A kind of leachate transportation pipe and preparation method thereof

A technology of leachate and pipe materials, which is applied in the field of pipe materials, can solve the problems of easy scaling and descaling costs of leachate transportation pipes, and achieve the effects of inhibiting the formation of easy-scaling biofilms, improving dispersibility, and improving anti-scaling performance

Active Publication Date: 2020-06-23
SOUTHWEST JIAOTONG UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a leachate transport pipe and its preparation method to solve the problems of easy fouling and high cost of scale removal in existing leachate transport pipes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of leachate transportation pipe and preparation method thereof
  • A kind of leachate transportation pipe and preparation method thereof
  • A kind of leachate transportation pipe and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The leachate transport pipe of this embodiment comprises the following raw materials: 9 parts of polymethylsiloxane epoxy acrylate, 1 part of hydrophobically modified nano-silica and 90 parts of high-density polyethylene.

Embodiment 2

[0041] The leachate transport pipe of this embodiment comprises the following raw materials: 12 parts of polymethylsiloxane epoxy acrylate, 3 parts of hydrophobically modified nano-silica and 85 parts of high-density polyethylene.

Embodiment 3

[0043]The leachate transport pipe of this embodiment comprises the following raw materials: 18 parts of polymethylsiloxane epoxy acrylate, 5 parts of hydrophobically modified nano-silica and 77 parts of high-density polyethylene.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a leachate transport pipe and a preparation method thereof, belonging to the technical field of pipes. Leachate transport tubing includes the following raw materials: polymethylsiloxane epoxy acrylate, hydrophobically modified nano-silica, and high-density polyethylene. The surface of the leachate transportation pipe of the invention has good anti-scaling performance; the surface of the material has good wear resistance, and the hydrophobic performance of the material surface after abrasion is improved, and its anti-scaling performance is obviously better than that of ordinary high-density polyethylene materials. The preparation method of the invention is simple, and the synthesis of the siloxane acrylate polymer adopts a two-step bulk polymerization method, and the whole process does not use organic solvents, and has no pollution to the environment; It leads to the shortcoming of short service life, and the bulk polymer and the modified nanopowder in the blend system have the same functional group, which makes the blend system have good compatibility.

Description

technical field [0001] The invention relates to the technical field of pipes, in particular to a leachate transport pipe and a preparation method thereof. Background technique [0002] Landfill leachate has the characteristics of a wide variety of pollutants and complex components. Generally, it needs to be collected by the pipeline system and transported to the corresponding treatment facilities for subsequent treatment. Commonly used leachate transport pipes are mainly high-density polyethylene (HDPE) materials, and the main additives include antioxidants, carbon black masterbatches, calcium carbonate, paraffin and other fillers, among which carbon black and calcium carbonate fillers have strong water absorption. During the transportation of leachate, this kind of pipe is likely to cause contamination on the inner wall of the pipe, and then scale, resulting in pipe blockage, which may cause the pipe to burst in severe cases. Scaling of leachate transportation pipelines se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L51/00C08K9/06C08K3/36C08F265/06C08F265/04C08F230/08C08F220/18C08F220/32
CPCC08F265/04C08F265/06C08K2201/011C08L23/06C08L2203/18C08L2207/062C08L51/003C08K9/06C08K3/36C08F230/08
Inventor 赵锐李敏
Owner SOUTHWEST JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products