A kind of macroporous hybrid material and preparation method thereof

A hybrid material and pore volume technology, applied in chemical instruments and methods, refined hydrocarbon oil, inorganic chemistry, etc., to achieve high desulfurization rate, improve diffusion, and increase adsorption capacity

Active Publication Date: 2022-04-05
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, domestic diesel adsorption desulfurization has just started, and it is still in the laboratory research stage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of macroporous hybrid material and preparation method thereof
  • A kind of macroporous hybrid material and preparation method thereof
  • A kind of macroporous hybrid material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] According to the mass fraction of copper nitrate, nickel nitrate, zinc nitrate and aluminum nitrate in the solution is 13.7wt%, 4.1wt%, 3.7wt%, 3.2wt%, weigh the raw materials and add ternary solvent (water 3 wt%-ethanol 25 wt%) %-N,N-dimethylformamide 72wt%), after stirring at 50°C to dissolve it completely, adjust the pH value of the solution to 6; secondly, add 0.23wt% cetyl trimethyl bromide Ammonium was used as a template, and 0.11wt% of 3-mercaptopropyltrimethoxysilane was added as a mercapto modifier, and mixed evenly; then, a ternary complexing agent (2,5-dihydroxy-terephthalic acid 9.0 wt%-terephthalic acid 11.1wt%-trimellitic acid 79.9wt%) was added to the solution, stirred rapidly to make it evenly mixed, and then the solution was transferred to a stainless steel reaction kettle lined with polytetrafluoroethylene, at 100 Crystallization at ℃ for 16h. After the crystallization, the product was washed with acetone for 5 times, and suction-filtered, and the fil...

Embodiment 2

[0033] The preparation method is the same as in Example 1, except that the ternary solvent is water 1 wt%-ethanol 30 wt%-N,N-dimethylformamide 69wt%; the template is sodium dodecylbenzenesulfonate, The dosage is 0.42%; the thiol modifier is mercaptoacetic acid, the dosage is 0.21%; the crystallization temperature is 120°C, the crystallization time is 18h, the drying temperature is 160°C, and the drying time is 20h. Prepared A2# sample with a pore volume of 0.817 cm 3 / g, XRD spectrum, the relative intensity I / I of each diffraction peak 0 , and the average pore size distribution are listed in figure 1 , Table 1 and image 3 middle.

Embodiment 3

[0035] The preparation method is the same as in Example 1, except that the ternary solvent is water 5wt%-ethanol 10wt%-N,N-dimethylformamide 85wt%; the template agent is dodecylamine, and the dosage is 0.89%; The active agent is methyl thioglycolate, the dosage is 0.45%; the crystallization temperature is 140°C, the crystallization time is 12h, the drying temperature is 180°C, and the drying time is 16h. Prepared A3# sample with a pore volume of 0.810 cm 3 / g, XRD spectrum, the relative intensity I / I of each diffraction peak 0 , and the average pore size distribution are listed in figure 1 , Table 1 and image 3 middle.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a hybrid material, the pore volume of the hybrid material is 0.3-1.2 cm 3 / g, the hybrid material is composed of Cu, Ni, Zn, Al multi-metal and composite complexing agent, the mass percentage of the Cu element in the hybrid material is 5%-40% in terms of CuO, and the Ni The mass percentage of elements in the hybrid material as NiO is 1%-30%, the mass percentage of the Zn element in the hybrid material as ZnO is 1%-30%, and the Al element is Al 2 o 3 The mass percentage calculated in the hybrid material is 1%-30%, and the balance is a composite complexing agent, which is composed of 2,5-dihydroxy-terephthalic acid, terephthalic acid and 1, Composed of 3,5-benzenetricarboxylic acid; the preparation method of the hybrid material: introducing Zn, Ni and Al into the Cu-containing hybrid material through isomorphic substitution. The hybrid material has excellent desulfurization performance, and the desulfurization rate reaches over 99%.

Description

technical field [0001] The invention relates to a macroporous hybrid material and a preparation method thereof, in particular to a multi-element metal macroporous organic hybrid material and a preparation method thereof. Background technique [0002] In the 21st century, in view of the hazards of sulfur compounds after burning thiophene sulfides in diesel oil, and the society's high attention to the atmospheric environment and human health, countries around the world have formulated strict fuel emission standards and new regulations, and have taken measures to improve fuel quality. Taking European and American diesel as an example, developed countries such as Europe and the United States have imposed strict restrictions on the sulfur content in diesel, from 350ppm in Euro III in 2000 to 50ppm in Euro IV in 2005, and then to 2008. The latest Euro V standard sulfur content is less than 10ppm sulfur-free diesel. The U.S. Environmental Protection Agency (EPA) issued low-sulfur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/22B01J20/30B01J20/28C10G25/00
Inventor 张信伟李杰王海洋尹泽群刘全杰
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap