A kind of multifunctional paint suitable for battery box and its preparation method and application

A battery box, multi-functional technology, used in conductive coatings, anti-corrosion coatings, fire-retardant coatings, etc., can solve the problems of inability to improve the heat dissipation performance of the battery box, poor anti-corrosion and fire-proof effect, and unknown alkali resistance, and achieve excellent adhesion. , The effect of obvious heat dissipation and excellent comprehensive performance

Active Publication Date: 2021-02-19
烯世达材料科技(启东)有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent forms a layer of elastic protective film on the outer surface of the box, which can quickly rebound and return to its original shape after being hit. Therefore, after spraying this protective coating on the box, it can protect the battery box well. However, this patent It also cannot improve the heat dissipation performance that restricts the service life of the battery box, and the anti-corrosion and fire prevention effect is poor. In addition, the alkali resistance is unknown, and the adhesion is relatively poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of multifunctional paint suitable for battery box and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The present embodiment provides a kind of multifunctional coating that is applicable to battery box, and its raw material comprises: graphene aqueous solution 45% (the mass content of graphene is 10%), water-based resin 30% (wherein polyurethane RU -71-035 and acrylic resin AC-106 mixed at a mass ratio of 6:4), polyvinylpyrrolidone PVP: 0.9%, polydimethylsiloxane Ls-3110: 0.5%, dimethylethanolamine DEMA: 0.6%, Polyacrylate thickener DN-2222: 0.8%, modified polycarbodiimide crosslinking agent XR-5580: 1.0%, polydimethylsiloxane wear agent DC-51: 5%, silicone resistance Combustion agent DC-8008: 15%, oily defoamer T-501: 0.15%, the balance is water.

[0038] Mix the graphene aqueous solution, water-based resin and part of the water into the mixer, control the speed at 2000 rpm, and stir for 30 minutes; then add polyvinylpyrrolidone PVP, polydimethylsiloxane Ls-3110, Dimethylethanolamine DEMA, polyacrylate thickener DN-2222, modified polycarbodiimide crosslinker XR-5580, ...

Embodiment 2

[0040] The present embodiment provides a kind of multifunctional coating that is applicable to battery box, and its raw material comprises: graphene aqueous solution 45% (the mass content of graphene is 10%), water-based resin 30% (wherein polyurethane RU -71-035 and acrylic resin AC-106 mixed at a mass ratio of 4:3), polyvinylpyrrolidone PVP: 0.9%, polydimethylsiloxane Ls-3110: 0.5%, dimethylethanolamine DEMA: 0.6%, Polyacrylate thickener DN-2222: 0.8%, modified polycarbodiimide crosslinking agent XR-5580: 1.0%, polydimethylsiloxane wear agent DC-51: 5%, silicone resistance Combustion agent DC-8008: 15%, oily defoamer T-501: 0.15%, the balance is water.

[0041] Mix the graphene aqueous solution, water-based resin and part of the water into the mixer, control the speed at 2000 rpm, and stir for 30 minutes; then add polyvinylpyrrolidone PVP, polydimethylsiloxane Ls-3110, Dimethylethanolamine DEMA, polyacrylate thickener DN-2222, modified polycarbodiimide crosslinker XR-5580, ...

Embodiment 3

[0043] The present embodiment provides a kind of multifunctional coating that is applicable to battery box, and its raw material comprises: graphene aqueous solution 45% (the mass content of graphene is 10%), water-based resin 30% (wherein polyurethane RU -71-035 and acrylic resin AC-106 mixed at a mass ratio of 12:7), polyvinylpyrrolidone PVP: 0.9%, polydimethylsiloxane Ls-3110: 0.5%, dimethylethanolamine DEMA: 0.6%, Polyacrylate thickener DN-2222: 0.8%, modified polycarbodiimide crosslinking agent XR-5580: 1.0%, polydimethylsiloxane wear agent DC-51: 5%, silicone resistance Combustion agent DC-8008: 15%, oily defoamer T-501: 0.15%, the balance is water.

[0044] Mix the graphene aqueous solution, water-based resin and part of the water into the mixer, control the speed at 2000 rpm, and stir for 30 minutes; then add polyvinylpyrrolidone PVP, polydimethylsiloxane Ls-3110, Dimethylethanolamine DEMA, polyacrylate thickener DN-2222, modified polycarbodiimide crosslinker XR-5580,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a multifunctional coating suitable for battery boxes, its preparation method and application. A combination of one or more of a leveling agent, a pH regulator, an anti-wear agent, a flame retardant and a defoamer; the water-based resin is composed of a water-based polyurethane resin and a water-based acrylic acid with a mass ratio of 11:10-9:5 Composed of resin, the thickener is polyacrylate thickener DN-2222, and the cross-linking agent is modified polycarbodiimide cross-linking agent XR-5580; it is prepared by mixing the raw materials with each other through a certain feeding method; And the application of the above-mentioned coating in the coating on the outer surface of the battery box of a new energy electric vehicle; the coating of the present invention can have excellent adhesion, alkali resistance, abrasion resistance, salt spray resistance and viscosity while having high heat dissipation And other physical and mechanical properties, its efficient heat dissipation can not be affected by the external environment.

Description

technical field [0001] The invention belongs to the field of coatings for new energy vehicles, in particular to coatings for battery boxes of new energy vehicles, in particular to a multifunctional coating suitable for battery boxes and its preparation method and application. Background technique [0002] In order to protect the environment, save energy and protect the environment, and promote green energy, one of the ways to protect the environment is to expand the use of electric vehicles and reduce the use of fuel-efficient vehicles. However, electric vehicles have been in a downturn now, restricting The main factor in the development of electric vehicles is the service life of new energy power batteries. In response to this problem, most of the battery boxes currently used to store new energy batteries are equipped with cooling holes, but due to the opening of the cooling holes, rainwater can easily enter the inside of the battery box when it rains, short-circuiting the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D5/18C09D5/24C09D5/08C09D5/25C09D7/61C09D7/63C09D7/65
CPCC08L2201/02C08L2201/04C08L2203/20C08L2205/035C09D5/00C09D5/08C09D5/18C09D5/24C09D175/04C09D7/61C09D7/63C09D7/65C08L33/00C08K3/042
Inventor 徐冬春蔺洪振雍婷婷高春华郝永波
Owner 烯世达材料科技(启东)有限公司