Easy-to-peel hot sealing film

A heat-sealing film and easy-peeling technology, applied in the field of new materials, can solve the problems of high electric heat loss of sealing equipment, high heat-sealing temperature, inconvenient use, etc., and achieve lower heat-sealing temperature, good compatibility, and ease of use Effect

Inactive Publication Date: 2019-07-23
合肥绿普包装材料有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Heat-sealing bags are widely used in daily chemical product packaging, food and drug packaging and other fields. At present, the commonly used heat-sealing films are polyethylene films or polypropylene films. However, although polypropylene films used for heat sealing have better stiffness , Tensile strength, but when it is processed, the required heat-sealing temperature is high, resulting in high electric heat loss of the sealing equipment, and the peeling force is large, it is not easy to peel off, causing greater inconvenience in use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Easy-to-peel hot sealing film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An easy-peelable heat-sealing film made of the following components in parts by weight: polypropylene resin 75, polyethylene terephthalate 18, modifier 8, basalt fiber 7, nano-titanium dioxide 1.2, coupling Agent 1.5, amidated modified vermiculite powder 12, plasticizer 1;

[0018] Described modifying agent preparation method comprises the following steps:

[0019] Dissolve the rosin resin in the organic solvent in the reaction kettle according to the mass ratio of 3.2:15, heat to 75°C, stir at 1200r / min for 40min, feed nitrogen into the reaction kettle, remove the air in the reaction kettle, and then add Fmoc-glycine and 4-dimethylaminopyridine, the molar ratio of Fmoc-glycine and 4-dimethylaminopyridine is 1:1.2, the addition of Fmoc-glycine is 3.8% of the rosin resin quality, and the temperature is adjusted to 92°C , stirred at 1000r / min for 2 hours, let stand for 1 hour, cooled the temperature in the reactor to 0°C and kept it for 10 minutes, then added dropwise 10...

Embodiment 2

[0028] An easy-peelable heat-sealing film made of the following components in parts by weight: polypropylene resin 78, polyethylene terephthalate 22, modifier 10, basalt fiber 11, nano-titanium dioxide 1.4, coupling Agent 1.7, amidated modified vermiculite powder 15, plasticizer 2;

[0029] Described modifying agent preparation method comprises the following steps:

[0030] Dissolve the rosin resin in the organic solvent in the reaction kettle according to the mass ratio of 3.2:15, heat to 75°C, stir at 1200r / min for 40min, feed nitrogen into the reaction kettle, remove the air in the reaction kettle, and then add Fmoc-glycine and 4-dimethylaminopyridine, the molar ratio of Fmoc-glycine and 4-dimethylaminopyridine is 1:1.2, the addition of Fmoc-glycine is 3.8% of the rosin resin quality, and the temperature is adjusted to 92°C , stirred at 1000r / min for 2 hours, let stand for 1 hour, cooled the temperature in the reactor to 0°C and kept it for 10 minutes, then added dropwise ...

Embodiment 3

[0039] An easy-peelable heat-sealing film, made of the following components in parts by weight: polypropylene resin 76, polyethylene terephthalate 20, modifier 9, basalt fiber 10, nano-titanium dioxide 1.3, coupling Agent 1.6, amidated modified vermiculite powder 13, plasticizer 1.5;

[0040] Described modifying agent preparation method comprises the following steps:

[0041]Dissolve the rosin resin in the organic solvent in the reaction kettle according to the mass ratio of 3.2:15, heat to 75°C, stir at 1200r / min for 40min, feed nitrogen into the reaction kettle, remove the air in the reaction kettle, and then add Fmoc-glycine and 4-dimethylaminopyridine, the molar ratio of Fmoc-glycine and 4-dimethylaminopyridine is 1:1.2, the addition of Fmoc-glycine is 3.8% of the rosin resin quality, and the temperature is adjusted to 92°C , stirred at 1000r / min for 2 hours, let stand for 1 hour, cooled the temperature in the reactor to 0°C and kept it for 10 minutes, then added dropwise...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an easy-to-peel hot sealing film. The easy-to-peel hot sealing film is prepared from the following components: polypropylene resin, polyethylene terephthalate, a modifying agent, basalt fibers, nano titanium dioxide, a coupling agent, amidation modified vermiculite flour and a plasticizer. The easy-to-peel hot sealing film prepared by the invention is applicable to heat-sealing packing of objects including various foods and the like and has good peeling performance.

Description

technical field [0001] The invention belongs to the field of new materials, and in particular relates to an easily peelable heat-sealing film. Background technique [0002] Heat-sealing bags are widely used in daily chemical product packaging, food and drug packaging and other fields. At present, the commonly used heat-sealing films are polyethylene films or polypropylene films. However, although polypropylene films used for heat sealing have better stiffness , Tensile strength, however, when it is processed, the required heat-sealing temperature is higher, resulting in higher electric heat loss of the sealing equipment, and the peeling force is larger, it is not easy to peel off, causing greater inconvenience in use. Contents of the invention [0003] The object of the present invention is to provide an easy-peelable heat-sealing film for the existing problems. [0004] The present invention is achieved through the following technical solutions: [0005] An easy-peelabl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L67/02C08L93/04C08K13/06C08K7/10C08K3/22C08K9/04C08K3/34C08K5/11C08J5/18
CPCC08J5/18C08J2323/12C08J2467/02C08J2493/04C08K3/34C08K5/11C08K7/10C08K9/04C08K13/06C08K2003/2241C08K2201/011
Inventor 张腾飞
Owner 合肥绿普包装材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com