Preparing method of Nixing pottery embedded with shells

A technology of Nixing pottery and shells, which is applied in the field of preparation of Nixing pottery, can solve the problems of poor three-dimensional effect, lack of visual impact, and single shape of porcelain plates in shell carving paintings, so as to increase appreciation, maintain integrity, and shape full effect

Inactive Publication Date: 2019-04-12
钦州市永和坭兴陶艺有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The combination of shell carving paintings and ceramic handicrafts in the prior art only uses coagulant to paste the shells on the porcelain plate. The existing defect is: the lack of visual impact due to the single shape of the porcelain plate
Shell carving paintings pasted with gelatin are easily damaged due to touch or glue aging, and shell carving paintings pasted on the porcelain plate have a weak three-dimensional effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] The preparation method of the Nixing pottery inlaid with shells of the present embodiment comprises the following steps:

[0044] Step 1: Prepare blank

[0045] The blank is made of the following raw materials in mass percentage: take 40% of the eastern mud and 60% of the western mud, mix them evenly, grind and dehydrate to make a blank;

[0046] Step 2: Body Forming

[0047] The blank of step 1 is made into a green body;

[0048] Step 3: Recessed lighting

[0049]On the green body obtained in step 2, select a position, cut it into a circle, take out the cut clay piece and process it into an arc surface; paste the arc surface clay piece back to the original cutting position, and obtain a concave arc shape body;

[0050] Step 4: Firing the green body

[0051] Place the concave arc-shaped green body obtained in step 3 in the kiln and fire it in two stages. First, the temperature is raised to 420°C at a rate of 70°C per hour, and then to 130°C per hour. The speed is ...

Embodiment 2

[0063] The preparation method of the Nixing pottery inlaid with shells of the present embodiment comprises the following steps:

[0064] Step 1: Prepare blank

[0065] The blank is made of the following raw materials in mass percentage: take 50% of the east mud and 50% of the west mud, mix evenly, grind and dehydrate to make a blank;

[0066] Step 2: Body Forming

[0067] The blank of step 1 is made into a green body;

[0068] Step 3: Recessed lighting

[0069] On the green body obtained in step 2, select a position, cut it into a rectangle, take out the cut clay piece and process it into an arc surface; paste the arc surface clay piece back to the original cutting position, and obtain a concave circular arc shape Body;

[0070] Step 4: Firing the green body

[0071] Place the concave arc-shaped green body obtained in step 3 in the kiln and fire it in two stages. First, the temperature is raised to 420°C at a rate of 70°C per hour, and then to 130°C per hour. The speed i...

Embodiment 3

[0083] The preparation method of the Nixing pottery inlaid with shells of the present embodiment comprises the following steps:

[0084] Step 1: Prepare blank

[0085] The blank is made of the following raw materials in mass percentage: take 60% of Dongni and 40% of Xini, mix them evenly, grind and dehydrate to make a blank;

[0086] Step 2: Body Forming

[0087] The blank of step 1 is made into a green body;

[0088] Step 3: Recessed lighting

[0089] On the green body obtained in step 2, select a position, cut it into a diamond shape, take out the cut clay piece and process it into an arc surface; paste the arc surface clay piece back to the original cutting position, and obtain a concave circular arc shape Body;

[0090] Step 4: Firing the green body

[0091] Place the concave arc-shaped green body obtained in step 3 in the kiln and fire it in two stages. First, the temperature is raised to 420°C at a rate of 70°C per hour, and then to 130°C per hour. The speed is rai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparing method of Nixing pottery embedded with shells, and belongs to the technical field of pottery product decoration. The preparing method of Nixing pottery embedded with the shells comprises the following steps of firstly, blank preparing; secondly, blank forming; thirdly, sunken inner chamber forming; fourthly, blank firing; fifthly, shell grinding; sixthly, shellcutting and splicing; seventhly, epoxy resin glue mixed solution preparing; and eighthly, shell carving picture bonding. The blank body is opened, a sunken arc face is formed on the blank body, in theopened sunken arc face, the epoxy resin glue is used for carrying out layer-by-layer casting, the shell carving pictures are fixed, the layer-by-layer bonded shell carving pictures can show the morethree-dimensional vision effect, and through casting of the epoxy resin, the complete modeling completeness of the Nixing pottery artware can be kept.

Description

technical field [0001] The invention relates to a preparation method of Nixing pottery inlaid with shells, belonging to the technical field of pottery decoration. Background technique [0002] Nixing pottery, scientific name Zini pottery, flourished in the Xianfeng period of the Qing Dynasty. It is a specialty of Qinzhou City, Guangxi, and a product of China's National Geographical Indication. Nixing pottery in Qinzhou, Yixing Zisha pottery in Jiangsu, Rongchang pottery in Sichuan and Jianshui pottery in Yunnan are known as "China's Four Famous Pottery". [0003] The preparation process of Nixing pottery is characterized by "double-material mixing, fusion of flesh and blood, natural biscuit firing, smelting to produce color (kiln transformation), pottery engraving and pottery modeling". Specifically, it includes the following steps: 1) Preparing the blank: the blank is made of pottery clay, and the local unique east and west clay in Qinzhou are selected as raw materials. 2...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B44C5/00B28B11/00
CPCB28B11/001B44C5/00
Inventor 刘俭黄晓聪
Owner 钦州市永和坭兴陶艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com