Surface hardening treatment process of melamine decorative panel

A decorative panel, melamine technology, applied in the direction of decorative art, special decorative structure, coating, etc., can solve the problem that the decorative panel can not meet the impact resistance, etc., to achieve enhanced use strength, good resistance, strength and flexibility Effect

Inactive Publication Date: 2019-05-24
FOSHAN CITY YATE OFFICE FURNITURE CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a surface hardening treatment process for melamine decorative panels, which has the advantages of low cost and simple operation, and solves the problem that the existing hardening of the surface of melamine decorative panels cannot meet the requirements of good impact resistance of the decorative panels. The question of force requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A surface hardening treatment process for a melamine decorative panel, comprising the following steps:

[0028] (1) First hang the melamine decorative panel on the jig and clean it with ultrasonic waves.

[0029] (2) Then soak the melamine decorative panel in soda water for 10-30 minutes, and then irradiate the melamine decorative panel under an ultraviolet lamp with a wavelength of 220-240nm for 10 minutes.

[0030] (3) Next, soak the surface of the melamine decorative panel with a tartaric acid solution with a concentration of 8%-12% for 40 minutes.

[0031] (4) The surface of the melamine decorative panel is then fumigated with hot water vapor.

[0032] (5) Dry the outer surface of the melamine decorative panel for 1-3 hours.

[0033] (6) Brush the surface of the melamine decorative panel with a layer of 2-3mm thick hardening material, and wait for the hardening material to dry for later use.

[0034] (7) Finally, brush the strengthening liquid on the surface of t...

Embodiment 2

[0039] A surface hardening treatment process for a melamine decorative panel, comprising the following steps:

[0040] (1) First hang the melamine decorative panel on the jig and clean it with ultrasonic waves.

[0041] (2) Then soak the melamine decorative panel in soda water for 10-30 minutes, and then irradiate the melamine decorative panel under an ultraviolet lamp with a wavelength of 220-240nm for 10 minutes.

[0042] (3) Next, soak the surface of the melamine decorative panel with a tartaric acid solution with a concentration of 8%-12% for 40 minutes.

[0043] (4) The surface of the melamine decorative panel is then fumigated with hot water vapor.

[0044] (5) Dry the outer surface of the melamine decorative panel for 1-3 hours.

[0045] (6) Brush the surface of the melamine decorative panel with a layer of 2-3mm thick hardening material, and wait for the hardening material to dry for later use.

[0046] (7) Finally, brush the strengthening liquid on the surface of t...

Embodiment 3

[0051] A surface hardening treatment process for a melamine decorative panel, comprising the following steps:

[0052] (1) First hang the melamine decorative panel on the jig and clean it with ultrasonic waves.

[0053] (2) Then soak the melamine decorative panel in soda water for 10-30 minutes, and then irradiate the melamine decorative panel under an ultraviolet lamp with a wavelength of 220-240nm for 10 minutes.

[0054] (3) Next, soak the surface of the melamine decorative panel with a tartaric acid solution with a concentration of 8%-12% for 40 minutes.

[0055] (4) The surface of the melamine decorative panel is then fumigated with hot water vapor.

[0056] (5) Dry the outer surface of the melamine decorative panel for 1-3 hours.

[0057] (6) Brush the surface of the melamine decorative panel with a layer of 2-3mm thick hardening material, and wait for the hardening material to dry for later use.

[0058] (7) Finally, brush the strengthening liquid on the surface of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a surface hardening treatment process of a melamine decorative panel. The surface hardening treatment process comprises the following steps: firstly, the melamine decorative panel is hung on a jig and cleaned through ultrasonic waves; then the melamine decorative panel is soaked in soda for 10-30 minutes; and then the melamine decorative panel is irradiated under an ultraviolet lamp with the wavelength being 220-240 nm for 10 minutes. According to the surface hardening treatment process of the melamine decorative panel, the melamine decorative panel is cleaned firstly, then subjected to antioxidant treatment through a tartaric acid solution, and then dried; the outer surface of the melamine decorative panel is hardened through a hardening material to obtain a layer of impact-resistant protective film; finally, the hardening degree of the outer surface is increased through reinforcing liquid; and compared with a traditional mode that the melamine decorative panelis hardened only through paint brushing, according to the treatment process, the strength and flexibility of the outer surface of the melamine decorative panel are higher, and a good resistance effecton the impact load is achieved.

Description

technical field [0001] The invention relates to the technical field of decorative panels, in particular to a surface hardening treatment process for melamine decorative panels. Background technique [0002] Melamine decorative panel, referred to as melamine board, the full name is melamine impregnated film paper veneer wood-based panel, its manufacturing process is to soak paper with different colors or textures in melamine resin adhesive, and then dry to a certain degree of curing, It is paved on the surface of particleboard, moisture-proof board, medium density fiberboard, plywood, blockboard, multi-layer board or other hard fiberboard, and is a decorative board formed by hot pressing. In the production process, it is generally composed of several layers of paper, and the number depends on the use. Melamine decorative panels are often used in interior construction and decoration of various furniture and cabinets. There are also some panels, walls, and cabinets. Cabinet la...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B44C5/04C09D1/00C09D7/61C09D7/63C09D7/65
Inventor 李光伟
Owner FOSHAN CITY YATE OFFICE FURNITURE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com