Hand die wax and preparing method and application thereof

A hand mold, wax liquid technology, applied in decorative art, decorative structure and other directions, can solve problems such as high brittleness, and achieve the effect of smooth molding

Active Publication Date: 2019-03-08
GUANGZHOU DEXIN WAX PROD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Based on this, it is necessary to provide a hand mold wax with high toughness and smooth mol

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hand die wax and preparing method and application thereof
  • Hand die wax and preparing method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0038] Refer to figure 1 , The preparation method of hand mold wax in one embodiment includes the following steps:

[0039] S110. According to the mass percentage, weigh the raw materials for the preparation of hand-molded wax. The raw materials for the preparation of hand-molded wax include: 60%-85% petroleum wax, 1%-15% flow modifier, 1%-10% The toughening agent and 8% to 20% stiffness agent.

[0040] Among them, the petroleum wax is selected from at least one of fully refined paraffin wax with a melting point lower than 55°C, semi-refined paraffin wax with a melting point lower than 55°C, and microcrystalline wax with a melting point lower than 80°C. Specifically, the fully refined paraffin wax with a melting point lower than 55°C is selected from at least one of 52# fully refined paraffin wax and 54# fully refined paraffin wax, and the semi-refined paraffin wax with a melting point lower than 55°C is selected from 52# semi-refined paraffin wax and 54# At least one of semi-ref...

Example Embodiment

[0054] Example 1

[0055] (1) In terms of mass percentage, weigh out 85% of 52# fully refined paraffin wax, 5.6% of amorphous α-olefin copolymer, 8% of stearic acid, 0.1% of dibutylhydroxytoluene, 0.1% % Toner and 1.2% C5 hydrogenated petroleum resin;

[0056] (2) Add 52# fully refined paraffin wax to the reaction kettle, adjust the working temperature of the reactor to 100°C, make 52# fully refined paraffin wax uniformly melt, and obtain basic wax liquid A;

[0057] (3) Add the amorphous α-olefin copolymer, stearic acid, dibutylhydroxytoluene and toner to the basic wax liquid A, control the temperature to 100°C, and stir for 1 hour at a stirring speed of 450r / min to obtain Wax B;

[0058] (4) Add C5 hydrogenated petroleum resin to wax liquid B, adjust the kinematic viscosity of wax liquid at 80℃ to 5.2mm 2 / s, continue to stir at 100°C for 1 h, and cool to room temperature to obtain hand mold wax.

Example Embodiment

[0059] Example 2

[0060] (1) In terms of mass percentage, weigh 54.7% of 52# fully refined paraffin wax, 5.3% of W445 microcrystalline wax, 9.8% of oligomers, 12.8% of stearic acid, 2.1% of low molecular weight polystyrene Ethylene, 0.5% tert-butyl hydroquinone, 0.2% toner, 9.8% terpene resin and 4.8% diisononyl phthalate;

[0061] (2) Add 52# fully refined paraffin wax and W445 microcrystalline wax to the reaction kettle, adjust the working temperature of the reaction kettle to 100°C, so that the waxes are uniformly melted to obtain basic wax liquid A;

[0062] (3) Add oligomers, stearic acid, low molecular weight polystyrene, tert-butyl hydroquinone and toner to the basic wax liquid A, control the temperature at 110°C, and stir at a stirring speed of 550r / min 1h, get wax liquid B;

[0063] (4) Add terpene resin and diisononyl phthalate to wax liquid B, adjust the kinematic viscosity of wax liquid at 80℃ to 14.7mm 2 / s (80°C), continue to stir at 110°C for 1 hour, and cool to obtai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melting pointaaaaaaaaaa
Melting pointaaaaaaaaaa
Kinematic viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to hand die wax and a preparing method and application thereof. According to the mass percent, raw materials for preparing the hand die wax include 60%-85% of petroleum wax, 1%-15% of a flow modifier, 1%-10% of a toughening agent and 8%-20% of a stiffening agent. In the hand die wax, the toughening agent, the stiffening agent and the flow modifier are added, a certain proportion is adopted, the tenacity and rigidity of the hand die wax can be adjusted through the toughening agent and the stiffening agent, the rigidity and the tenacity of the prepared hand die wax are balanced, and accordingly during hand die wax shell stripping, the hand die wax cannot be damaged. Through the flow modifier, the hand die wax can have certain mobility when achieving certain bonding performance, so that the hand die wax is smoothly formed, and the phenomenon of flow line filament drawing is avoided.

Description

technical field [0001] The invention relates to the technical field of wax materials, in particular to a hand mold wax and its preparation method and application. Background technique [0002] Wax hand products refer to designing a favorite or memorable gesture, immersing the hand in a low-temperature (generally below 62°C) molten hand mold wax liquid, so that the surface of the hand is coated with multiple layers of wax liquid, which will come out after cooling. Wax shell, and then according to personal preference, dyed various colors and matched with exquisite small ornaments to make wax hand art. Because the finished wax hand product replicates and clones the information of each person's fingers and palms, it has unique personality and commemorative significance, and is loved by many people. [0003] Wax hand art originated from western European and American countries. Although it has entered the domestic market not long ago, wax hand art is strong in modeling, rich in c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B44C3/04C08L91/06C08L23/02C08L57/02C08L25/06C08L45/00C08L23/06C08L23/08C08K5/09
CPCB44C3/046C08L91/06C08L2205/025C08L2205/03C08L2205/035C08L2205/06C08L23/02C08L57/02C08K5/09C08L25/06C08L45/00C08L23/0853C08L23/06
Inventor 黄家龙范智勇范德贤
Owner GUANGZHOU DEXIN WAX PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap