Caulking agent for ceramic tiles

A kind of jointing agent and ceramic tile technology, applied in the field of tile jointing agent, can solve the problems of efflorescence, unsightly surface, weak adhesion, etc. on the surface of the building joints, so as to inhibit the efflorescence phenomenon, improve the flexibility, and increase the viscosity. Effect

Inactive Publication Date: 2019-05-28
蔡京翠
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, after the existing tile jointing agent is used, because the cement mortar material contains a lot of free calcium hydroxide, it can cause the surface of the building joint to be blotted with alkali, and there will be an unsightly phenomenon; in addition, the existing jointing agent cannot Effectively prevent the erosion of microorganisms such as mold and algae; the joint agent has poor flexibility, weak adhesion, low water resistance and impermeability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] In order to make the objectives, technical solutions, and advantages of the present invention clearer and more comprehensible, the present invention will be further described in detail below in conjunction with embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, but not to limit the present invention.

[0008] A tile jointing agent, comprising the following components: 20 parts of 32.5 white cement; 40 parts of heavy calcium powder of 400 mesh; 0.84 parts of 1# colloidal crystal; 2 parts of high activity silica; 2 parts of bactericide; 3 parts of adsorbent Parts; 4 parts of 108 glue, 5 parts of curing agent.

[0009] The present invention can significantly reduce the content of free calcium hydroxide in the cement mortar material due to the addition of high-activity silica in the jointing agent, thereby inhibiting the generation of efflorescence on the surface of the cement mortar; due to the addit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a caulking agent for ceramic tiles. The caulking agent is prepared from the following components: 10 to 20 parts of 32.5 white cement, 20 to 40 parts of 400-mesh calcium triple superphosphate powder, 0.42 to 0.84 part of 1# colloidal crystal, 1 to 2 parts of high-activity silicon dioxide, 1 to 2 parts of fungicide, 1 to 3 parts of an adsorbent, 2 to 4 parts of 108 glue and1 to 5 parts of a curing agent. The caulking agent involved in the invention can effectively prevent the erosion of microorganisms such as mildew and algae, has strong adhesive force, and has the characteristics of simple components and low cost.

Description

Technical field [0001] The invention relates to the technical field of building materials, in particular to a tile jointing agent. Background technique [0002] At present, after the existing tile jointing agent is used, because the cement mortar material contains free calcium hydroxide for a long time, it can cause the surface of the building joints to be efflorescence, which is unsightly. In addition, the existing jointing agent cannot Effectively prevent the corrosion of molds, algae and other microorganisms; the jointing agent has poor flexibility, weak adhesion, low water resistance and impermeability. Summary of the invention [0003] The purpose of the present invention is to overcome the shortcomings of the prior art and provide a tile grout. [0004] The present invention is realized through the following technical solutions: [0005] A tile jointing agent, comprising the following components: 32.5 white cement 10-20 parts; 400 mesh heavy calcium powder 20-40 parts; 1# coll...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B14/06C04B24/26C04B111/20
Inventor 蔡京翠
Owner 蔡京翠
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com