A kind of porcelain algal silica composite material and preparation method thereof

A technology of silicon composite material and porcelain, which is applied in the field of porcelain algae silicon composite material and its preparation, can solve the problems of poor air permeability, lack of adsorption of harmful gases, and high rigidity

Active Publication Date: 2021-07-06
宁国格闰新材料科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Common assembled buildings in China mostly use inorganic cement artificial stone, UHPC (Ultra High Performance Concrete) panels, ceramics, natural stone and other materials. They have the common disadvantages of high overall density, high rigidity, and poor air permeability. Lack of effective adsorption of harmful gases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of porcelain algal silica composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A porcelain algae silica composite material, comprising in parts by weight:

[0040] Kaolin 25Kg, diatomite 40Kg, cement 30Kg, silica fume 7Kg, basalt fiber 4Kg, magnesium oxide 10Kg, magnesium sulfate 20Kg, bamboo powder 40Kg, condensate fluid 1Kg.

[0041] A preparation method of porcelain algae silica composite material, comprising the steps of:

[0042] Step 1. Weigh the raw materials of each component according to the formula of the porcelain algae-silicon composite material for later use;

[0043] Step 2, premix the bamboo powder and cement evenly, then add magnesium oxide, magnesium sulfate, basalt fiber and silica fume to mix evenly for the second time, and finally add kaolin, diatomaceous earth and a small amount of water to mix evenly to obtain a mixed dry material;

[0044] Step 3. Add diatomite and kaolin to the high-speed mixer and mix at a speed of 1400-1500rpm for 5-15 minutes, so that the temperature of diatomite and kaolin in the high-speed mixer reach...

Embodiment 2

[0047] A kind of porcelain algae silicon composite material, comprises by weight Kg:

[0048] Kaolin 10Kg, diatomite 20Kg, cement 20Kg, silica fume 6Kg, basalt fiber 3Kg, magnesium oxide 5Kg, magnesium sulfate 10Kg, bamboo powder 30Kg, condensate fluid 1Kg.

[0049] The preparation method of the composite material of Example 2 is the same as that of Example 1.

Embodiment 3

[0051] A kind of porcelain algae silicon composite material, comprises by weight Kg:

[0052] Kaolin 50Kg, diatomite 60Kg, cement 20Kg, silica fume 10Kg, basalt fiber 6Kg, magnesium oxide 20Kg, magnesium sulfate 40Kg, bamboo powder 70Kg, condensate fluid 2Kg.

[0053] The preparation method of the composite material of embodiment 3 is the same as that of embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a porcelain algal silica composite material and a preparation method thereof, and relates to the technical field of inorganic building materials. Porcelain algal silica composite material includes 10-50 parts of kaolin, 20-60 parts of diatomite, 20-40 parts of cement, 5-10 parts of silica fume, 2-6 parts of basalt fiber, and 3-20 parts of magnesium oxide in parts by weight. 5-40 parts of magnesium sulfate, 20-70 parts of bamboo powder, and 0.2-2 parts of rock condensate; the preparation method is to mix the above raw materials evenly. The porcelain algae-silicon composite material prepared by the present invention is poured to form products such as plates, walls, and components. The obtained products have the advantages of smooth and smooth surface, fire and flame retardancy, moisture and mildew resistance, heat insulation and sound insulation, non-toxic and anti-aging, and can be adsorbed at the same time. Harmful substances such as formaldehyde in the air.

Description

technical field [0001] The invention belongs to the technical field of inorganic building materials, and in particular relates to a porcelain algal silica composite material and a preparation method thereof. Background technique [0002] Prefabricated buildings are becoming more and more common in the field of construction, such as low-rise buildings that use wood as the standard building material in the United States, Japan and other countries, or the common bungalow-style simple assembled buildings in China. [0003] Common assembled buildings in China mostly use inorganic cement artificial stone, UHPC (Ultra High Performance Concrete) panels, ceramics, natural stone and other materials. They have the common disadvantages of high overall density, high rigidity, and poor air permeability. Harmful gases lack effective adsorption. Contents of the invention [0004] The object of the present invention is to provide a porcelain algae-silicon composite material and its prepar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/30
CPCC04B28/30C04B2201/50C04B14/106C04B14/08C04B7/02C04B18/146C04B14/46C04B18/265C04B22/16C04B22/0013C04B24/06C04B22/142C04B24/383
Inventor 张永亮高艳慧
Owner 宁国格闰新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap