A kind of preparation method of high cotton feeling microfiber sofa leather bass

A sofa leather bass and microfiber technology, applied in fiber processing, fiber types, textiles and papermaking, etc., can solve the problems of easy collapse of cells, reduce the use time of recycling equipment, and reduce the purity of waste polyethylene particles, so as to improve the product quality. Quality, improved recycling value, sensual plump effect

Active Publication Date: 2021-04-30
重庆双象超纤材料有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the past, in order to achieve this purpose, low-modulus polyurethane resins were generally used. Because the superfiber in the present invention adopts the toluene fiber opening process, the low-modulus polyurethane resin has a large corrosion rate and the cells are easy to collapse during the process of toluene fiber opening. etc., the softness of the prepared microfiber synthetic leather is relatively good, but it has the disadvantages of poor myogenesis, weak fleshy feeling, thick creases, etc., which reduces the economic benefits and makes its cost high. The corrosion rate is high, and a large amount of polyurethane components enter the crude toluene, which leads to easy blockage of pipes and evaporators during the toluene recovery process. At the same time, the purity of waste polyethylene particles is greatly reduced, which reduces the recovery value of waste polyethylene and reduces the cost of recycling equipment. usage time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of high cotton feeling microfiber sofa leather bass
  • A kind of preparation method of high cotton feeling microfiber sofa leather bass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023]Preparation method of Khmer Sweet Microfiber Sofa Revolution, including the following steps:

[0024](1) Preparation of "Island" composite fiber: Nylon 6 (PA6) and line-type low-density polyethylene (LDPE), according to PA6: LDPE = 50: 50, after mixed melt extrusion method obtained line density 6dtex, "island" composite short fiber with a length of 51mm, of which PA6 is "island", and LDPE is "sea";

[0025](2) Preparation of ultrapine non-woven fabric: Using the composite short fibers in step (1), a process of opening, sorting, spreading net, acupuncture, gave 450 g / m2Non-woven fabric;

[0026](3) Trunteing: The non-woven fabric in step (2), after 155 ° C * 3 min, LDPE will be softened, and then the density is 0.28 g / cm after the pressure roll is formed.3Non-woven fabric;

[0027](4) impregnation: The impregnation containing a solid content of 22.4%, and the nonwoven fabric obtained by the step (3) is impregnated in the slurry through the impregnation apparatus, and the cleaning and w...

Embodiment 2

[0035]Preparation method of Khmer Sweet Microfiber Sofa Revolution, including the following steps:

[0036](1) Preparation of "Island" type composite fiber: Nylon 6 (PA6) and line-type low density polyethylene (LDPE), according to PA6: LDPE = 53: 47, after mixed melt extrusion method obtained line density 6.0dtex, "island" composite short fibers having a length of 51mm, of which PA6 is "island", LDPE is "sea";

[0037](2) Preparation of ultrapine non-woven fabric: Using the composite short fibers in step (1), a process of opening, sorting, spreading net, acupuncture, gave 450 g / m2Non-woven fabric;

[0038](3) Trunteing: The non-woven fabric in step (2), after 155 ° C * 3 min, LDPE will be softened, and then the density is 0.28 g / cm after the pressure roll is formed.3Non-woven fabric;

[0039](4) impregnation: The solid content of 24.8% is prepared, and the nonwoven fabric obtained by step (3) is impregnated in a penetrating slurry through a thin-impregnated apparatus, and the cleaning and w...

Embodiment 3

[0047]Preparation method of Khmer Sweet Microfiber Sofa Revolution, including the following steps:

[0048](1) Preparation of "Island" composite fiber: Nylon 6 (PA6) and line-type low-density polyethylene (LDPE), according to PA6: LDPE = 50: 50, after mixed melt extrusion method obtained line density 5.5dtex, "island" composite short fiber with a length of 51mm, of which PA6 is "island", LDPE is "sea";

[0049](2) Preparation of ultrapine non-woven fabric: Using the composite short fibers in step (1), a process of opening, sorting, spreading net, acupuncture, gave 450 g / m2Non-woven fabric;

[0050](3) Trunteing: The non-woven fabric in step (2), after 155 ° C * 3 min, LDPE will be softened, and then the density is 0.28 g / cm after the pressure roll is formed.3Non-woven fabric;

[0051](4) impregnation: The solid content of 24.5% is prepared, and the nonwoven fabric obtained by step (3) is impregnated in the system-impregnated slurry, and the cleaning and water is washed to obtain the microfi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Basis weightaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of preparation of ultrafine fiber synthetic leather, and in particular relates to a preparation method of ultrafine fiber sofa leather bass, comprising the following processing steps: spinning, non-woven fabric, non-woven fabric shaping, wet impregnation, extraction, and drying Oiling, kneading and finishing. The preparation method of the present invention adopts novel polyurethane to wet impregnate the microfiber non-woven fabric, and is equipped with a reasonable superfiber production process, so that the microfiber bass prepared by the present invention has the characteristics of plump flesh and relatively delicate creases, and can be Improve the grade of microfiber sofa leather, comparable to calfskin and goatskin, greatly reduce the consumption of raw materials, increase the recycling value of waste polyethylene, and improve product quality, and the economy is relatively high.

Description

Technical field[0001]The present invention belongs to the preparation of beam-shaped ultra-fine fibers, and specific methods for the preparation of Khmer Skin Soft Sofa Revolution.Background technique[0002]Ultrafine fiber synthesis leather (referred to as ultra-film) is a high-end artificial leather that develops on the basis of natural leather. It is formed by the bundle ultrafine fibers and polyurethanes. It is based on the nylon 6 microfibers as a three-dimensional stereo "skeleton", and the polyurethane is "meat", closely wrapped in the "skeleton" structure, with an irregular sponge structure . Bes' microstructure is similar to the collagen fibers of natural leather, and also has similar tissue structures and physical chemical properties similar to natural leather. The microfiber leather has almost all characteristics and advantages of natural leather, and is better than natural leather in terms of mechanical strength, chemical resistance, unity, protection, automated cutting, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/564D06M11/76D01F8/12D01F8/06D04H1/4382D06M101/34D06M101/20
CPCD01F8/06D01F8/12D04H1/4382D06M11/76D06M15/564D06M2101/20D06M2101/34
Inventor 邬花元刘安秦尉雷邹杰
Owner 重庆双象超纤材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com