Thick white glaze ceramics and preparation method thereof
A technology of white glaze and ceramics, which is applied in the field of fertile white glaze ceramics and its preparation, which can solve the problems of reduced permeability of the green body, difficulty in sintering of the green body, and easy downward flow, etc., and achieves the expansion of the firing temperature range, high temperature High viscosity, pinhole reduction effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0027] A fertile white glaze, which is composed of the following raw materials in parts by weight: 55 parts of water crystal frit, 30 parts of potassium feldspar, 8 parts of Longyan kaolin, 1 part of zinc oxide, 4 parts of Guangfeng calcined talc, 2 parts of strontium carbonate, 0.5 parts of titanium dioxide.
[0028] Wherein, the crystal frit has a high initial melting temperature, a high viscosity at high temperature, and a slow decrease in viscosity as the temperature increases.
[0029] Wherein, K in the potassium feldspar 2 The percentage content of O is 13.2%, Na 2 The percentage content of O is 2.3%.
[0030] The preparation method of plump white glaze comprises the following steps:
[0031] Step 1: Select raw materials, select crystal frit, potassium feldspar, and Longyan kaolin;
[0032] Step 2: Weigh the raw materials according to the ratio, put the raw materials in the ball mill respectively, and perform ball milling according to the ratio of raw materials: ball...
Embodiment 2
[0037] A fertile white glaze, which is composed of the following raw materials in parts by weight: 60 parts of crystal frit, 25 parts of potassium feldspar, 7 parts of Longyan kaolin, 1 part of zinc oxide, 5 parts of Guangfeng calcined talc, 2 parts of strontium carbonate, titanium 0.5 part of white powder.
[0038] Wherein, the crystal frit has a high initial melting temperature, a high viscosity at high temperature, and a slow decrease in viscosity as the temperature increases.
[0039] Wherein, K in the potassium feldspar 2 The percentage content of O is 13.6%, Na 2 The percentage content of O is 2.0%.
[0040] The preparation method of plump white glaze comprises the following steps:
[0041] Step 1: Select raw materials, select crystal frit, potassium feldspar, and Longyan kaolin;
[0042] Step 2: Weigh the raw materials according to the ratio, put the raw materials in the ball mill respectively, and perform ball milling according to the ratio of raw materials: ball s...
Embodiment 3
[0047] A fertile white glaze, which is composed of the following raw materials in parts by weight: 60 parts of crystal frit, 30 parts of potassium feldspar, 6 parts of Longyan kaolin, 2 parts of zinc oxide, 3 parts of Guangfeng calcined talc, 1 part of strontium carbonate, titanium 0.6 part of white powder.
[0048] Wherein, the crystal frit has a high initial melting temperature, a high viscosity at high temperature, and a slow decrease in viscosity as the temperature increases.
[0049] Wherein, K in the potassium feldspar 2 The percentage content of O is 13.2%, Na 2 The percentage content of O is 2.3%.
[0050] The preparation method of plump white glaze comprises the following steps:
[0051] Step 1: Select raw materials, select crystal frit, potassium feldspar, and Longyan kaolin;
[0052] Step 2: Weigh the raw materials according to the ratio, put the raw materials in the ball mill respectively, and perform ball milling according to the ratio of raw materials: ball s...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology