High-strength and high-tenacity titanium alloy tubular product used for oil and gas exploitation and preparation method thereof

A titanium alloy and high-strength technology, which is applied in the field of high-strength and high-toughness titanium alloy pipes and their preparation, can solve the problems that the strength and toughness of titanium alloy pipes are difficult to meet, and achieve the effects of excellent mechanical properties, high strength, and convenient preparation and processing.

Active Publication Date: 2019-05-03
BC P INC CHINA NAT PETROLEUM CORP +2
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem that the strength and toughness of existing titanium alloy pipes are difficult to meet the environmental requirements of oil and gas fields such as ultra-deep and high pressure, and to provide a high-strength and high-toughness titanium alloy pipe and its preparation method. The oil pipe has high strength, high toughness and good fatigue performance, which can meet the needs of oil and gas exploitation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength and high-tenacity titanium alloy tubular product used for oil and gas exploitation and preparation method thereof
  • High-strength and high-tenacity titanium alloy tubular product used for oil and gas exploitation and preparation method thereof
  • High-strength and high-tenacity titanium alloy tubular product used for oil and gas exploitation and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The invention provides a high-strength and high-toughness titanium alloy drilling tool pipe composition design and preparation method used in oil and gas development of deep wells and ultra-deep wells. The oil pipes made of titanium alloy materials are used in meeting the severe oil and gas development conditions in China. In addition to corrosion resistance, it also has high strength, high toughness and good fatigue performance.

[0030] The high-strength and high-toughness titanium alloy material of the present invention is composed of the following components by mass percentage, Al: 3.8-5.0%, V: 2.4-3.3%, Fe: 1.3-1.8%, Nb: 0.4-0.8%, Ni: 0.3-1.0 %, O ≤ 0.2%, C ≤ 0.04%, N ≤ 0.04%, H ≤ 0.0135%, the balance is Ti; on this basis, one of Cr: 0.15-0.35%, Mo: 0.05-1.0% can also be added One or two alloying elements.

[0031] In the alloy composition of the present invention, a small amount of Fe element is used to replace part of V element with higher price. Fe element is ...

Embodiment 1

[0042] The composition of the high-strength and high-toughness titanium alloy material used in the oil and gas development of deep wells and ultra-deep wells of the present invention is composed of Al: 4.53%; V: 3.11%; Fe: 1.69%; Ni: 0.33%; Nb: 0.77%; O: 0.12%; C: 0.035%; N: 0.007%; H: 0.0131%; Mo: 0.09%, and the balance is Ti.

[0043] The preparation processing method of above titanium alloy tube comprises the following steps:

[0044] 1) The titanium alloy composition with the above ratio is dispersed and batched and then pressed into an electrode. It is melted in a vacuum consumable furnace for three times and vacuum smelted to form an ingot. The outer diameter of the ingot is 400 mm, and there is no obvious iron element segregation. ;

[0045] After peeling the ingot, cutting the riser, removing the bottom pad, and sampling and analyzing the chemical composition, the ingot is heated to a temperature of 1000-1050 °C, and the temperature is lowered for more than two times ...

Embodiment 2

[0051] The composition of the high-strength and high-toughness titanium alloy material used in the oil and gas development of deep wells and ultra-deep wells of the present invention is composed of Al: 4.92%; V: 2.56%; Fe: 1.41%; Ni: 0.89%; Nb: 0.51%; O: 0.13%; C: 0.028%; N: 0.016%; H: 0.0134%; Mo: 0.88%, Cr: 0.19%; the balance is Ti;

[0052] The preparation and processing method of the above-mentioned titanium alloy tube comprises the following steps:

[0053] 1) The titanium alloy composition with the above ratio is dispersed and batched, then pressed into an electrode, melted in a vacuum consumable furnace for three times and vacuum smelted to form an ingot. The outer diameter of the ingot is 600 mm, and there is no obvious iron element segregation ;

[0054] After peeling the ingot, cutting the riser, removing the bottom pad, and sampling and analyzing the chemical composition, the ingot is heated to a temperature of 1000-1050 °C, and the temperature is lowered for more ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Grainaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-strength and high-tenacity titanium alloy tubular product used for oil and gas exploitation and a preparation method thereof. Safe and effective exploitation of oil andgas wells is ensured, and the problems that strength and tenacity of existing titanium alloy pipes cannot meet environment characteristics, such as ultra-large depth and high pressure, of oil and gasfields are mainly solved. Besides Ti, the titanium alloy tubular product is mainly composed of, by mass, 3.8%-5.0% of Al, 2.4%-3.3% of V, 1.3%-1.8% of Fe, 0.4%-0.8% of Nb, 0.3%-1.0% of Ni, smaller than or equal to 0.2% of O, smaller than or equal to 0.04% of C, smaller than or equal to 0.04% of N and smaller than or equal to 0.0135% of H, and one or two of following alloy elements, namely, 0.15%-0.35% of Cr and 0.05%-1.0% of Mo are further added. Meanwhile, the invention further provides the preparation method of the titanium alloy tubular product.

Description

technical field [0001] The invention relates to the field of pipes for oil and gas development in the petroleum and natural gas industry, in particular to a high-strength and high-toughness titanium alloy pipe used in oil and gas development of deep wells and ultra-deep wells and a preparation method thereof, so as to ensure safe and effective exploitation of oil and gas wells. Background technique [0002] With the further deepening of oil and gas development, the development of many western and southwestern oil and gas fields in China has high temperature (greater than 140°C), high pressure (greater than 100MPa), well depth (greater than 5000m), and high corrosive media (CO 2 、H 2 S, CL － ) and other harsh environments; in order to meet the corrosion resistance requirements of oil and gas field development for tubing and casing, considering that titanium alloy materials have excellent characteristics such as high strength, excellent corrosion resistance, low elastic modul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C14/00C22C1/02C22F1/02C22F1/18E21B17/00
Inventor 刘强宋生印白强田峰汪蓬勃杨专钊王远
Owner BC P INC CHINA NAT PETROLEUM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap