A kind of sodium alginate-dopamine/polyvinyl alcohol hydrogel and its preparation method and application

A technology of sodium alginate and polyvinyl alcohol, applied in bandages, medical science, etc., can solve the problems of poor wound healing effect, complicated preparation process, high reaction conditions, etc., achieve broad biomedical application prospects, improve mechanical properties, absorb water The effect of sexual comfort

Active Publication Date: 2021-09-07
JINAN UNIVERSITY
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the existing hydrocolloid dressings only consider biocompatibility and mechanical properties when designing, and do not introduce a substance that can promote wound healing. This type of dressing has obvious disadvantages: such as high preparation cost, complicated preparation process and Difficult to remove impurities, high reaction conditions and poor wound healing effects, etc., cannot comprehensively solve the post-care problems of pressure sores

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sodium alginate-dopamine/polyvinyl alcohol hydrogel and its preparation method and application
  • A kind of sodium alginate-dopamine/polyvinyl alcohol hydrogel and its preparation method and application
  • A kind of sodium alginate-dopamine/polyvinyl alcohol hydrogel and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] (1) Sterilization of experimental raw materials and instruments

[0041] The experimental raw materials were sterilized by irradiating the raw materials with ultra-clean bench for 1 hour, and the glass instruments were sterilized at 121°C for 20 minutes under high-pressure conditions.

[0042] (2) Preparation of sodium alginate-dopamine

[0043] Take 2g of sodium alginate (SA) and add it into 100ml of distilled water, stir and dissolve at 800rpm for 12h, and prepare an SA solution for later use. Add 0.5755g N-hydroxysuccinimide (NHS) and 0.9585g 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide hydrochloride to the SA solution according to the molar ratio of 1:1 and add Stir at 800 rpm for 20 min, then add 1.5473 g of dopamine (DA) at room temperature and stir at 800 rpm for 24 hours. After the reaction is completed, the prepared sodium alginate-dopamine (SA-DA) solution is sealed and stored at 2-8°C.

[0044] (3) Preparation of sodium alginate-dopamine / polyvinyl alcohol...

Embodiment 2

[0060] In Vitro Cell Experiment of Sodium Alginate-Dopamine / Polyvinyl Alcohol Hydrogel

[0061] Before the in vitro cytotoxicity test, the freeze-dried hydrogel sample prepared in Example 1 was sterilized by Co60 γ-ray radiation.

[0062] (1) Take out NIH 3T3 cells (purchased from Wuhan Punuosai Life Technology Co., Ltd.) in liquid nitrogen and resuscitate them with DMEM culture medium.

[0063] (2) Subculture several times with DMEM culture medium, take the cells in the logarithmic growth phase and count the NIH3T3 cells with a cell counting plate, adjust the cell density to 5×10 4 individual / mL.

[0064] (3) Take a 96-well plate and add 100 μL to 30 wells of it. Step (2) The cell density is 5×10 4 cells / mL of DMEM culture solution was used as the experimental group; at the same time, another 3 wells were taken and set as a blank control group, that is, only 100 μL of DMEM culture solution (without cells) was added, and placed at 37°C, 5% CO 2 Incubate for 24 hours in a ce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elastic modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sodium alginate-dopamine / polyvinyl alcohol hydrogel, a preparation method and application thereof. It is achieved through the following scheme: dopamine (DA) is introduced into neurotransmitters through chemical cross-linking grafted sodium alginate (SA) to communicate with cells to transmit chemical substances to promote wound healing, improve physical adhesion and improve material biocompatibility, Then, it is compounded with medical-grade polyvinyl alcohol (PVA), a cheap and easy-to-obtain material with good biocompatibility, to improve the physical properties of the hydrogel, thereby preparing a hydrogel with higher mechanical strength. The hydrogel prepared by the application has good biocompatibility and excellent physical properties, and the reaction raw materials are cheap and easy to obtain, the reaction conditions are mild and the operation steps are simple and convenient. It has broad application prospects in decubitus wound care and biomedicine.

Description

technical field [0001] The invention belongs to the field of biopolymer materials, and in particular relates to a sodium alginate-dopamine / polyvinyl alcohol hydrogel and a preparation method and application thereof. Background technique [0002] Bed sores, also known as pressure sores, are a common clinical complication. The main external causes of pressure sores are the pressure factors: vertical pressure (local tissue is subject to continuous vertical pressure, such as body bone tuberosity), friction (skin friction), shear force (a force applied to an object After getting up, it will lead to a plane sliding in parallel and opposite direction. For example, when the body slides down when the head of the bed is raised, the parallel friction between the skin and the bed, coupled with the gravity in the vertical direction of the skin, will lead to the generation of shear force and cause local skin blood. circulatory disturbances leading to pressure sores). At present, clinica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information