Polyether-ether-ketone composite material surface chemical plating pre-treatment technology

A technology of composite materials and polyether ether ketone, which is applied in metal material coating technology, liquid chemical plating, coating, etc., can solve the problems of low product qualification rate and low bonding strength, and achieve stable process and high surface tension , Improve the effect of binding force

Active Publication Date: 2019-04-19
镇江阿尔法特种镀膜科技有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the deficiencies of the prior art, provide a pretreatment process before electroless plating on the surface of polyether ether ketone composite materials, and solve the problems of low bonding strength and low product qualification rate in the prior art. The metal coating after the pretreatment process before electroless plating has high bonding strength, is not easy to fall off, has a high product qualification rate and is suitable for industrial applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyether-ether-ketone composite material surface chemical plating pre-treatment technology
  • Polyether-ether-ketone composite material surface chemical plating pre-treatment technology
  • Polyether-ether-ketone composite material surface chemical plating pre-treatment technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A pretreatment process before electroless plating on the surface of a polyether ether ketone composite material, comprising the following steps:

[0039]Step 1. Stress relief: wash the surface of the finished polyether ether ketone composite material with ethanol for at least 2 times, then put it in an oven at a temperature of 40-80°C and dry it for 2-10 hours. After drying, polyether is obtained Etherketone composite parts are ready for use;

[0040] Step 2. Degreasing: put the polyetheretherketone composite material part in step 1 into the dewaxed water at a temperature of 50-80 °C for ultrasonic cleaning for 5-30 minutes, and obtain the degreased polyether ether ketone composite material part for use;

[0041] Step 3. Pretreatment: Wash the polyether ether ketone composite material parts degreased in step 2 with water for at least 2 times, then soak them in the pretreatment solution at a temperature of 20-30°C for at least 5 minutes, take them out and wash them with ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of surface modification and electroplating of special materials, and particularly relates to a polyether-ether-ketone composite material surface chemical plating pre-treatment technology. The polyether-ether-ketone composite material surface chemical plating pre-treatment technology comprises the following steps of stress removal, oil removal, pretreatment, etching, adjustment activation and peptizing chemical plating. The polyether-ether-ketone composite material surface chemical plating pre-treatment technology solves the problems of the low bonding strength and the low product qualification rate in the prior art; and a metal plating layer obtained after the chemical plating pre-treatment technology is high in bonding strength, is not prone tofalling off, is high in product qualification rate and is suitable for industrial application.

Description

technical field [0001] The invention belongs to the technical field of surface modification and electroplating of special materials, and in particular relates to a pretreatment process before electroless plating on the surface of a polyetheretherketone composite material. Background technique [0002] Plastics are common items in everyday life. Now the market is common to have decorative metal layers on some plastic surfaces, which are bright and smooth. The surface metallization of these plastics is generally processed by physical vapor deposition techniques or chemical deposition techniques. However, physical vapor deposition technology is difficult to metallize the surface of heterogeneous parts. [0003] Electroplating is mainly for electrical conductors, which consumes more energy. The electroless plating process is simple and the production process is convenient, but pretreatment between plastic polymers is required to activate the surface. For example: the general...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C18/30C23C18/20C23C18/24
CPCC23C18/2086C23C18/24C23C18/30
Inventor 吴王平汤佳伟汤立新
Owner 镇江阿尔法特种镀膜科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap