Preparation method of side-chain hydrophilic polyester fabric moisture absorption and sweat releasing finishing agent and the finishing agent

A polyester fabric, moisture wicking technology, applied in the direction of fiber treatment, fiber type, textile and paper making, etc., can solve the problem that the finishing agent cannot take into account the hydrophilic and washable at the same time, and achieve excellent hydrophilic performance and washable performance, Solve the effect of poor water solubility and high synthesis efficiency

Inactive Publication Date: 2019-11-22
DYMATIC CHEM
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to overcome the disadvantage that the polyester polyether block copolymerized finishing agent cannot take into account both hydrophilicity and washability, and to provide a polyester fabric with good hydrophilicity, strong comfort, and good washability Preparation method and finishing agent of moisture-absorbing and sweat-wicking finishing agent to overcome deficiencies in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of side-chain hydrophilic polyester fabric moisture absorption and sweat releasing finishing agent and the finishing agent
  • Preparation method of side-chain hydrophilic polyester fabric moisture absorption and sweat releasing finishing agent and the finishing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Synthesis of side chain hydrophilic diols: first add 37g glycidyl alcohol and 500g monomethyl-terminated ethylene glycol (molecular weight is 1000), add 179g ethanol, keep warm at 60°C for 5 hours, change to reduced pressure distillation after the reaction ends, and distill Remove ethanol to get side chain hydrophilic diol.

[0022] Synthesis of side-chain hydrophilic moisture-absorbing and sweat-wicking agent: first, dehydration reaction is carried out on polyethylene glycol and side-chain hydrophilic diol, and the temperature is controlled at 100-105° C. for vacuum dehydration for 1 hour. After the dehydration is completed, 40g dimethyl terephthalate, 150g polyethylene glycol, 30g ethylene glycol, 40g side chain hydrophilic glycol, and 0.06g zinc acetate are added to the reaction vessel equipped with a thermometer and a nitrogen tube in sequence, Slowly raise the temperature under the protection of nitrogen, and when the temperature rises to 170°C in 25-30 minutes, co...

Embodiment 2

[0026] Synthesis of side-chain hydrophilic diols: first add 37g glycidyl alcohol and 500g monomethyl-terminated ethylene glycol (the number average molecular weight is 1000), add 179g ethanol, keep warm at 60°C for 5 hours, and change to vacuum distillation after the reaction , Ethanol is evaporated to obtain a side chain hydrophilic diol.

[0027] Synthesis of side-chain hydrophilic moisture-absorbing and sweat-wicking agent: first, dehydration reaction is carried out on polyethylene glycol and side-chain hydrophilic diol, and the temperature is controlled at 100-105° C. for vacuum dehydration for 1 hour. After the dehydration is completed, 38g dimethyl terephthalate, 160g polyethylene glycol, 28g ethylene glycol, 50g side chain hydrophilic glycol, and 0.08g calcium acetate are added to the reaction vessel equipped with a thermometer and a nitrogen tube in sequence, Slowly raise the temperature under the protection of nitrogen, and when the temperature rises to 170°C in 25-30...

Embodiment 3

[0031] Synthesis of side chain hydrophilic diols: first add 37g glycidyl alcohol and 500g monomethyl-terminated ethylene glycol (molecular weight is 1000), add 179g ethanol, keep warm at 60°C for 5 hours, change to reduced pressure distillation after the reaction ends, and distill Remove ethanol to get side chain hydrophilic diol.

[0032] Synthesis of side-chain hydrophilic moisture-absorbing and sweat-wicking agent: first, dehydration reaction is carried out on polyethylene glycol and side-chain hydrophilic diol, and the temperature is controlled at 100-105° C. for vacuum dehydration for 1 hour. After the dehydration is completed, 30g dimethyl terephthalate, 140g polyethylene glycol, 24g ethylene glycol, 42g side chain hydrophilic glycol, and 0.07g magnesium acetate are added to the reaction vessel equipped with a thermometer and a nitrogen tube in sequence. Slowly raise the temperature under the protection of nitrogen, and when the temperature rises to 170°C in 25-30 minute...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of a polyester fabric moisture absorption and sweat releasing finishing agent with a hydrophilic side chain, wherein the method comprises the following steps: with dimethyl terephthalate, ethylene glycol, polyethylene glycol, a self-made side chain hydrophilic diol and a catalyst as raw materials, carrying out transesterification, and carrying out polycondensation to synthesize the polyester-polyether copolymerization moisture absorption and sweat releasing finishing agent suitable for polyester fabrics. The method is high in synthesis efficiency,the finished fabric is good in hydrophilicity, high in comfort and good in washability, and the problem that an existing moisture absorption and sweat releasing agent cannot give consideration to hydrophilicity and washability at the same time is solved.

Description

technical field [0001] The invention relates to the technical field of moisture-absorbing and perspiration-absorbing finishing agents for polyester fabrics, in particular to a method for preparing a moisture-absorbing and perspiration-absorbing finishing agent that is applied to polyester fabrics and is both hydrophilic and washable, and the finishing prepared by the method agent. Background technique [0002] From the perspective of human body wearing comfort, people hope that sweat can be absorbed and transferred by clothing, and sweat can be evaporated quickly on the surface of clothing to keep the surface of the skin and the microclimate zone inside the clothing dry. , Summer clothing is particularly important. In recent years, as consumers pay more and more attention to comfort when purchasing clothes, the demand for moisture-wicking clothes is growing rapidly. Synthetic fibers have excellent properties that natural fibers cannot match, especially the most widely used...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G63/672D06M15/53D06M15/507D06M101/32
CPCC08G63/672D06M15/507D06M15/53D06M2101/32
Inventor 张世恒梁永标许志军杨之卓郭玉良黄尚东
Owner DYMATIC CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap