Cathode electrophoretic paint resin with high salt spray resistance and preparation method thereof

A cathodic electrophoresis and salt spray resistance technology, which is applied in the direction of electrophoretic coatings, coatings, etc., can solve the problems of not being able to achieve high salt spray resistance, so as to improve the salt spray resistance of the paint film, improve the quality, and high salt spray resistance performance effect

Inactive Publication Date: 2019-08-13
SHENZHEN CHIBOOM TECH CO LTD
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The salt spray resistance of existing electrophoretic coating resins is

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cathode electrophoretic paint resin with high salt spray resistance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] In order to have a clearer understanding of the technical features, purposes and effects of the present invention, the specific implementation manners of the present invention will now be described with reference to the accompanying drawings.

[0016] A kind of preparation method of cathodic electrophoretic paint resin of high salt spray resistance performance of the present invention, in its preferred embodiment, raw material comprises solvent, initiator, monomer and neutralizing agent; Said monomer comprises: methacrylic acid Methyl ester, styrene, hydroxyethyl methacrylate, dimethylaminoethyl methacrylate, butyl acrylate, phosphate monomer; the initiator includes: azobisisobutyronitrile; the solvent includes: isobutyronitrile One or more mixtures of propanol, ethylene glycol ether, ethylene glycol butyl ether, ethyl acetate, butyl acetate, ethylene glycol ether acetate and n-butanol; the neutralizer includes: formic acid, acetic acid and one of lactic acid;

[0017]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Disclosed are a cathode electrophoretic paint resin with high salt spray resistance and a preparation method thereof. Monomers adopted for the resin comprise monomers of methyl methacrylate, styrene,hydroxyethyl methacrylate, 2-(dimethylamino)ethyl methacrylate, butyl acrylate and phosphate; an initiator comprises azodiisobutyronitrile; a solvent is one or a mixture of more of isopropanol, ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, ethyl acetate, butyl acetate, ethylene glycol monoethyl ether acetate and n-butyl alcohol; a neutralizing agent comprises one of formic acid, acetic acid and lactic acid. The solvent is loaded in a reactor, the initiator and the solvent are added for stirring, and heating is conducted to 80-100 DEG C; a mixture of the monomers and the initiator is added dropwise 1-5 times for 2-4 hours, and after dropwise addition, heat preservation is conducted for 0.5-2.5 hours at 80-100 DEG C; the remaining initiator is added for supplementation twice, and after heat preservation continues for 0.5-2.5 hours, the electrophoretic paint resin is obtained. The cathode electrophoretic paint resin has high salt spray resistance, the salt spray resistance of a paint film of the electrophoretic paint is greatly improved, and the quality of a product processed by the electrophoretic paint is further improved.

Description

technical field [0001] The invention relates to a cathodic electrophoretic paint resin, in particular to a cathodic electrophoretic paint resin with high salt spray resistance and a preparation method thereof. Background technique [0002] With the continuous enhancement of people's ecological awareness, the development and application of environmentally friendly materials have attracted more and more attention. As a green and environmentally friendly water-based electrophoretic coating, people have attracted widespread attention. The special resin for water-based electrophoretic coatings based on water-based acrylic resin has become one of the research hotspots. one. With the continuous expansion of the scope of application of cathodic electrophoretic coatings, electrophoretic coatings are also used for decorative products such as various household appliances, hardware and office supplies, etc., which have high requirements for appearance, especially in the metal surface tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F220/34C08F220/14C08F212/08C08F220/20C08F220/18C08F230/02C09D5/44
CPCC08F220/34C09D5/4411C09D5/4488C08F220/14C08F212/08C08F220/20C08F220/1804C08F230/02
Inventor 李兵兵陈友志吴晓丹
Owner SHENZHEN CHIBOOM TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap