Anti-slip wood-plastic floor and production method

A technology of wood-plastic floor and production method, applied in the field of wood-plastic floor, can solve the problems of poor anti-skid performance, low wear coefficient and elastic coefficient of the floor, and achieve the advantages of easy popularization and promotion, low brittleness and high elongation. Effect

Inactive Publication Date: 2019-05-31
安徽锦汇新材料科技有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The wood-plastic floor in the prior art has poor anti-skid performance during use, and the wear resistance coefficie

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-slip wood-plastic floor and production method
  • Anti-slip wood-plastic floor and production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Embodiment 1. The raw materials used in the manufacture of non-slip wood-plastic flooring are as follows in parts by weight:

[0050] 15-16 parts of resin, 13-14 parts of styrene-butadiene rubber, 30-40 parts of wood powder, 3-4 parts of silicon dioxide, 6-9 parts of epoxy resin, 15-20 parts of calcium carbonate, 5- 8 parts, 2-3 parts of coupling agent, 2-3 parts of other additives.

[0051] S1: Add styrene-butadiene rubber, resin, plasticizer oil and toughening agent into the melting furnace according to the above weight, and add other additives to melt at the same time;

[0052] S2: Then add silicon dioxide, epoxy resin, calcium carbonate, plasticizer oil and coupling agent into the melting furnace, stir at high speed for 15-20 minutes to granulate;

[0053] S3: Extrude the mixed raw material obtained in S2 through a twin-screw extruder, and the temperature of each zone of the extruder is:

[0054] Zone 1 temperature: 160~165℃,

[0055] Zone 2 temperature: 165~170℃...

Embodiment 2

[0063] Embodiment 2. The raw materials used in the manufacture of non-slip wood-plastic flooring are as follows in parts by weight:

[0064] 16-17 parts of resin, 14-15 parts of styrene-butadiene rubber, 30-40 parts of wood powder, 3-4 parts of silicon dioxide, 6-9 parts of epoxy resin, 15-20 parts of calcium carbonate, 5- 8 parts, 2-3 parts of coupling agent, 3 parts of toughening agent, 2-3 parts of other additives.

[0065] S1: Add styrene-butadiene rubber, resin, plasticizer oil and toughening agent into the melting furnace according to the above weight, and add other additives to melt at the same time;

[0066] S2: Then add silicon dioxide, epoxy resin, calcium carbonate, plasticizer oil and coupling agent into the melting furnace, stir at high speed for 15-20 minutes to granulate;

[0067] S3: Extrude the mixed raw material obtained in S2 through a twin-screw extruder, and the temperature of each zone of the extruder is:

[0068] Zone 1 temperature: 160~165℃,

[0069]...

Embodiment 3

[0077] Embodiment 3, the raw materials used in the manufacture of anti-skid type wood-plastic floor are as follows in parts by weight:

[0078] 16-17 parts of resin, 15-16 parts of styrene-butadiene rubber, 30-40 parts of wood powder, 3-4 parts of silicon dioxide, 6-9 parts of epoxy resin, 15-20 parts of calcium carbonate, 5- 8 parts, 2-3 parts of coupling agent, 3-4 parts of toughening agent, 2-3 parts of other additives.

[0079] S1: Add styrene-butadiene rubber, resin, plasticizer oil and toughening agent into the melting furnace according to the above weight, and add other additives to melt at the same time;

[0080] S2: Then add silicon dioxide, epoxy resin, calcium carbonate, plasticizer oil and coupling agent into the melting furnace, stir at high speed for 15-20 minutes to granulate;

[0081] S3: Extrude the mixed raw material obtained in S2 through a twin-screw extruder, and the temperature of each zone of the extruder is:

[0082] Zone 1 temperature: 160~165℃,

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-slip wood-plastic floor and a production method. The anti-slip wood-plastic floor comprises 15-18 parts of resin, 13-16 parts of butadiene styrene rubber, 30-40 parts of wood powder, 3-4 parts of silicon dioxide, 6-9 parts of epoxy resin, 15-20 parts of calcium carbonate, 5-8 parts of plasticizing oil, 2-3 parts of coupling agents, 3-5 parts of flexibilizers and 2-3parts of other auxiliaries. The added butadiene styrene rubber with good thermoplasticity, rebound elasticity and wear resistance and excellent slip resistance and vibration reducing performance is melted to prepare the wood-plastic floor, the floor can prevent slip and is comfortable and convenient to popularize, active groups of the added flexibilizers can chemically react with the resin, a reaction product is incompletely compatible after curing, so that the phase of the resin is separated, the physical performance and the structure of the epoxy resin can be effectively improved, the elongation of the epoxy resin is increased after curing, the brittleness of the epoxy resin is decreased, cracks of the wood-plastic floor in use are prevented, the flexibility of the floor is improved, and the service life of the floor is prolonged.

Description

technical field [0001] The invention relates to the technical field of wood-plastic flooring, in particular to an anti-slip wood-plastic flooring and a production method thereof. Background technique [0002] Wood-plastic flooring is a floor made of wood-plastic composite materials. It has the same processing characteristics as wood. It can be sawed, drilled, and nailed with ordinary tools. It is very convenient and can be used like ordinary wood. At the same time, it has the woody feeling of wood and the water-resistant and anti-corrosion properties of plastic, making it an excellent and durable outdoor waterproof and anti-corrosion building material. [0003] The wood-plastic floor in the prior art has poor anti-slip performance during use, and the wear resistance coefficient and elastic coefficient of the floor are not high, so it cannot give people a good sense of comfort when stepping on it. Therefore, need badly a kind of antiskid type wood-plastic floor and productio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L97/02C08L101/00C08L9/06C08L63/00C08K13/02C08K5/12C08K3/36C08K3/26E04F15/10B29C48/92
Inventor 汪洋
Owner 安徽锦汇新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka