Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A high-performance orthodontic bite and its preparation method

A high-performance, orthodontic technology, applied in the field of orthodontic materials, can solve problems such as poor resilience, difficult production, and poor bite resistance, and achieve improved mechanical strength and resilience, good deformation resistance, and deformation resistance The effect of excellent performance

Active Publication Date: 2022-02-22
苏州多美新健康科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Existing bites generally use styrene-butadiene rubber, TPE or TPR (poor resilience and bite resistance)
Styrene-butadiene rubber has high raw material cost, difficult production, and sharp cutting end, which is not easy to form
TPE or TPR has poor resilience and poor bite resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A high-performance orthodontic bite prepared from the following raw materials in parts by weight: the high-performance orthodontic bite is prepared from the following raw materials in parts by weight: 70 parts of silica gel, 20 parts of modified nano fillers, organic silicon 15 parts of oxane-modified styrene-butadiene rubber, 18 parts of maleic anhydride grafted hydrogenated styrene-butadiene block co-extract, 3 parts of vulcanizing agent, and 2 parts of crosslinking agent.

[0025] The modified nano filler is modified attapulgite, modified sepiolite and modified white carbon black with a mass ratio of 1:1:1, and the preparation method of the modified nano filler is as follows:

[0026] The modified nano-filler was pulverized with a pulverizer, then dispersed in an aqueous solution, stirred and mixed, and polyethylene glycol was added to ultrasonically disperse at a temperature of 35°C for 1 hour, the precipitate was collected by suction filtration, and the precipitate ...

Embodiment 2

[0035] A high-performance orthodontic bite, prepared from the following raw materials in parts by weight: 60 parts of silica gel, 10 parts of modified nano filler, 10 parts of organosiloxane modified styrene-butadiene rubber, maleic anhydride grafted hydrogenated styrene - 10 parts of butadiene block co-extract, 1 part of vulcanizing agent, 1 part of crosslinking agent;

[0036] The modified nano filler is modified attapulgite, and the preparation method of the modified nano filler is as follows:

[0037] Use a pulverizer to grind the modified nanofiller, then disperse it in the aqueous solution and mix it, add polyethylene glycol and disperse it ultrasonically for 0.5h at a temperature of 30°C, collect the precipitate by suction filtration, and vacuum dry the precipitate A modified nano filler is prepared.

[0038] The vulcanizing agent is trimercapto-s-triazine.

[0039] The mass ratio of the polyethylene glycol to the modified nano filler is 5:1.

[0040] The crosslinkin...

Embodiment 3

[0046] A high-performance orthodontic bite, prepared from the following raw materials in parts by weight: 65 parts of silica gel, 15 parts of modified nano-fillers, 12 parts of organosiloxane-modified styrene-butadiene rubber, maleic anhydride grafted hydrogenated styrene - 15 parts of butadiene block co-extract, 2 parts of vulcanizing agent, 1.5 parts of crosslinking agent;

[0047] The modified nano filler is modified sepiolite, and the preparation method of the modified nano filler is as follows:

[0048]Use a pulverizer to crush the modified nanofiller, then disperse it in the aqueous solution and mix it, add polyethylene glycol and ultrasonically disperse at a temperature of 32°C for 0.8h, collect the precipitate by suction filtration, and vacuum dry the precipitate A modified nano filler is prepared.

[0049] The vulcanizing agent is ethylenethiourea.

[0050] The mass ratio of the polyethylene glycol to the modified nano filler is 6:1.

[0051] The cross-linking agen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-performance orthodontic bite and a preparation method thereof, which is prepared from the following raw materials in parts by weight: 60-80 parts of silica gel, 10-30 parts of modified nano filler, and organosiloxane modified butyl styrene 10-20 parts of rubber, 10-25 parts of maleic anhydride grafted hydrogenated styrene-butadiene block co-extract, 1-5 parts of vulcanizing agent, and 1-3 parts of crosslinking agent. According to the test results, the rubber bite prepared by the present invention has good mechanical strength, and the compression permanent deformation test results show that the rubber bite has good deformation resistance and good resilience. The method has simple process and convenient operation, can save a large amount of manpower and material resources, is low in cost, produces no toxic irritating smell during the preparation process, is safe and environment-friendly, and the obtained chew has high resilience and strong bite resistance. Therefore, the method of the present invention has wide application prospects in the field of chewing gum.

Description

technical field [0001] The invention belongs to the technical field of orthodontic materials, and in particular relates to a high-performance orthodontic bite and a preparation method thereof. Background technique [0002] Bite is a silicone rod that is used in conjunction with invisible braces. The use of bites can make the invisible braces fit better with the teeth, ensuring the balance of the entire orthodontic force system during orthodontics. Therefore, the use of chewing gum mainly has the following functions: 1. Make the invisible braces fit better. Grinding can eliminate the gap between the braces and the teeth, making the braces more invisible and making the gap smaller; 2. Preventing the occurrence of braces face , because the teeth will be a little sore and soft after wearing braces, and it is troublesome to take off the braces when eating, etc., which will lead to eating less food than usual, and the use of chewing function will also be reduced, which may lead to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L83/04C08L51/00C08L71/02C08L15/00C08K13/06C08K3/34C08K3/36C08K5/14
CPCC08L83/04C08K2201/011C08K2201/014C08L2205/035
Inventor 程德盛
Owner 苏州多美新健康科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com