Glazed ceramic decorative wall tile and manufacturing method thereof

A manufacturing method and technology of ceramic bricks, which are applied in the field of building ceramic materials and lightweight foamed ceramics, and can solve the problems of high total cost, waste of resources, environmental pollution, etc.

Inactive Publication Date: 2019-12-24
恩平市华昌陶瓷有限公司
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition to using a large amount of solid waste in the ceramic industry as the main raw material for the green body, the method of the present invention solves the problems of environmental pollution and resource waste caused by a large amount of solid waste being dumped and landfilled, and also solves the difficulties and difficulties encountered in foamed ceramics. Provided a set of innovative solutions, includi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glazed ceramic decorative wall tile and manufacturing method thereof
  • Glazed ceramic decorative wall tile and manufacturing method thereof
  • Glazed ceramic decorative wall tile and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] A method for manufacturing ceramic glazed decorative wall tiles, comprising the following steps:

[0062] (1) In terms of percentage by weight, weigh and mix the following ceramic brick body raw materials, and then wet pulverize them with a ball mill to become foamed ceramic body mud. The moisture content of the mud is 35%, and the fineness is 250 mesh sieves Amount 1.4%;

[0063] The ceramic brick body includes the following raw materials: 73.1% of waste squeezed mud from ceramic factories, 5% of rotten tile powder or stone powder tailings, 1% of coal-water slurry slag, 2% of foamed ceramic recycling waste, 3% of talc, 10% of clay, Bentonite 5%, foaming agent 0.9%;

[0064] (2) carry out spray drying after described mud is passed through 80 mesh sieves, then pass through 16 mesh sieves and obtain the powdery blank that moisture content is 7.5%, standby after stale for 50 hours;

[0065] (3) According to the respective weight percentages of the three kinds of glazes, ...

Embodiment 2

[0075] A method for manufacturing ceramic glazed decorative wall tiles, comprising the following steps:

[0076] (1) In terms of percentage by weight, weigh the following ceramic brick body raw materials and mix them, and then wet pulverize them with a ball mill to become foamed ceramic body mud. The moisture content of the mud is 34%, and the fineness is 250 mesh sieves. Amount 1.5%;

[0077] The ceramic brick body includes the following raw materials: 64.3% of waste squeezed mud from ceramic factories, 10% of rotten tile powder or stone powder tailings, 2% of coal-water slurry slag, 3% of foamed ceramic recycling waste, 3% of talc, 12% of clay, Bentonite 5%, foaming agent 0.7%;

[0078] (2) Spray-dry the mud after passing through a 60 mesh sieve, then pass through a 14 mesh sieve to obtain a powdery base with a moisture content of 7%, and put it aside after stale for 50 hours;

[0079] (3) According to the respective weight percentages of the three kinds of glazes, weigh t...

Embodiment 3

[0089] A method for manufacturing ceramic glazed decorative wall tiles, comprising the following steps:

[0090] (1) In terms of percentage by weight, weigh and mix the following ceramic brick body raw materials, and then wet pulverize them with a ball mill to become foamed ceramic body mud. The moisture content of the mud is 33%, and the fineness is 250 mesh sieves. Amount 1.6%;

[0091] The ceramic brick body includes the following raw materials: 42.4% of waste squeezed mud from ceramic factories, 28% of rotten tile powder or stone powder tailings, 4% of coal-water slurry slag, 5% of foamed ceramic recycling waste, 3% of talc, 12% of clay, Bentonite 5%, foaming agent 0.6%;

[0092] (2) Spray-dry the mud after passing through a 50 mesh sieve, then pass through a 12 mesh sieve to obtain a powdery base with a moisture content of 7%, which is set aside after stale for 50 hours;

[0093] (3) According to the respective weight percentages of the three kinds of glazes, weigh them...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thermal conductivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a glazed ceramic decorative wall tile. The wall tile comprises a ceramic tile body and a glaze surface, wherein the ceramic tile body comprises 15-80% of ceramic factory wastepressed mud, 5-75% of rotten ceramic tile powder or stone powder tailings, 1-10% of coal water slurry slag, 0-20% of foamed ceramic recycled waste, 0-12% of talc, 5-20% of clay, 2-15% of bentonite and0.3-1.5% of a foaming agent; and the glaze surface comprises an isolation glaze located on the surface of the ceramic tile body, a surface glaze located on the isolation glaze and a protective glazelocated on the surface glaze. Solid waste in the ceramic industry is used as main raw materials, and the wall tile and the method conform to the trend of environmental protection, greenness and sustainable development. The foamed ceramic wall tile has a water absorption rate of less than 0.4%, a density of 0.9-1.4 g/cm<3>, compressive strength of more than 8 MPa, breaking strength of more than 5 MPa, tensile strength of more than 2 MPa, a heat conductivity coefficient of 0.25-0.46 w/m.k, and a combustion performance of AI grade.

Description

technical field [0001] The invention belongs to the technical field of building ceramic materials and the field of lightweight foamed ceramics, and specifically relates to a medium-density foamed ceramic glazed decorative wall tile based on industrial solid waste utilization and rapid bare firing in a roller kiln and a manufacturing method thereof. Background technique [0002] Traditional ceramic tiles are generally solid and dense, with a density of 2.3-2.5g / cm 3 Whether it is used for exterior walls or interior walls, it will greatly increase the load-bearing capacity of the wall. When used for exterior walls of high-rise buildings, the safety is even worse. Large-scale ceramic tiles are used for high-rise exterior walls. It has been explicitly banned in many places, and because their thermal conductivity is relatively large, generally around 2.0w / m.k, they do not have the functions of heat insulation and sound absorption, and cannot be used for the insulation of building...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/02C04B33/135C04B33/132C04B33/13C04B33/04C03C8/00C04B41/86
CPCC03C8/00C04B33/04C04B33/13C04B33/1324C04B33/1355C04B38/02C04B41/5022C04B41/86C04B2235/6562C04B2235/6565C04B2235/6567C04B2235/77C04B2235/96C04B2235/9607C04B38/0067Y02P40/60
Inventor 何绍坚
Owner 恩平市华昌陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap