Manufacturing method of copper-series flambed glaze

A manufacturing method and kiln-changing glaze technology, which is applied in the field of ceramics, can solve the problems of single kiln-changing glaze varieties and achieve the effect of ensuring health

Pending Publication Date: 2019-10-18
JIANGSU GAOCHUN CERAMICS
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the deepening of people's understanding of kiln-changing glaze, the beauty of kiln-changing defects has gradually been loved by people, so it is regarded as artistic enamel and appreciated by people. Especially in recent years, kiln-changing glaze can be used on daily tableware to make artistic ceramics practical Chemical use is the future development trend, and the existing ceramic patterns can no longer meet people's needs
[0004] In the patent document (CN109081589A) of the applicant's earlier application, a feather-shaped kiln-changing glaze is disclosed, which uses Fe 2 o 3 and MnO 2 As a coloring agent, ceramic melanin is used as a coloring correction agent to obtain a feather-shaped kiln-changing glaze with black and white colors, which meets the needs of users who prefer this color, but the variety of kiln-changing glazes with this color is still too single to satisfy other colors. Therefore, it is necessary to continue to develop kiln-changing glazes with more colors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of copper-series flambed glaze
  • Manufacturing method of copper-series flambed glaze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] In terms of parts by mass, the composition of the copper-based kiln underglaze includes: SiO 2 64.7; Al 2 o 3 11.6 copies; B 2 o 3 6.5 parts; Na 2 O is 2.71 parts; CaO is 5.39 parts; K 2 O is 4.21 parts; CuO is 3.8 parts; BaO is 0.75 parts; MgO is 0.42 parts; 2 3.62 parts; other ingredients are less than 1 part;

[0031] The composition of the topcoat includes: SiO 2 55.45 parts; CaO 6.23 parts; Al 2 o 3 10.4 copies; K 2 O is 3.86 parts; B 2 o 3 3.79 parts; Na 2 O is 1.93 parts; ZnO is 8.12 parts; Ca 3 (PO 4 ) 2 0.45 parts; TiO 2 It is 3.9 parts; other ingredients are less than 1 part.

[0032] Specifically, the following raw materials are used for preparation:

[0033] Bottom glaze raw materials: 26 parts of feldspar, 6 parts of Suzhou soil, 14 parts of quartz, 6 parts of calcite weight stone, 4 parts of titanium dioxide, 48 parts of frit, 4 parts of industrial copper oxide, and 4 parts of melanin 1 part, make the base glaze;

[0034] Surface glaze ...

Embodiment 2

[0047] In parts by mass, raw materials for the bottom glaze: 22 parts for feldspar, 7 parts for Suzhou soil, 17 parts for quartz, 4 parts for calcite, 2.5 parts for titanium dioxide, 53 parts for frit, 3 parts for industrial copper oxide, Melanin is 1.3 parts;

[0048] Surface glaze raw materials: 26 parts of feldspar, 8 parts of calcite, 35 parts of frit, 16.5 parts of quartz, 4 parts of Suzhou soil, 1.0 part of bone ash, 5 parts of titanium dioxide, 10 parts of industrial zinc oxide, Barium carbonate is 2.5 parts, and dolomite is 1 part.

[0049] The constituents of the above-mentioned frit and the pre-calcination of the raw materials zinc oxide and titanium dioxide are the same as in Example 1.

[0050] The preparation method of copper-based kiln variable glaze comprises the following steps:

[0051] (1) Preparation of bottom glaze slurry and top glaze slurry

[0052] Preparation of bottom glaze glaze slurry: mix bottom glaze raw materials: water: balls in a weight ratio...

Embodiment 3

[0059] In parts by mass, raw materials for the bottom glaze: 28 parts for feldspar, 5 parts for Suzhou soil, 14 parts for quartz, 7 parts for calcite, 4.5 parts for titanium dioxide, 46 parts for frit, 4.5 parts for industrial copper oxide, Melanin is 0.6 parts;

[0060] Surface glaze raw materials: 31 parts of feldspar, 10.3 parts of calcite, 26 parts of frit, 13 parts of quartz, 5 parts of Suzhou soil, 1.2 parts of bone ash, 5.8 parts of titanium dioxide, 9 parts of industrial zinc oxide, Barium carbonate is 4.2 parts, and dolomite is 1 part.

[0061] The constituents of the above-mentioned frit and the pre-calcination of the raw materials zinc oxide and titanium dioxide are the same as in Example 1.

[0062] The preparation method of copper-based kiln variable glaze comprises the following steps:

[0063] (1) Preparation of bottom glaze slurry and top glaze slurry

[0064] Preparation of bottom glaze glaze slurry: Mix bottom glaze raw materials: water: balls in a weight ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses copper-series flambed glaze. Ground glaze of the copper-series flambed glaze is prepared from the components: SiO2, Al2O3, B2O3, Na2O, CaO, K2O, CuO, BaO, MgO, and less than one part of other components; and overglaze is prepared from the components: SiO2, CaO, Al2O3, K2O, B2O3, Na2O, ZnO, Ca3(PO4)2, TiO2, and less than one part of other components. The invention further provides a preparation method of the copper-series flambed glaze. The preparation method comprises the steps that (1) glaze slip of the ground glaze and glaze slip of the overglaze are prepared; (2) glazing is conducted; and (3) a blank is fired. Under the conditions of the components, raw materials and the preparation method, the copper-series flambed glaze can be prepared, the further demand of people for the color of the flambed glaze is met, as for the copper-series flambed glaze, the dissolving-out amount of lead and cadmium is not detected, the copper-series flambed glaze can be used as adecoration of tea-tasting tea sets and daily tableware and is very safe, and the health of people is ensured.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a method for manufacturing copper-based kiln-transformed glaze. Background technique [0002] Ceramic kiln-changing glaze is one of the decoration techniques for ceramic surfaces. It has many changes, rich colors, and the most complicated shape. In ancient my country, most of the kiln-changing glazes were obtained by chance. They were very unstable and difficult to be controlled by people, so it is called It is called "Kiln Change", and the saying goes "Kiln Change is unparalleled", which means that it is unpredictable and unique. [0003] With the deepening of people's understanding of kiln-changing glaze, the beauty of kiln-changing defects has gradually been loved by people, so it is regarded as artistic enamel and appreciated by people. Especially in recent years, kiln-changing glaze can be used on daily tableware to make artistic ceramics practical Chemical use ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/14C03C8/02C04B41/89
CPCC03C8/02C03C8/14C04B41/89
Inventor 刘志斌韩晓伟陈春明赵玉虎
Owner JIANGSU GAOCHUN CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com