A strontium-bismuth-titanium-based energy storage medium material for medium-temperature sintering and its preparation method

A strontium-bismuth-titanium-based storage and dielectric material technology is applied in the direction of fixed capacitor dielectric, fixed capacitor parts, fixed capacitors, etc., which can solve the difficult problems of improving the structure of multilayer ceramic capacitors, and achieve good practical value and high Effect of insulation resistivity and low loss

Active Publication Date: 2021-12-24
BEIJING YUANLIU HONGYUAN ELECTRONICS TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, due to the limitation of equipment and technology level, it is difficult to further improve the structure of multilayer ceramic capacitors.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A strontium-bismuth-titanium-based energy storage medium material for medium-temperature sintering and its preparation method
  • A strontium-bismuth-titanium-based energy storage medium material for medium-temperature sintering and its preparation method
  • A strontium-bismuth-titanium-based energy storage medium material for medium-temperature sintering and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] A method for preparing a strontium-bismuth-titanium-based energy storage medium material for medium-temperature sintering according to the invention, comprising:

[0048] Step 1, prepare base material:

[0049] Weigh analytically pure SrCO at a molar ratio of 1:x:(1+3x) 3 、 Bi 2 o 3 and TiO 2 Raw materials, wherein 0.04≤x≤0.11; put the weighed raw materials into a ball mill jar equipped with zirconia balls, and conduct mixed ball milling with deionized water as the medium, which lasts 7 to 9 hours; dry in an oven, dry The temperature is 110°C-120°C, and the drying time is 6-8 hours; calcined in a muffle furnace at 1100°C-1200°C for 2-3 hours to obtain SrO-xBi 2 o 3 -(1+3x)TiO 2 Powder.

[0050] Step 2. According to the ratio of the above-mentioned base material, modifier and sintering aid, weigh the base material, modifier and sintering aid, put them into a ball mill tank equipped with zirconia balls, add deionized water ball mill 5 hours, dried at 120°C for 6 h...

Embodiment 1

[0054] The invention provides a strontium-bismuth-titanium-based energy storage medium material for medium-temperature sintering, including a base material, a modifier and a sintering aid; wherein:

[0055] SrO-xBi 2 o 3 -(1+3x)TiO 2 To analyze pure SrCO 3 、 Bi 2 o 3 and TiO 2 As a raw material, weigh SrCO with a molar ratio of 1:0.04:1.12 3 、 Bi 2 o 3 and TiO 2 Raw materials, put the weighed raw materials into a ball mill tank equipped with zirconia balls, and carry out mixed ball milling with deionized water as a medium for 9 hours; then dry them in an oven at a drying temperature of 110°C for 8 hours ; Calcined at 1200°C for 2 hours in a muffle furnace to obtain SrO-0.04Bi 2 o 3 -1.12TiO 2 Powder.

[0056] Weigh the base material, modifier and sintering aid according to the weight ratio in Table 1 (unit: gram), use deionized water as the medium, ball mill and mix for 5 hours, dry at 120°C for 6 hours, and take out the ceramic powder After grinding and passing ...

Embodiment 2

[0064] The invention provides a strontium-bismuth-titanium-based energy storage medium material for medium-temperature sintering, including a base material, a modifier and a sintering aid; wherein:

[0065] SrO-xBi 2 o 3 -(1+3x)TiO 2 To analyze pure SrCO 3 、 Bi 2 o 3 and TiO 2 As a raw material, weigh SrCO with a molar ratio of 1:0.11:1.33 3 、 Bi 2 o 3 and TiO 2 Raw materials, put the weighed raw materials into a ball mill tank equipped with zirconia balls, and carry out mixed ball milling with deionized water as a medium for 7 hours; then dry them in an oven at a temperature of 120°C, and dry The time is 6 hours; then calcined in a muffle furnace at 1100°C for 3 hours to obtain SrO-0.11Bi 2 o 3 -1.33TiO 2 Powder.

[0066] Weigh the base material, modifier and sintering aid according to the weight ratio in Table 3 (unit: gram), use deionized water as the medium, ball mill and mix for 5 hours, dry at 120°C for 6 hours, and take out the ceramic powder After grindin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a strontium-bismuth-titanium-based energy storage medium material for medium temperature sintering and a preparation method, comprising a base material, a modifier and a sintering aid; the base material is SrO-xBi 2 O 3 ‑(1+3x)TiO 2 , 0.04≤x≤0.11; the modifier includes MnCO 3 , Mg(OH) 2 , Co 2 O 3 , and SrZrO 3 , CeO 2 and Y 2 O 3 One or more of them; sintering aids include H 3 BO 3 , ZnO, CaCO 3 and SiO 2 two or more of them. The invention adopts the solid phase method to prepare SrO-xBi 2 O 3 ‑(1+3x)TiO 2 Base material, by adding modifiers and sintering aids, an energy storage medium with high dielectric constant, breakdown strength and insulation resistivity, low loss and sintering temperature, and a stable and adjustable temperature coefficient can be obtained Material.

Description

technical field [0001] The invention relates to the technical field of electronic information materials and components, in particular to a strontium-bismuth-titanium-based energy storage medium material for medium-temperature sintering and a preparation method thereof. Background technique [0002] Energy storage capacitors have broad applications in fields such as hybrid electric vehicles, pulse power supplies, radar, and aerospace. With the development of technology, energy storage capacitors are mainly developed in the direction of miniaturization, light weight, high withstand voltage, high reliability and high energy storage. In order to meet the development trend of energy storage capacitors, the main measures are: (1) optimize the capacitor structure and adopt multilayer ceramic capacitor structure; (2) improve the performance of dielectric materials, such as increasing the dielectric constant, increasing the breakdown strength and reducing loss . At present, due to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/47C04B35/622C04B35/63H01G4/12
CPCC04B35/47C04B35/622C04B35/6303H01G4/1218H01G4/1209C04B2235/3298C04B2235/3206C04B2235/3267C04B2235/3275C04B2235/3225C04B2235/3229C04B2235/3248C04B2235/3208C04B2235/3284C04B2235/3418C04B2235/3409
Inventor 杨魁勇程华容齐世顺宋蓓蓓
Owner BEIJING YUANLIU HONGYUAN ELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com