Low-compression permanent deformation rubber covered roller silicon rubber and preparation method thereof

A permanent deformation and silicone rubber technology, applied in the field of rubber rollers, can solve the problems of small compression set, high compression set, and high aging retention rate, and achieve the effects of small compression set, high aging retention rate, and simple preparation method

Inactive Publication Date: 2019-09-10
DONGGUAN NANJU POLYMER MATERIAL CO LTD
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the technical problems existing in the background technology, the present invention proposes a kind of low compression set cot silicone rubber and its preparation method, which solves the problems of existing cot silicone rubber temperature resistance difference and high compression set; Rubber matching, powder selection and treatment are carried out in multiple ways, and in the case of high strength and tearing, the compression set is small and the aging retention rate is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with specific embodiments. It should be understood that these descriptions are exemplary only, and are not intended to limit the scope of the present invention. Also, in the following description, descriptions of well-known structures and techniques are omitted to avoid unnecessarily obscuring the concept of the present invention.

[0035] A kind of low compression set cot silicone rubber and its preparation method proposed by the present invention, each component comprises: 100 parts of silicone rubber, 20-70 parts of white carbon black, 15-50 parts of filler, 1-3 parts of structural control agent, 2-6 parts of heat-resistant agent, 0.1-1 part of coupling agent and 0.1-1 part of mold release agent.

[0036] In the present invention, the silicone rubber of the rubber roller is stable in quality, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-compression permanent deformation rubber covered roller silicon rubber and a preparation method thereof. The rubber comprises the following components in parts by weight:100 parts of a silicon rubber, 20-70 parts of white carbon black, 15-50 parts of a filling agent, 1-3 parts of a structuring control agent, 2-6 parts of a heat resistant agent, 0.1-1 part of a coupling agent and 0.1-1 part of a demolding agent. The rubber covered roller silicon rubber disclosed by the invention is stable in quality, excellent in aging resistance, mechanical property, physical property and chemical property, and good in use effect. Meanwhile, the rubber covered roller silicon rubber is simple in preparation method, convenient in process, good in operability, stable in qualityand good in practicability, is capable of solving the problems that a conventional rubber covered roller silicon rubber is poor in temperature resistance and high in permanent compression deformation,and has the characteristics of being small in permanent compression deformation, high in aging resistance rate, and the like while high strength and tearing resistance are met, and modes such as silicon rubber matching and powder selection and treatment can be multiply modified.

Description

technical field [0001] The invention relates to the field of rubber rollers, in particular to a silicone rubber with low compression set for rubber rollers and a preparation method thereof. Background technique [0002] The rubber roller is generally a roller-shaped product made of a core of metal and other materials, and the outer surface is covered with rubber. The rubber material covered on the outside is different, the characteristics of the rubber roller are also different, and the application is also different. [0003] Rubber rollers can be divided into natural rubber rollers, butyl rubber rollers, nitrile rubber rollers, neoprene rubber rollers, ethylene propylene rubber rollers, fluorine rubber rollers, polyurethane rubber rollers, silicone rubber rollers and carbon fiber rollers according to their materials. Among them, the silicone rubber roller has good high temperature resistance, high pressure resistance, ozone resistance, chemical inertness and non-adhesion t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/07C08L83/04C08L83/05C08K9/06C08K3/36C08K3/22C08K3/26C08K7/26C08K5/098C08K13/06
CPCC08K2003/222C08K2003/2227C08K2003/2241C08K2003/265C08K2003/267C08K2201/011C08K2201/014C08L83/04C08L2201/08C08L2205/025C08K9/06C08K3/36C08K3/22C08K3/26C08K7/26C08K5/098C08K13/06
Inventor 徐雁南吴奇明
Owner DONGGUAN NANJU POLYMER MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products