ABS/POK composite material and preparation method thereof

A composite material, POK technology, applied in the field of ABS/POK composite material and its preparation, can solve the problems of easy aging and discoloration of unsaturated polybutadiene double bonds, restricting the application and promotion of ABS materials, and poor resistance to organic solvents, etc. Stable product quality, large industrial application value, good gloss effect

Inactive Publication Date: 2019-10-25
KINGFA SCI & TECH CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, ABS material has poor resistance to oil and organic solvents, and is prone to swelling and damage in non-polar oils or chemical solvents. The unsaturated polybutadiene double bonds in the structure are prone to aging and discoloration, which affects the appearance of the product. This performance defect is extremely serious. The earth restricts the application and promotion of ABS materials in some product fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ABS/POK composite material and preparation method thereof
  • ABS/POK composite material and preparation method thereof
  • ABS/POK composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] In order to better illustrate the purpose, technical solutions and advantages of the present invention, the present invention will be further described below with reference to specific embodiments.

[0025] The preparation method of ABS / POK composite material in the embodiment of the present invention is:

[0026] (1) Mix the ABS resin, POK polyketone resin, PETG resin, compatibilizer and processing aid in proportion to a high-speed mixing mixer or enter the twin-screw extruder through a metering feeder alone;

[0027] (2) Under the conveying, mixing and shearing action of the twin-screw extruder, the ingredients in the formula are fully melted and plasticized, kneaded and mixed, extruded through the head, drawn, cooled, pelletized, dried, and packaged. The novel high-performance flame-retardant ABS composite material is obtained; wherein, the screw temperatures of each section of the twin-screw extruder from the feeding port to the die head are: the temperature of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Average particle sizeaaaaaaaaaa
Average particle sizeaaaaaaaaaa
Melt indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ABS / POK composite material. The ABS / POK composite material comprises the following components in parts by weight: 20 to 77.8 parts of ABS resin, 15 to 60 parts of POK polyketone resin and 5 to 30 parts of PETG resin. According to the invention, the POK polyketone resin is creatively alloyed with ABS, so the technical bottleneck problem of compatibility of a resin systemis well solved; mechanical properties of a material are greatly improved; meanwhile, good glass is endowed to the material by the PETG; excellent weather resistance and solvent resistance are endowedto the material by the POK resin; the disadvantages of a conventional ABS alloy material are compensated; and great industrial application value is achieved. Meanwhile, the invention also discloses apreparation method for the ABS / POK composite material.

Description

technical field [0001] The invention belongs to the technical field of ABS composite materials, in particular to an ABS / POK composite material and a preparation method thereof. Background technique [0002] ABS resin is a terpolymer composed of styrene, butadiene and acrylonitrile. It has the high fluidity of styrene, the toughness of butadiene and the corrosion resistance of acrylonitrile. Low temperature performance, electrical insulation performance, high gloss and excellent electroplating performance, and excellent creep resistance, high dimensional stability, small molding shrinkage and other excellent characteristics, used in plastic products in the fields of home appliances, automobiles, electronic appliances, etc. very broad. [0003] However, the ABS material has poor oil resistance and organic solvent resistance, and is prone to swelling and damage in non-polar oils or chemical solvents. The unsaturated polybutadiene double bond in the structure is prone to aging ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08L73/00C08L67/02C08L25/14B29C48/92
CPCB29C48/92B29C2948/9259B29C2948/92704C08L55/02C08L73/00C08L2205/035C08L2205/08C08L67/02C08L25/14
Inventor 秦旺平叶南飚黄险波付锦锋杨霄云
Owner KINGFA SCI & TECH CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com