Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Premixed mortar

A technology of ready-mixed mortar and sand material, which is applied in the field of ready-mixed mortar, can solve problems such as cracking of building plastering mortar, insufficient strength, unstable project quality, etc., and achieve low cost, high tensile strength, and low cost. The effect of easy shrinkage and cracking

Inactive Publication Date: 2019-06-28
广州市东浦建材有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the influence of the technical proficiency of the construction personnel and the quality of various raw materials such as cement and sand, the mortar used on the construction site, whether it is masonry mortar, plastering mortar, or ground leveling mortar, often has cracking phenomena in building plastering mortar ( Even if the most traditional clay brick walls are plastered with cement mortar, there will be large-scale cracks), resulting in unstable project quality, insufficient strength, and even poor quality, which has become a common problem in construction quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: a kind of ready-mixed mortar of the present invention, by weight, comprises following components: 50 parts of iron slag, 30 parts of fly ash, 20 parts of cement, 40 parts of sand material, 5 parts of wood fiber, latex powder 3 parts, 2 parts of calcium nitrite, and 15 parts of sepiolite, wherein the cement is preferably 32.5 grade ordinary Portland cement, and the sand material is preferably quartz sand with a particle size of 50 mesh, and its water content is less than 3%.

Embodiment 2

[0013] Embodiment 2: a kind of ready-mixed mortar of the present invention comprises following components by weight: 60 parts of iron slag, 40 parts of fly ash, 30 parts of cement, 50 parts of sand material, 8 parts of wood fiber, latex powder 5 parts, 4 parts of calcium nitrite, 20 parts of sepiolite, wherein the cement is preferably 32.5 grade ordinary Portland cement, and the sand material is preferably 60-mesh quartz sand with a water content of less than 3%.

Embodiment 3

[0014] Embodiment 3: a kind of ready-mixed mortar of the present invention, by weight, comprises following components: 80 parts of iron slag, 50 parts of fly ash, 40 parts of cement, 60 parts of sand material, 10 parts of wood fiber, latex powder 6 parts, 5 parts of calcium nitrite, and 25 parts of sepiolite, wherein the cement is preferably 32.5 grade ordinary Portland cement, and the sand material is preferably quartz sand with a particle size of 70 mesh, and its water content is less than 3%.

[0015] The ready-mixed mortar of the present invention has high tensile strength, strong cohesive force, and is not easy to shrink and crack; the cost is low, and a large amount of industrial waste is used, which not only reduces the product cost but also can turn waste into treasure, which is beneficial to energy saving Environmental friendly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
water contentaaaaaaaaaa
Login to View More

Abstract

The invention discloses premixed mortar. The premixed mortar contains the following components in parts by weight: 50-80 parts of iron-ore slag, 30-50 parts of coal ash, 20-40 parts of cement, 40-60 parts of sand, 5-10 parts of wood fibers, 3-6 parts of latex powder, 2-5 parts of calcium nitrite and 15-25 parts of sepiolite. The premixed mortar is high in tensile strength and strong in adhesion force and unlikely to be drily shrunk and cracked; the cost is low, and a large quantity of industrial wastes are adopted, so that the product cost is lowered, waste can be turned into wealth, and the energy conservation and the environment protection are promoted.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a ready-mixed mortar. Background technique [0002] With the improvement of people's living standards, the requirements for building quality are getting higher and higher. Due to the influence of the technical proficiency of the construction personnel and the quality of various raw materials such as cement and sand, the mortar used on the construction site, whether it is masonry mortar, plastering mortar, or ground leveling mortar, often has cracking phenomena in building plastering mortar ( Even if the most traditional clay brick wall is plastered with cement mortar, there will be large-scale cracking), resulting in unstable project quality, insufficient strength, and even poor quality, which has become a common problem in construction quality. Contents of the invention [0003] In order to overcome the deficiencies of the prior art, the invention provides a ready-mixed mort...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/34
Inventor 黄远建熊长鹏冯颖怡
Owner 广州市东浦建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com