Water-based ink for tipping paper

A tipping paper and water-based technology, which is applied in ink, chemical modification of natural resin, household appliances, etc., can solve the problems of slow drying speed of water-based ink, hard shrinkage of ink film, affecting printing speed and subsequent processing, etc., to reduce VOC Emission, soft ink film, good stability

Inactive Publication Date: 2019-11-29
WENZHOU LIKEDA PRINTING
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the poor wetting and dispersibility of acrylic resin on pigments, the printing effect is not good (blackheads, water lines), and at the same time, it becomes acrylic resin after curing and deamination. This type of resin is a brittle resin, and the ink film is hard and shrinks greatly. The paper curl is obvious. In addition, looking at the water-based ink printing on tipping paper in my country, there are still the following main problems in the application of tipping paper:
Tipping paper has clear requirements on product odor: there must be no odor that hinders cigarettes. The odor in water-based ink mainly comes from the ammonia substances used in the resin ammoniation process, and the odor is not friendly to the senses.
[0004] (2) Paper deformation is too large
Since the base paper for tipping paper printing has a quantitative range of 31-37g / m2, which is thin paper, water in ink printing will cause the paper to absorb moisture and become soft, resulting in serious deformation of the paper
[0005] (3) The drying speed is too slow
The drying speed of water-based ink is too slow, which affects the printing speed and subsequent processing, and it may also be the phenomenon of fog and paste in the gravure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A water-based tipping paper ink, comprising the following components in parts by weight, 20 parts of water-soluble polyvinyl butyral, 0.1 part of water-soluble modified rosin resin, 0.1 part of pigment, 0.1 part of filler, 0.1 part of wax powder, 50 parts of ethanol, 0.1 part of water and 0.1 part of dispersant, the water-soluble modified rosin resin is composed of water-soluble maleic acid, rosin pentaerythritol ester and triethanolamine ammonia in a ratio of parts by weight of 1:2:5:2.

[0033] The preparation method of described rosin pentaerythritol ester, comprises the steps:

[0034] Select 100 parts of rosin, heat it at 150°C-160°C to melt, add 12 parts of formaldehyde, stir at 90-100°C for 2-2.5 hours, add 5 parts of 2,3 pyrazine diacid anhydride and react at 180-200°C for 1.5- 2H, add 80 parts of pentaerythritol and 2 parts of magnesium oxide, heat up to 270-280°C, and vacuumize for 1 hour.

[0035] The concentration of the water-soluble polyvinyl butyl acetal...

Embodiment 2

[0049] A water-based tipping paper ink, comprising the following components in parts by weight, 35 parts of water-soluble polyvinyl butyral, 7 parts of water-soluble modified rosin resin, 23 parts of pigments, 25 parts of fillers, 0.5 parts of wax powder, 80 parts of ethanol, 43 parts of water and 0.5 part of dispersant, the water-soluble modified rosin resin is composed of water-soluble maleic acid, rosin pentaerythritol ester and triethanolamine ammonia in a ratio of parts by weight of 1:2:5:2.

[0050] The preparation method of described rosin pentaerythritol ester, comprises the steps:

[0051] Select 100 parts of rosin, heat it at 150°C-160°C to melt, add 24 parts of formaldehyde, stir at 90-100°C for 2-2.5 hours, add 10 parts of 2,3 pyrazine diacid anhydride and react at 180-200°C for 1.5- 2H, add 80 parts of pentaerythritol and 2.1 parts of magnesium oxide, heat up to 270-280°C, and vacuumize for 1 hour.

[0052] The concentration of the water-soluble polyvinyl butyral...

Embodiment 3

[0066] A water-based tipping paper ink, comprising the following components in parts by weight, 50 parts of water-soluble polyvinyl butyral, 15 parts of water-soluble modified rosin resin, 45 parts of pigment, 50 parts of filler, 1 part of wax powder, 95 parts of ethanol, 95 parts of water and 1 part of dispersant, the water-soluble modified rosin resin is composed of water-soluble maleic acid, rosin pentaerythritol ester and triethanolamine ammonia in a ratio of parts by weight of 1:2:5:2.

[0067] The preparation method of described rosin pentaerythritol ester, comprises the steps:

[0068] Select 100 parts of rosin, heat it at 150°C-160°C to melt, add 30 parts of formaldehyde, stir at 90-100°C for 2-2.5 hours, add 15 parts of 2,3 pyrazine diacid anhydride and react at 180-200°C for 1.5- 2H, add 80 parts of pentaerythritol and 2.2 parts of magnesium oxide, raise the temperature to 270-280 ° C, and vacuumize for 1 hour.

[0069] The concentration of the water-soluble polyvin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to water-based ink for tipping paper. The water-based ink is characterized by comprising the following components in parts by weight: 20-50 parts of water-soluble polyvinyl butyral, 0.1-15 parts of water-soluble modified rosin resin, 0.1-45 parts of a pigment, 0.1-50 parts of a filler, 0.1-1 part of wax powder, 50-95 parts of ethanol, 0.1-95 parts of water and 0.1-1 part of adispersant, wherein the water-soluble modified rosin resin consists of water-soluble maleic acid, pentaerythritol abietate and triethanolamine according to a weight ratio of 1:2:5:2. The water-basedink provided by the invention has the advantages of small odor, low viscosity and good stability.

Description

technical field [0001] The invention relates to the technical field of water-based ink, in particular to a water-based tipping paper ink. Background technique [0002] At present, many printing manufacturers have turned their attention to water-based inks. For this reason, relevant enterprises and units have proposed many technical solutions for "tipping paper printing inks". Such as patent number: 200810233722.6, announcement number: CN101429364 "environmentally friendly antibacterial water-based ink for tipping paper" (water-based acrylic resin); Water-based acrylic resin, water-based acrylic modified rosin resin); etc. However, most of the above-mentioned patents use acrylic or acrylic modified resins to carry out ammoniated water-based. Due to the poor wetting and dispersibility of acrylic resin on pigments, the printing effect is not good (blackheads, water lines), and at the same time, it becomes acrylic resin after curing and deamination. This type of resin is a bri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/106C09D11/08C09D11/033C09D11/037C09D11/03C09F1/04
CPCC09D11/03C09D11/033C09D11/037C09D11/08C09D11/106C09F1/04
Inventor 杨青青牛文兴岳敏肖志坚胡新根
Owner WENZHOU LIKEDA PRINTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com