Wet water high anti-skid ink-jet ceramic tile with sunken glaze effect and preparation method of tile

A ceramic tile and anti-skid technology, applied in the field of ceramic tile production and manufacturing, can solve the problems of difficult cleaning, easy to hide dirt, monotonous decorative visual effect, etc., and achieve the effects of bright color, excellent pollution resistance and good decorative effect.

Active Publication Date: 2019-07-26
MONALISA GRP CO LTD
View PDF10 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The glazed surface of ceramic tiles using this process is uneven, which is easy to hide dirt and difficult to clean, and also affects the visual aestheti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wet water high anti-skid ink-jet ceramic tile with sunken glaze effect and preparation method of tile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Step 1: Prepare the green body. The green body is obtained by pressing the ceramic base material commonly used in the field.

[0043] Step 2: Prepare anti-slip surface glaze according to the proportion: 50% potassium feldspar, 7% kaolin, 12% quartz, 11% calcined alumina, 5% nepheline, 7% zirconium silicate, 2% zinc oxide, 6% barium carbonate %. The chemical composition of the anti-skid glaze is: SiO 2 : 54.82%, Al 2 o 3 : 22.96%, Fe 2 o 3 : 0.2%, TiO 2 : 0.06%, CaO: 0.5%, MgO: 0.17%, K 2 O: 4.83%, Na 2 O: 2.74%, BaO: 4.65%, ZnO: 2%, ZrO 2 : 4.46%, loss on ignition: 2.83%. The non-slip surface glaze is poured on the dried brick adobe by glazing. The specific gravity of the glaze is 1.84, and the amount of glaze is 420g / m 2 .

[0044] Step 3: Use an inkjet machine to inkjet print the pattern.

[0045] Step 4: prepare gloss effect glaze according to the ratio: albite 68%: calcined kaolin: 15%, wollastonite: 10%, calcined talc: 6%, calcined zinc oxide 1%. The...

Embodiment 2

[0052] Step 1: Prepare the green body. The green body is obtained by pressing the ceramic base material commonly used in the field.

[0053] Step 2: Prepare anti-slip surface glaze according to the ratio: 40% potassium feldspar, 10% albite feldspar, 10% kaolin, 8% quartz, 8% calcined alumina, 10% zirconium silicate, 10% barium carbonate, oxide Zinc 4%. The chemical composition of the anti-skid glaze is: SiO 2 : 51.40%, Al 2 o 3 : 19.60%, Fe 2 o 3 : 0.22%, TiO 2 : 0.06%, CaO: 0.25%, MgO: 0.17%, K 2 O: 3.84%, Na 2 O: 2.34%, BaO: 7.75%, ZnO: 3.99%, ZrO 2 : 6.37%, loss on ignition: 3.76%. The non-slip surface glaze is poured on the dried brick adobe by glazing. The specific gravity of the glaze is 1.80, and the amount of glaze is 500g / m 2 .

[0054] Step 3: Use an inkjet machine to inkjet print the pattern.

[0055] Step 4: Prepare gloss effect glaze according to the ratio: albite 58%: calcined kaolin: 13%, wollastonite: 15%, calcined talc: 10%, calcined zinc oxide 3...

Embodiment 3

[0061] Step 1: Prepare the green body. The green body is obtained by pressing the ceramic base material commonly used in the field.

[0062] Step 2: Prepare the anti-slip surface glaze according to the proportion: 45% potassium feldspar, 5% albite feldspar, 8.5% kaolin, 10% quartz, 9.5% calcined alumina, 2.5% nepheline, 3% zinc oxide, silicon Zirconium acid 8.5%, barium carbonate 8%. The chemical composition of the anti-skid glaze is: SiO 2 : 53.04%, Al 2 o 3 : 21.28%, Fe 2 o 3 : 0.22%, TiO 2 : 0.06%, CaO: 0.39%, MgO: 0.17%, K 2 O: 4.33%, Na 2 O: 2.54%, BaO: 6.20%, ZnO: 2.99%, ZrO 2 : 5.42%, loss on ignition: 3.36%. The non-slip surface glaze is poured on the dried brick adobe by glazing. The specific gravity of the glaze is 1.82, and the amount of glaze is 460g / m 2 .

[0063] Step 3: Use an inkjet machine to inkjet print the pattern.

[0064] Step 4: Prepare gloss effect glaze according to the ratio: albite 63%: calcined kaolin: 14%, wollastonite: 12.5%, calcine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a wet water high anti-skid ink-jet ceramic tile with a sunken glaze effect and a preparation method of the tile. The preparation method includes sequentially applying anti-skidsurface glaze, decorative patterns, bright effect glaze and anti-skid protective glaze on a blank body, and then firing, wherein the mineral composition of the composition of the anti-skid surface glaze comprises 40-50% of potassium feldspar, 0-10% of albite, 7-10% of kaolin, 8-12% of quartz, 8-11% of calcined alumina, 0-5% of nepheline, 2-4% of zinc oxide, 7-10% of zirconium silicate and 6-10% ofbarium carbonate; and the mineral composition of the composition of the anti-skid protective glaze comprises 48-58% of potassium feldspar, 0-10% of albite, 10-20% of kaolin, 0-5% of quartz, 0-4% of nepheline, 2-5% of calcined alumina, 10-15% of barium carbonate and 5-8% of zinc oxide. The anti-skid ceramic tile can be used as a decorative material with a good decorative effect, excellent pollution resistance and anti-skid performance, and can be applied to the field of home decoration.

Description

technical field [0001] The invention relates to a wet water high anti-slip ink-jet ceramic brick with a sunken glaze effect and a preparation method thereof, belonging to the technical field of ceramic brick production. Background technique [0002] As a decorative material with good decorative effect and excellent pollution resistance, ceramic tiles are widely used in luxurious and high-end hotels, commercial buildings, office buildings, and family apartments. However, ceramic tiles ignore the slippery ground while beautifying the environment. And it is easy to cause the problem of slipping, and the accidents of falling and falling are frequent because the ground is too smooth. [0003] At present, a small number of ceramic tiles with anti-slip effect on the market basically use screen-printed convex glaze or spray some high-temperature dry particles to make the glaze surface uneven after firing to prevent slipping. The glazed surface of ceramic tiles using this process is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/89C03C8/00
CPCC03C8/00C04B41/52C04B41/89C04B41/4539C04B41/5022
Inventor 萧礼标汪陇军王贤超杨元东覃增成程科木
Owner MONALISA GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap