Special water-based ink for polyethylene-polyvinyl acetate thin films and preparation method of ink

A technology of water-based ink and polyvinyl ester, which is applied in ink, applications, household appliances, etc., and can solve problems such as false drying of printed matter, affecting printing production efficiency, and air pollution

Pending Publication Date: 2019-07-30
重庆宏图新材料科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, most manufacturers currently using polyethylene-vinyl acetate film printing are still using traditional solvent inks. Organic solvents in solvent-based inks account for 30% to 50% of the total ink. These organic solvents are alcohols , such as butanol, isopropanol, etc.; ethers, in the process of manufacture and use, a large amount of solvents volatilize, workers working in this environment for a long time will cause great damage to the nervous system, and solvent-based inks will produce A large amount of VOCS causes air pollution, which has great disadvantages to VOCS treatment. Therefore, solvent-based ink is the biggest pollution in the printing industry at present. The printing coating amount of solvent-based ink is about 10% higher than that of water-based ink, and the printing cost is higher than that of water-based ink. Water-based ink, because polyethylene-polyvinyl acetate film is composed of PE and EVA, because PE

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special water-based ink for polyethylene-polyvinyl acetate thin films and preparation method of ink
  • Special water-based ink for polyethylene-polyvinyl acetate thin films and preparation method of ink
  • Special water-based ink for polyethylene-polyvinyl acetate thin films and preparation method of ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0093] A. Water-based ink binder (high molecular weight resin, hydrophilic value: 10-12) content: 20%

[0094] B. Rutile titanium dioxide content: 28%

[0095] C. Water-based ink dispersant liquid content: 1%

[0096] D. Alcohol solvent content: 25%

[0097] E. Deionized water content: 11.7%

[0098] F. High acid value acrylic acid content: 6%

[0099] G. Water-based ink binder (low molecular weight resin, hydrophilic value: 11-13) content: 5%

[0100] H. Adhesive content: 1.5%

[0101] J. Smoothing agent liquid content: 0.3%

[0102] K, weathering agent liquid content: 1.5%

[0103] White ink preparation includes the following steps:

[0104](1) Pre-dispersion of ingredients: According to the production process sheet, clean the special production material tank, and after checking the item number is correct, put part D alcohol solvent, part E deionized water in turn, after stirring and mixing evenly, put A water-based Ink binder (high molecular weight resin, hydrophili...

Embodiment 2

[0108] A. Water-based ink binder (high molecular weight resin, hydrophilic value: 10-12) content: 20%

[0109] B. Rutile titanium dioxide content: 29%

[0110] C. Water-based ink dispersant liquid content: 1%

[0111] D. Alcohol solvent content: 24%

[0112] E. Deionized water content: 11.7%

[0113] F. High acid value acrylic acid content: 6%

[0114] G. Water-based ink binder (low molecular weight resin, hydrophilic value: 11-13) content: 5%

[0115] H. Adhesive content: 1.5%

[0116] J. Smoothing agent liquid content: 0.3%

[0117] K, weathering agent liquid content: 1.5%

[0118] (1) Pre-dispersion of ingredients: According to the production process sheet, clean the special production material tank, and after checking the item number is correct, put part D alcohol solvent, part E deionized water in turn, after stirring and mixing evenly, put A water-based Ink binder (high molecular weight resin, hydrophilic value: 10-12). Adjust the speed of the disperser to 300-40...

Embodiment 3

[0122] A. Water-based ink binder (high molecular weight resin, hydrophilic value: 10-12) content: 19%

[0123] B. Rutile titanium dioxide content: 30%

[0124] C. Water-based ink dispersant liquid content: 1%

[0125] D. Alcohol solvent content: 24%

[0126] E. Deionized water content: 11.7%

[0127] F. High acid value acrylic acid content: 6%

[0128] G. Water-based ink binder (low molecular weight resin, hydrophilic value: 11-13) content: 5%

[0129] H. Adhesive content: 1.5%

[0130] J. Smoothing agent liquid content: 0.3%

[0131] K, weathering agent liquid content: 1.5%

[0132] (1) Pre-dispersion of ingredients: According to the production process sheet, clean the special production material tank, and after checking the item number is correct, put part D alcohol solvent, part E deionized water in turn, after stirring and mixing evenly, put A water-based Ink binder (high molecular weight resin, hydrophilic value: 10-12). Adjust the speed of the disperser to 300-40...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a special water-based ink for polyethylene-polyvinyl acetate thin films and a preparation method of the ink. The ink comprises, by weight, a first water-based ink connecting material, a coloring agent, a water-based ink dispersing agent liquid, an alcohol solvent, 10-15% of deionized water, high-acid-value acrylic acid, 4-5% of a second water-based ink connecting material,1.5-2% of an adherence promoter, 0.3-0.4% of a slipping agent liquid and 1-2% of a weather-resistant agent liquid, wherein the first water-based ink connecting material is high-molecular-weight resin,and the hydrophilic value of the high-molecular-weight resin is 10-12; The second water-based ink connecting material is low-molecular-weight resin, and the hydrophilic value of the low-molecular-weight resin is 11-13. The ink prepared through the method has the advantages of being good in liquidity, excellent in shallow screen printing transfer effect, high in printing adaptability and the like.

Description

technical field [0001] The invention relates to the technical field of water-based ink, in particular to a special water-based ink for polyethylene-vinyl acetate film and a preparation method thereof. Background technique [0002] With the continuous enhancement of human environmental protection awareness, green environmental protection has become the development theme of the 21st century. In recent years, many countries have increased the requirements and constraints of hygiene and environmental protection in packaging and printing. Due to the use of organic solvent inks and varnishes, It will emit hydrocarbons, pollute the air, and damage health. Therefore, at present, printing materials in developed countries basically no longer use solvent-based printing materials. Research, development and application of pollution-free, less-polluting, and pollution-free printing materials have become green packaging. The inevitable requirement of development, therefore, more attention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/033C09D11/107C09D11/10C09D11/03
CPCC09D11/03C09D11/033C09D11/10C09D11/107
Inventor 庞健赵静夏永颂
Owner 重庆宏图新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap