK (M630A, Hyosung Korea) at 100-110°C for 4-6 hours, and 5 parts by weight of nylon elastomer (PEBAX 5533, Arkema) at 90-100°C for 4- After 6 hours, 5 parts by weight of nylon 6 (1010C2, DSM) was baked at 100-110°C for 4-6 hours, mixed with 0.1 parts by weight of primary antioxidant 1076, 0.2 parts by weight of auxiliary antioxidant 168, and 0.1 parts by weight Parts of lubricant EBS (ethylene bis stearamide), 0.1 parts by weight of nucleating agent CAV102P of Clariant, Germany. Add it to a high-speed mixer and mix evenly. The mixing temperature does not exceed 90°C and the mixing time is less than 30 minutes. Put the uniformly mixed material into the co-rotating twin-screw extruder, melt and extrude, the extrusion temperature is 230-260°C, the screw speed is 300-500r / min, the vacuum degree is -0.04MPa~-0.1MPa; Cool in a sink and chop into pieces. The prepared raw material is a ternary blend alloy material with balanced rigidity...

Embodiment 2

[0042] Bake 80 parts by weight of polyketone POK (M630A, Hyosung Korea) at 100-110°C for 4-6 hours, and 5 parts by weight of nylon elastomer (PEBAX 5533, Arkema) at 90-100°C for 4- After 6 hours, 15 parts by weight of nylon 6 (1010C2, DSM) was baked at 100-110°C for 4-6 hours, mixed with 0.1 parts by weight of primary antioxidant 1076, 0.2 parts by weight of auxiliary antioxidant 168, and 0.1 parts by weight The lubricant EBS (ethylene bis stearamide) of part, the nucleating agent CAV 102P of German Clariant company of 0.1 weight part. . Add it to a high-speed mixer and mix evenly. The mixing temperature does not exceed 90°C and the mixing time is less than 30 minutes. Put the uniformly mixed material into the co-rotating twin-screw extruder, melt and extrude, the extrusion temperature is 230-260°C, the screw speed is 300-500r / min, the vacuum degree is -0.04MPa~-0.1MPa; Cool in a sink and chop into pieces. The prepared raw material is a ternary blend alloy material with bal...

Embodiment 3

[0044] Bake 70 parts by weight of polyketone POK (M630A, Hyosung Korea) at 100-110°C for 4-6 hours, and 5 parts by weight of nylon elastomer (PEBAX 5533, Arkema) at 90-100°C for 4- After 6 hours, 25 parts by weight of nylon 6 (1010C2, DSM) was baked at 100-110°C for 4-6 hours, mixed with 0.1 parts by weight of primary antioxidant 1076, 0.2 parts by weight of auxiliary antioxidant 168, and 0.1 parts by weight The lubricant EBS (ethylene bis stearamide) of part, the nucleating agent CAV 102P of German Clariant company of 0.1 weight part. Add it to a high-speed mixer and mix evenly. The mixing temperature does not exceed 90°C and the mixing time is less than 30 minutes. Put the uniformly mixed material into the co-rotating twin-screw extruder, melt and extrude, the extrusion temperature is 230-260°C, the screw speed is 300-500r / min, the vacuum degree is -0.04MPa~-0.1MPa; Cool in a sink and chop into pieces. The prepared raw material is a ternary blend alloy material with balanc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
hardnessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a stiffness and toughness balanced ternary blend alloy material which is prepared from the following components in parts by weight: 30-90 parts of POK polyketone, 5-30 parts ofnylon elastomers, 5-70 parts of PA6, 0.05-0.3 part of a nucleating agent, 0.05-1 part of a lubricating agent, 0.05-0.3 part of a primary antioxidant and 0.05-0.3 part of an auxiliary antioxidant. Theinvention further provides a preparation method of the ternary blend alloy material. The preparation method comprises the following steps: mixing the components in parts by weight, and performing melt extrusion granulating by a twin-screw extruder unit, thereby obtaining the ternary blend alloy material disclosed by the invention. Compared with ordinary POK or nylon, the ternary blend alloy material disclosed by the invention maintains low water-absorbing quality and high wear resistance of the POK material, the characteristics of the nylon material such as high modulus and excellent chemicalresistance are additionally increased, and another function that is not owned by the two is increased, namely, the excellent characteristic of high toughness.

Description

technical field [0001] The invention relates to the field of chemistry, in particular to polymer plastic alloy composite materials, in particular to a ternary blend alloy material with balanced rigidity and toughness and a preparation method thereof. Background technique [0002] POK polyketone (polyketone) is a kind of crystalline engineering plastic with excellent comprehensive performance developed and produced by Korea Hyosung Group. material. [0003] The material has high heat distortion temperature, chemical resistance, hydrolysis resistance, fuel resistance, high friction resistance, low gas permeability, high barrier property, etc., and its wear resistance is more than 14 times that of POM. [0004] Polyketone POK was successfully developed by Hyosung for the first time. It mainly uses a new polymer material composed of carbon monoxide, which is a serious air pollutant, and petrochemical raw materials (ethylene, propylene). The advantages of polyketone are wear re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L73/00C08L77/00C08L77/02
CPCC08L73/00C08L2205/03C08L77/00C08L77/02
Inventor 周扬波郑晓清李文国黄锦河陈建和
Owner SHANGHAI GAOXINKE PLASTIC PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More