Surface processing technology of mineral casting

A technology for mineral castings and surface processing, applied in the field of mineral castings, can solve the problems of insufficient corrosion resistance of mineral castings and cumbersome processes, and achieve the effects of enhanced corrosion resistance, low price and high strength

Inactive Publication Date: 2019-12-31
常州高鼎新材料科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a mineral casting surface processing technology to solve the above-mentioned background technology that usually requires mineral castings to be cast and molded after demoulding, after the surface is polished and cleaned, the surface that is not completely smooth after grinding is repaired with putty. Then spray paint after grinding, the process is cumbersome and the corrosion resistance of processed mineral castings is not strong enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Surface processing technology of mineral casting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The specific steps of the mineral casting surface processing technology are as follows:

[0035] S1. Demoulding on the inner surface of the mold: Drive the high-pressure pump to suck the release agent, pressurize it to 30MPa, and then spray it on the inner surface of the mold for mineral casting casting, so that there is no compressed air in the sprayed release agent to avoid compressed air. Ingress of moisture and other impurities leads to unsatisfactory release effect, which makes the surface of the release agent uneven;

[0036] S2. Coating anti-corrosion coating: mix the raw materials of anti-corrosion coating in equal proportions according to the set amount and put them in the container. The raw materials of anti-corrosion coating include polyacrylate, curing agent, pebbles and river sand, and the anti-corrosion coating The raw materials are: 60kg of polyacrylate, 20kg of curing agent, 12kg of pebbles and 8kg of river sand according to the mass specific gravity, an...

Embodiment 2

[0042] S1. Demoulding on the inner surface of the mold: drive the high-pressure pump to suck the release agent, pressurize it to 15MPa, and then spray it on the inner surface of the mold for casting mineral castings. In this way, there is no compressed air in the sprayed release agent to avoid compressed air. Ingress of moisture and other impurities leads to unsatisfactory release effect, which makes the surface of the release agent uneven;

[0043] S2. Coating anti-corrosion coating: mix the raw materials of anti-corrosion coating in equal proportions according to the set amount and put them in the container. The raw materials of anti-corrosion coating include polyacrylate, curing agent, pebbles and river sand, and the anti-corrosion coating The raw materials are: 5.8kg of polyacrylate, 2.2kg of curing agent, 1.5kg of pebbles and 0.5kg of river sand according to the mass specific gravity, and then use the mechanical arm to paint the anti-corrosion coating evenly on the surface...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of mineral castings, and specifically relates to a surface processing technology of a mineral casting. The specific steps of the surface processing technology of the mineral casting are as follows: S1, performing demolding on an inner surface of a mold: driving a high-pressure pump to suck a mold release agent, performing pressurizing to 15-30 MPa and then performing spraying on the inner surface of the mold for casting the mineral casting; S2, coating an anti-corrosion coating: mixing raw materials of the anti-corrosion coating in equal proportionsand placing the anti-corrosion coating in a container, and then uniformly coating the surface of the mold release agent with the anti-corrosion coating through a brushing manner by using a robot arm;S3, oven-drying the anti-corrosion coating: performing heating and oven-drying on the inside of the mold by using a dryer, wherein an oven-drying temperature is controlled to 50-70 DEG C, an oven-drying time is set to 30-50 min, and a completely sealed oven-drying method is used; S4, performing raw material casting and shaping; S5, coating the anti-corrosion coating again; and S6, oven-drying theanti-corrosion coating again. The working procedure of the technology is simple, and the processed mineral casting has stronger anti-corrosion performance.

Description

technical field [0001] The invention relates to the technical field of mineral castings, in particular to a surface processing technology of mineral castings. Background technique [0002] With the continuous damage of non-renewable resources, people are now more enthusiastic about environmental protection. No matter in which field, energy conservation and environmental protection have become the first appeal. Therefore, as a new type of environmental protection material, mineral castings, with their own performance and The price advantage has replaced traditional cast iron castings in some fields. In terms of performance, it is mainly manifested in: stronger forming ability and integration ability, higher processing accuracy, shock absorption is more than ten times that of traditional cast iron castings, thermal stability and resistance More corrosive. [0003] Nowadays, the processing of mineral castings usually requires the mineral castings to be casted and demoulded, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B26/00C04B41/65
CPCC04B26/00C04B28/00C04B41/009C04B41/50C04B41/65C04B14/02C04B14/06C04B14/386C04B40/00C04B41/4535C04B41/4857C04B41/46C04B41/4543
Inventor 邵如意徐建国
Owner 常州高鼎新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com